Groove-priority dual damascene copper interconnection method for reducing coupling capacitance of redundant metal

A redundant metal, trench priority technology, applied in the direction of the photoplate process of circuits, electrical components, patterned surfaces, etc., to achieve the effect of reducing production costs, increasing productivity, and reducing etching steps

Inactive Publication Date: 2013-08-28
SHANGHAI HUALI MICROELECTRONICS CORP
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its cost is much higher than traditional single exposure forming technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Groove-priority dual damascene copper interconnection method for reducing coupling capacitance of redundant metal
  • Groove-priority dual damascene copper interconnection method for reducing coupling capacitance of redundant metal
  • Groove-priority dual damascene copper interconnection method for reducing coupling capacitance of redundant metal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] In order to make the content of the present invention clearer and easier to understand, the content of the present invention will be described in detail below in conjunction with specific embodiments and accompanying drawings.

[0035] Figure 3A to Figure 3ISchematically shows a cross-sectional view of each step of the trench-priority dual damascene copper interconnection method for reducing redundant metal coupling capacitance according to a preferred embodiment of the present invention. The trench-first dual damascene copper interconnect method utilizes double exposure technology and formable hard film photoresist to reduce redundant metal coupling capacitance.

[0036] Specifically, as Figure 3A to Figure 3I As shown, the trench-priority double damascene copper interconnect method for reducing redundant metal coupling capacitance according to a preferred embodiment of the present invention includes:

[0037] The first step: first deposit a dielectric layer 2 on t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a groove-priority dual damascene copper interconnection method for reducing coupling capacitance of redundant metal. According to the groove-priority dual damascene copper interconnection method for reducing the coupling capacitance of the redundant metal, a dielectric layer is firstly deposited on a substrate silicon wafer and then the dielectric layer is coated with first photoresist; metallic grooves are formed in a first photoresist film through exposure and development, and the metallic grooves formed in the first photoresist penetrate through the first photoresist; in the same developing machine, the first photoresist is coated with RELACS to solidify the metallic grooves in the first photoresist, the RELACS can react with the surface of the first photoresist to form an isolating film which can not dissolve in second photoresist under the heating condition, and then the remaining RELACS which does not react with the surface of the first photoresist is removed; the first photoresist on which the isolating film is formed is coated with the second photoresist; a through hole in each metallic groove and a redundant metallic groove located in the first photoresist are formed in a second photoresist film through exposure and development.

Description

technical field [0001] The invention relates to the field of semiconductor manufacturing, and more specifically, the invention relates to a groove-priority double damascene copper interconnection method for reducing redundant metal coupling capacitance. Background technique [0002] As the integration level of semiconductor chips continues to increase, the feature size of transistors continues to shrink. After entering the 130nm technology node, limited by the high resistance characteristics of aluminum, copper interconnection gradually replaces aluminum interconnection and becomes the mainstream of metal interconnection. Since the copper dry etching process is not easy to realize, the manufacturing method of the copper wire cannot be obtained by etching the metal layer like the aluminum wire. The widely used manufacturing method of copper wire is damascene technology called damascene process. [0003] Damascus damascene copper interconnects can be realized through a varie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01L21/768H01L21/027G03F7/00G03F7/40
Inventor 毛智彪
Owner SHANGHAI HUALI MICROELECTRONICS CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap