Rust-proof soft film composition and preparation method thereof

A technology of soft film composition and antirust agent, which is applied in the direction of lubricating composition, petroleum industry, additives, etc., and can solve the problem of destroying the original appearance of the metal surface when it can only be used indoors in a natural environment without rain and light. , limit the scope of use and other issues, to achieve excellent salt spray resistance and heat and humidity resistance, excellent anti-rust effect, prolong the effect of protection time

Active Publication Date: 2013-11-13
WUHAN RES INST OF MATERIALS PROTECTION
View PDF6 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the fact that the existing soft film antirust oil products tend to focus on certain aspects of performance, the oil film is thin, easy to flow or dry and brittle, and the comprehensive performance is not good, and the antirust effect is poor when the use environment is relatively complicated or harsh.
Chinese patent CN102031189A discloses a soft film antirust oil, which mainly consists of kerosene, machine oil, zinc naphthenate, barium dinonylnaphthalenesulfonate and other antirust agents. The oil film is thin, the strength is low, and the dropping point is low. It is easy to be lost under the action of light, heat or rain. Although the antirust performance is good, it can only be used indoors in a natural environment without rain or light; Chinese patent CN101768499A discloses a grease-type antirust with gas phase antirust function. Rust oil, due to the addition of phenolic resin lipid film modifier and octadecylamine, benzotriazole tributylamine vapor phase anti-rust agent in the formula, although the anti-rust oil film has the ability to resist the sun and rain, and has a gas-phase anti-rust function, But because there is no self-healing function, it cannot resist damage
In addition, Chinese patent CN102719184A discloses a self-healing anti-corrosion coating, which is made by adding polyurethane microcapsules to a coating composed of hydroxyacrylic resin, pigments, corrosion-inhibiting pigments, organic solvents, etc., and the coating surface treatment requirements are high. The coating film is difficult to remove, it is inconvenient to use, and the surface treatment will destroy the original shape of the metal surface, which greatly limits its scope of use, and is not suitable for use as an anti-rust soft film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rust-proof soft film composition and preparation method thereof
  • Rust-proof soft film composition and preparation method thereof
  • Rust-proof soft film composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of translucent antirust soft film composition of the present invention, its composition and mass percent are:

[0046]

[0047] The rheological agent is selected from polyamide modified castor oil derivatives,

[0048] Specifically used is LUVOTIX HT 2.5 from Lefus Chemical Company

[0049] Antifoaming agent is selected from modified polysiloxane,

[0050] Specifically, Deqian Chemical Company Defom6500 0.5

[0051] Xylene 8

[0052] n-Butanol 4

[0053] According to the above preparation method, add xylene, n-butanol, phenolic resin, petroleum resin, and vaseline into the reactor, stir and raise the temperature to 60°C, and keep it warm for 30 min. After the film-forming agent is completely dissolved, cool down to 45°C, and then Add barium dinonylnaphthalene sulfonate, barium petroleum sulfonate, dicyclohexylamine nitrite, microcapsule antirust agent, rheological agent, and defoamer, and continue stirring for 30 min at 45°C to obtain a uniform liquid . ...

Embodiment 2

[0055] A kind of black antirust soft film composition of the present invention, its composition and mass percent are:

[0056]

[0057]

[0058] The rheological agent is selected from polyamide modified castor oil derivatives,

[0059] Specifically used is LUVOTIX HT 2.5 from Lefus Chemical Company

[0060] Antifoaming agent is selected from modified polysiloxane,

[0061] Specifically, Deqian Chemical Company Defom6500 0.5

[0062] Xylene 14

[0063] n-Butanol 8

[0064] The above preparation method is as follows: add xylene, n-butanol, phenolic resin, petroleum resin, and beeswax into the reactor, stir and heat up to 60°C, keep it warm for 30 minutes, and cool down to 45°C after the film-forming agent is completely dissolved. Add barium dinonylnaphthalene sulfonate, barium oxidized petroleum tallow soap, dicyclohexylamine nitrite, benzotriazole dodecylamine, microcapsule antirust agent, carbon black, rheological agent, defoaming agent in sequence, at 45°C Under th...

Embodiment 3

[0066] A kind of blue antirust soft film composition of the present invention, its composition and mass percent are:

[0067]

[0068] The rheological agent is selected from polyamide modified castor oil derivatives,

[0069] Specifically used is LUVOTIX HT 2.5 from Lefus Chemical Company

[0070] Antifoaming agent is selected from modified polysiloxane,

[0071] Specifically, Deqian Chemical Company Defom6500 0.5

[0072] Xylene 6

[0073] n-Butanol 2.5

[0074] According to the above preparation method, add xylene, n-butanol, phenolic resin, petroleum resin, and beeswax into the reactor, stir and raise the temperature to 60°C, and keep it warm for 30 minutes. After the film-forming agent is completely dissolved, cool down to 45°C, and then Add barium dinonylnaphthalene sulfonate, magnesium lanolin soap, 2-ethyl-4-methylimidazole, benzotriazole dodecylamine, microcapsule rust inhibitor, phthalocyanine blue, rheological agent, defoamer, Stirring was continued for 30 mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rust-proof soft film composition and a preparation method thereof, belonging to the technical field of metal protection and particularly relating to a metal rust preventing technology. The rust-proof soft film composition disclosed by the invention comprises the following components in a formula in percentage by mass: 40-70 of film forming agent, 2-10 of corrosion and rust inhibitor, 1-5 of vapor phase inhibitor, 4-10 of microcapsule antirust agent, 0-10 of pigment, 1-3 of rheological agent, 0.2-1.0 of defoaming agent and 10-25 of solvent. The rust-proof soft film composition disclosed by the invention has an excellent rust-proof effect and an excellent self-repairing function; rust-proof gas volatilized by the film can meet the rust-proof requirements of inner and outer surfaces of workpieces with complex structures such as inner metal cavities, inner walls of pipelines, grooves and the like; when the rust-proof soft film is destroyed in a use process, a rust-proof core with an excellent self-repairing function of the microcapsule antirust agent can be automatically repaired, so that the condition that the rust-proof film is invalid in advance because of being destroyed is avoided, and the protection time of a protective film is prolonged; and the rust-proof soft film composition can comprehensively meet the requirement for metal rust-proof protection under severe environments such as outdoor sun and rain, sand-dust and the like.

Description

technical field [0001] The invention relates to an anti-rust soft film composition and a preparation method thereof, belonging to the technical field of metal protection, in particular to the metal anti-rust technology. Background technique [0002] Metal equipment is easily corroded by the external environment or medium in the process of manufacturing, storage, transportation and use. After the surface is corroded and rusted, the performance and commodity value of the equipment will be greatly damaged, and even its service life will be greatly affected. , or cause major accidents, causing heavy losses to the national economy and national defense construction. Therefore, the protection of metal surfaces is of great significance to the development level of the machinery manufacturing industry, to safe production, and to the utilization efficiency of natural resources. [0003] Soft film anti-rust is one of the important ways to protect metal surfaces. Compared with other typ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M167/00C10N30/12C10N50/02
Inventor 张迎平汪洋刘兰轩刘秀生
Owner WUHAN RES INST OF MATERIALS PROTECTION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com