Asphalt polymer cement waterproof coating

A waterproof coating and polymer technology, applied in the field of asphalt-based waterproof coatings, can solve the problems of affecting the waterproof function of polymer waterproof coatings, unable to use waterproof roofing, short service life, etc., and achieve low price, good waterproofness, and excellent construction. Effect

Active Publication Date: 2013-07-03
KUNMING FENGXING WATERPROOF MATERIAL
View PDF2 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, polymer cement-based waterproof materials still have poor water resistance and short service life, so they cannot be used for second-level and above waterproof roofs and important waterproof projects.
When acrylate polymer emulsion is used as the liquid material of polymer cement waterproof coating, there are disadvantages such as poor water resistance, which affects the waterproof function of polymer waterproof coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt polymer cement waterproof coating
  • Asphalt polymer cement waterproof coating
  • Asphalt polymer cement waterproof coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The emulsified asphalt raw materials in the invented product are proportioned according to the following (Table 1) (weight ratio, the same below):

[0041] Table 1 Formula table of emulsified asphalt (100 parts of emulsified asphalt)

[0042]

[0043] The manufacturing process of emulsified asphalt is as follows:

[0044] (1) Dehydrate the asphalt at 110°C-130°C for 1 hour to 2 hours, then heat it gently to 130°C-160°C, and measure it for later use;

[0045] (2) Heat the tap water to 45°C-65°C and measure it for later use;

[0046] (3) Add the emulsifier and stabilizer to the standby hot water, stir evenly to make an emulsified aqueous solution, control the temperature at 45°C-65°C, and set aside;

[0047] (4) Turn on the emulsifier system, pour the emulsified aqueous solution that meets the temperature requirements into the emulsification, and immediately pour in the hot asphalt that meets the temperature requirements, and the emulsified asphalt that meets the req...

Embodiment 2

[0059] Proportion the emulsified asphalt raw materials according to the following (Table 4) (weight ratio, the same below):

[0060] Table 4 Formula of emulsified asphalt (100 parts of emulsified asphalt)

[0061]

[0062]

[0063] The emulsified asphalt manufacturing process of embodiment 2 is as embodiment 1

[0064] Then the raw materials in the invention product are proportioned (weight ratio, the same below) as follows (Table 5):

[0065] Table 5 A component of asphalt polymer cement waterproof coating (100 coatings)

[0066] emulsified asphalt Modified Latex 1 Modified latex 2 water Example 1 Pure acrylic latex Styrene Acrylic Latex tap water 40 30 15 15

[0067] Table 6 B component of asphalt polymer cement waterproof coating (100 parts of coating)

[0068] cement filler 1 filler 2 Auxiliary White cement calcium carbonate wollastonite Superplasticizer 50 30 18 2

[0069] The manufacturing...

Embodiment 3

[0071] Proportion the emulsified asphalt raw materials according to the following (Table 7) (weight ratio, the same below):

[0072] Table 7 Emulsified asphalt formula table (100 parts emulsified asphalt)

[0073]

[0074]

[0075] The emulsified asphalt manufacturing process of embodiment 3 is as embodiment 1

[0076] Then the raw materials in the invented product are proportioned according to the following (Table 8) (weight ratio, the same below):

[0077] Table 8 A component of asphalt polymer cement waterproof coating (100 coatings)

[0078]

[0079] Table 9 B component of asphalt polymer cement waterproof coating (100 coatings)

[0080] cement filler 1 filler 2 Auxiliary White cement calcium carbonate talcum powder Superplasticizer 50 33 15 2

[0081] The manufacturing process of the asphalt polymer cement waterproof coating of embodiment 3 is as embodiment 1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an asphalt polymer cement waterproof coating which consists of a component A and a component B. The component A comprises the raw materials in percentage by weight as follows: 20-50% of emulsified asphalt, 30-50% of modified latex and 10-30% of water. The component B comprises the raw materials in percentage by weight as follows: 40-60% of cement, 20-40% of staffing and 1-5% of assistant. The coating provided by the invention is low in price, good in waterproofness and good in flexibility, and can resist corrosion caused by low concentration inorganic acid, base and salt. The asphalt polymer cement waterproof coating can be independently used as a film waterproof layer in waterproof and corrosion resisting projects of kitchens and bath rooms, basements and bridge floors.

Description

technical field [0001] The invention relates to an asphalt-based waterproof coating, which is mainly used for coatings in the field of waterproof and anticorrosion, in particular to an asphalt polymer cement waterproof coating. technical background [0002] At present, polymer cement-based waterproof materials still have poor water resistance and short service life, and cannot be used for second-level and above waterproof roofs and important waterproof projects. When the acrylate polymer emulsion is used as the liquid material of the polymer cement waterproof coating, there are disadvantages such as poor water resistance, which affects the waterproof function of the polymer waterproof coating. Asphalt has the advantages of wide source of materials, low price, low-concentration inorganic acid, alkali and salt corrosion, and it is waterproof and self-healing to a certain extent. Contents of the invention [0003] This product is an anti-leakage and anti-corrosion bituminous...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04
Inventor 常英刘金景
Owner KUNMING FENGXING WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com