Preparation method of beta zeolite with multilevel pore canals

A technology of zeolite beta and channels, which is applied in the field of preparation of zeolite beta with multi-stage channels, can solve the problems of high price, complicated preparation process, and difficulty in realizing industrial scale application, and achieve the effects of eliminating influence and saving consumption

Inactive Publication Date: 2015-06-03
EAST CHINA UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In these examples, a notable feature is the use of mesoscopic templates such as mesoporous carbons, polymers, organosilanes, and inorganic nanoparticles in the process of synthesizing zeolites. Complex and difficult to implement on an industrial scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of beta zeolite with multilevel pore canals
  • Preparation method of beta zeolite with multilevel pore canals
  • Preparation method of beta zeolite with multilevel pore canals

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024] 1. Take 32.19 grams of ethyl orthosilicate (28% SiO 2 ), 35.34 grams of tetraethylammonium hydride (25% aqueous solution) and 0.96 grams of sodium hydroxide were stirred at room temperature to obtain a homogeneous solution.

[0025] 2. Take 2 grams of aluminum sulfate octadecahydrate completely dissolved in 20ml of deionized water, add dropwise to the homogeneous solution obtained in 1 while stirring, and stir at a constant temperature of 80°C until a dry gel is obtained.

[0026] 3. Transfer the obtained xerogel into a 100ml hydrothermal kettle and heat it at 140°C for 48 hours, then cool, dry, add 2.4 grams of silane coupling agent (such as vinyltrimethoxysilane, etc.) In the mixture, stir evenly and transfer to a petri dish to dry.

[0027] 4. Transfer the dried solid into a 100ml hydrothermal kettle and heat it at 140°C for 72 hours, then cool, filter, wash, dry, and roast to obtain SiO 2 / Al 2 o 3 50 zeolite with hierarchical channels.

example 2

[0029] 1. Take 32.19 grams of ethyl orthosilicate (28% SiO 2 ), 55.2 grams of tetraethylammonium hydroxide (20% aqueous solution) and 0.96 grams of sodium hydroxide were stirred at room temperature to obtain a homogeneous solution.

[0030] 2. Take 0.40 g of aluminum chloride and completely dissolve it in 20 ml of deionized water, add it dropwise into the homogeneous solution obtained in 1 while stirring, and stir at a constant temperature of 80°C until a xerogel is obtained.

[0031] 3. Transfer the obtained xerogel into a 100ml hydrothermal kettle and heat it at 140°C for 48 hours, then cool, dry, add 2.6 grams of silane coupling agent (such as vinyltrimethoxysilane) and an appropriate amount of ethanol In the mixture, stir evenly and transfer to a petri dish to dry.

[0032] 4. Transfer the dried solid into a 100ml hydrothermal kettle and heat it at 140°C for 72 hours, then cool, filter, wash, dry, and roast to obtain SiO 2 / Al 2 o 3 100 zeolite with hierarchical channe...

example 3

[0034] 1. Get 32.19 grams of silica sol (28% SiO 2 , Shanghai Hengsheng Chemical Industry), 35.34 grams of tetraethylammonium hydroxide (25% aqueous solution) and 0.96 grams of sodium hydroxide, stirred at room temperature to obtain a homogeneous solution.

[0035] 2. Take 0.25 g of aluminum sulfate octadecahydrate and completely dissolve it in 20 ml of deionized water, and add it dropwise to the homogeneous solution obtained in 1 while stirring. After continuing to stir for 2 hours, stir at a constant temperature of 80° C. until a dry gel is obtained.

[0036] 3. Transfer the obtained xerogel into a 100ml hydrothermal kettle and heat it at 140°C for 48 hours, then cool, dry, add 2.6 grams of silane coupling agent (such as vinyltrimethoxysilane) and mix evenly with appropriate amount of ethanol solution, stirred evenly and then transferred to a Petri dish to dry.

[0037] 4. Transfer the dried solid into a 100ml hydrothermal kettle and heat it at 140°C for 72 hours, then coo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of beta zeolite with multilevel pore canals is disclosed by the invention, and comprises: uniformly mixing a silicon source, a tetraethylammonium hydroxide solution, sodium hydroxide and a complete dissolved aluminium source, stirring at a certain constant temperature, and forming a xerogel; carrying out a first hydrothermal treatment for the obtained xerogel, cooling, grinding, and adding a proper amount of a silane coupling agent; and carrying out a second hydrothermal treatment, cooling, filtering, roasting, and obtaining the beta zeolite with multilevel pore canals. The preparation method and the post-processing method are simple, yield is high, and industrial amplification production is easy to realize.

Description

technical field [0001] The invention relates to a method for preparing zeolite with both micropores and mesoporous channels, in particular to synthesizing nanoscale multi-level channel beta zeolite through a solid-phase crystallization method. Background technique [0002] As one of the five major zeolites, β has important industrial application value. It is a zeolite with strong acidity and a three-dimensional 12-membered ring structure. Because it has a three-dimensional macroporous structure and has both acid catalytic properties and reaction selectivity, it has a wide range of applications in petrochemical and fine chemical industries, and shows excellent catalytic performance in many catalytic reactions. [0003] Although traditional molecular sieves have many unique advantages, most of their pores are between 0.5 and 1.3nm, which belong to microporous materials (<2nm). For molecules whose molecular size is larger than their pore diameter, it is often difficult to e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/04
Inventor 周兴贵陈娇朱卡克
Owner EAST CHINA UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com