Marine heavy anticorrosive epoxy aluminum-nickel-rare earth-enriched nano paint and preparation method thereof

A nano-coating and heavy-duty anti-corrosion technology, applied in the field of coatings, can solve the problems of high preparation temperature, achieve the effect of low dosage, improve comprehensive performance, and improve corrosion resistance

Active Publication Date: 2015-03-18
SHANDONG LONGQUAN PIPELINE ENG
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the preparation temperature is still high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A marine heavy-duty epoxy aluminum-nickel-rich rare earth nano-coating, which is composed of two components, A and B, according to a mass ratio of 18:1. In parts by mass, Component A includes the following components and contents:

[0060] 16 parts of E44 epoxy resin;

[0061] 4 parts of hydroxyacrylic resin;

[0062] 140 parts of nano aluminum powder;

[0063] 25 parts of nano nickel powder;

[0064] Rare earth powder 1 part;

[0065] 4 parts of talcum powder;

[0066] 2 parts of barium sulfate;

[0067] 5 parts of organic bentonite powder;

[0068] 1 part soybean lecithin;

[0069] 12 parts of solvent, solvent is that xylene and n-butanol are formulated according to volume ratio 5:1;

[0070] In terms of the ratio of parts by mass, component B includes the following components and content:

[0071] 60 parts of cardanol modified polyamide resins;

[0072] 40 parts of solvent, the solvent is pr...

Embodiment 2

[0078] A marine heavy-duty epoxy aluminum-nickel-rich rare earth nano-coating, which is composed of two components, A and B, according to a mass ratio of 18:1. In parts by mass, Component A includes the following components and contents:

[0079] 14 parts of E44 epoxy resin;

[0080] 3 parts of hydroxyacrylic resin;

[0081] 125 parts of nano aluminum powder;

[0082] 28 parts of nano nickel powder;

[0083] Rare earth powder 1 part;

[0084] 3 parts talcum powder;

[0085] 2 parts barium sulfate;

[0086] 3 parts of organic bentonite powder;

[0087] 1 part soybean lecithin;

[0088] 10 parts of solvent, solvent is xylene and n-butanol according to volume ratio 5:1 preparation;

[0089] In terms of the ratio of parts by mass, component B includes the following components and content:

[0090] 50 parts of cardanol modified polyamide resins;

[0091] 50 parts of solvent, the solvent is prepared from xy...

Embodiment 3

[0097] A marine heavy-duty epoxy aluminum-nickel-rich rare earth nano-coating, which is composed of two components, A and B, according to a mass ratio of 18:1. In parts by mass, Component A includes the following components and contents:

[0098] 18 parts of E44 epoxy resin;

[0099] 6 parts of hydroxyacrylic resin;

[0100] 145 parts of nano aluminum powder;

[0101] 30 parts of nano nickel powder;

[0102] Rare earth powder 2 parts;

[0103] 6 parts of talcum powder;

[0104] 4 parts of barium sulfate;

[0105] 5 parts of organic bentonite powder;

[0106] 2 parts soybean lecithin;

[0107] 13 parts of solvent, solvent is that xylene and n-butanol are formulated according to volume ratio 5:1;

[0108] In terms of the ratio of parts by mass, component B includes the following components and content:

[0109] 60 parts of cardanol modified polyamide resins;

[0110]40 parts of solvent, the solvent is prepared ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses marine heavy anticorrosive epoxy aluminum-nickel-rare earth-enriched nano paint which is prepared from a component A and a component B according to a mass ratio of 18:1, wherein the component A comprises the following components in parts by mass: 14-18 parts of epoxy resin, 3-6 parts of hydroxy acrylic resin, 125-145 parts of nano aluminum powder, 25-30 parts of nano nickel powder, 1-2 parts of rare earth powder, 3-6 parts of talcum powder, 2-4 parts of barium sulfate, 3-5 parts of anti-settling aid, 1-2 parts of dispersing aid and 10-13 parts of solvent; and the component B comprises the following components in parts by mass: 50-60 parts of curing agent and 40-50 parts of solvent. The invention also discloses a preparation method of the paint. According to the invention, the nano aluminum powder content in a paint film is high, the cost is low, the process is simple, and no special equipment is needed. A coating prepared by the invention has high matrix binding force, favorable binding force with other various additional coatings, excellent corrosion resistance in the marine atmospheric environment and long service life. Thus, the paint disclosed by the invention can be used as heavy anticorrosive paint for steel structures such as drilling platforms, bridges and the like in the marine atmospheric environment.

Description

technical field [0001] The invention relates to a coating technology, in particular to a marine heavy-duty anti-corrosion epoxy aluminum-nickel-rich rare earth nano coating and a preparation method thereof. Background technique [0002] At present, metal corrosion is a very serious problem. It is roughly estimated that the annual loss of metal structures, equipment and materials due to corrosion is approximately equivalent to 20%-40% of the metal output of the year, and more than 100 million tons of metals are scrapped due to corrosion every year in the world, and the economic loss accounts for 100% of the national total. 1.5%-3.5% of the total economic output value. In China, the economic loss caused by metal corrosion is as high as more than 30 billion yuan per year, accounting for 4% of the gross national product. Especially the marine corrosion in the marine environment, the corrosion of metal and other components in the marine environment, the harm it causes is very s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D133/00C09D7/12C09D5/10
Inventor 邢士波李晓刚李丽崔国华董超芳杨体绍
Owner SHANDONG LONGQUAN PIPELINE ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap