Preparation method of polytetrafluoroethylene rubber roller

A technology of polytetrafluoroethylene rubber roller and polytetrafluoroethylene, which is applied in the direction of shafts and bearings, can solve the problems of increasing processing difficulty and achieve the effects of short service life, super high and low temperature resistance, and broad market prospects

Active Publication Date: 2016-01-06
浙江宁奇环保材料科技有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent is only to set a polytetrafluoroethylene film layer on the surface of the rubber roller, and the polytetrafluoroethylene film layer is attached to the outer layer of glue. The thickness of the polytetrafluoroethylene film layer is not enough to easily cause peeling. And the hard glue layer also increases the processing difficulty of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polytetrafluoroethylene rubber roller

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The specific implementation manner of the present invention will be described in detail below in conjunction with the accompanying drawings.

[0022] Such as figure 1 The polytetrafluoroethylene rubber roller shown, the rubber roller includes a roller body and a metal mandrel, the roller body adopts a cylindrical sleeve 1 made of polytetrafluoroethylene, the wall thickness of the sleeve 1 is 30mm, and the metal core The rod is installed in the sleeve 1 and fixed with the sleeve 1. The surface of the metal mandrel is provided with saber teeth in the axial direction, and the metal mandrel and the sleeve 1 are tightly fitted and fixed by the saber teeth. The metal mandrel includes a metal pipe body 2 and a connecting end 3, the wall thickness of the metal pipe body 2 is 20 mm, the metal pipe body 2 is set in the casing 1, and the connecting end 3 is set in the The two ends are welded with the inner wall of the metal pipe body 2, the connecting end 3 is provided with a sha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of PTFE (Poly Tetra Fluoro Ethylene) rubber rollers. The production method comprises the following steps of enabling PTFE resin fine powder to be produced into a blank and placing the blank into a constant temperature furnace; placing the PTFE blank into a sintering furnace; enabling the outer shape, the inner shape and the size of the blank which is taken out to meet the needs of the rubber roller through machining, enabling a steel core of the rubber roller to be machined into a metal core rod and enabling the inner diameter of the blank and the outer diameter of the steel core to be machined according to the size ratio; enabling the size well-processed blank to be uniformly baked under the high temperature, enabling the blank to sleeve the well machined steel core directly after the blank is taken out, enabling the blank to sleeve the steel core firmly in an oil pressure pushing and squeezing mode and then cooling; enabling the steel molding blank which is cooled into the normal temperature to be machined into the various types of rubber rollers according to the figure. The PTFE rubber rollers have the advantages of overcoming the defects that the traditional rubber rollers are short in service life, easy to age and the like, greatly reducing the production cost of rubber roller users and being particularly suitable for industries of papermaking, galvanization, pickling and the like.

Description

technical field [0001] The invention relates to a preparation method of industrial rubber rollers. Background technique [0002] Existing industrial rubber rollers are cored with metal or other materials, and the roll-shaped products made of vulcanized rubber. Due to the poor wear resistance and heat resistance of this industrial rubber roller, corrosion and aging will occur once it is used in a harsh industrial environment, and its mechanical properties are poor, and its service life is short. [0003] Chinese invention patent (application number: 201210351099, application date: September 20, 2012) discloses an industrial rubber roller, including a metal core, the metal core is covered with an outer layer of rubber, and the outer layer of rubber is in contact with the metal A hard rubber layer is arranged between the cores, and a polytetrafluoroethylene film layer is pasted on the outer wall of the outer rubber layer. This patent is only to set a polytetrafluoroethylene f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16C13/00
Inventor 章宁陈岗
Owner 浙江宁奇环保材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com