Antistatic nylon textile

A textile and antistatic technology, applied in the field of nylon textiles, can solve the problems of non-antistatic, complex process, unimproved water and oil repellency and durability, etc., achieve soft hand feeling, superior washing durability, and simple processing method easy effect

Active Publication Date: 2013-06-26
TORAY IND INC
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of method is simple and easy to operate, but its antistatic effect is not long-lasting, especially in low-humidity environments; (2) Using blended interweaving to mix conductive fibers into nylon textiles, this method has stable conductivity and is not limited by climatic conditions , but it involves physical and mechanical processing, the process is complicated, and the finished product feels bad
Generally, after oil-repellent and water-repellent treatment, the fibers are hydrophobic and do not have antistatic properties.
[0004] Chinese patent CN101492885 discloses an antistatic film-like resin-wrapped fiber containing polyamide textiles. The surface of the single fiber of the textile is wrapped with an antistatic film-like resin layer. After washing 20 times according to the JIS L 0217 No. 103 standard According to the JIS L 1094 standard, the friction band voltage of the textile is below 3000V. This patent solves the antistatic and durability problems of nylon textiles by adding conductive particles to film-forming agents such as polyether polyurethane, and does not improve Its water and oil repellency and its durability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic nylon textile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] ① Preparation of fiber textiles: Nylon (100%) thin woven fabric

[0037] ② Working fluid preparation:

[0038] Hydrophilic film-forming agent (polyether-type hydrophilic polyurethane resin) 40g / L

[0039] Water and oil repellent film former (fluorine resin) 20g / L

[0040] Catalyst PARASIN-U (Qingdao Dayuan Chemical) 4g / L

[0041] The balance is soft water

[0042] ③ processing

[0043] After dyeing the prepared nylon (100%) thin woven fabric, use the above-mentioned working solution for padding processing (rolling liquid rate 35%), and then treat it in a steamer (saturated steam 105 ° C × 10 minutes), and finally use Hot air type common needle plate setting machine (175°C × 45 seconds) for setting to obtain the antistatic nylon textile of the present invention, the surface of the single fiber of the obtained textile is covered with a film resin layer, and the film resin layer is produced by the terminal group of the nylon fiber. It is formed of cross-linked poly...

Embodiment 2

[0045] ① Preparation of fiber textiles: Nylon (100%) thin woven fabric

[0046] ② Working fluid preparation:

[0047] Hydrophilic film-forming agent (polyether-type hydrophilic polyurethane resin) 50g / L

[0048] Water and oil repellent film former (fluorine resin) 30g / L

[0049] Catalyst PARASIN-U (Qingdao Dayuan Chemical) 5g / L

[0050] The balance is soft water

[0051] ③ processing

[0052] After dyeing the prepared nylon (100%) thin woven fabric, use the above-mentioned working solution for padding processing (rolling liquid rate 35%), and then treat it in a steamer (saturated steam 105 ° C × 10 minutes), and finally use Hot air type ordinary needle plate setting machine (175°C×45 seconds) for setting to obtain the antistatic nylon textile of the present invention, the surface of the single fiber of the obtained textile is covered with a film resin layer, and the film resin layer is formed by the terminal group of the nylon fiber. It is formed of cross-linked polyether...

Embodiment 3

[0054] ① Preparation of fiber textiles: Nylon (100%) thin woven fabric

[0055] ② Working fluid preparation:

[0056] Hydrophilic film-forming agent (polyether-type hydrophilic polyurethane resin) 60g / L

[0057] Water and oil repellent film former (fluorine resin) 40g / L

[0058] Catalyst PARASIN-U (Qingdao Dayuan Chemical) 6g / L

[0059] The balance is soft water

[0060] ③ processing

[0061] After dyeing the prepared nylon (100%) thin woven fabric, use the above-mentioned working solution for padding processing (rolling liquid rate 35%), and then treat it in a steamer (saturated steam 105 ° C × 10 minutes), and finally use Hot air type common needle plate setting machine (175°C × 45 seconds) for setting to obtain the antistatic nylon textile of the present invention, the surface of the single fiber of the obtained textile is covered with a film resin layer, and the film resin layer is produced by the terminal group of the nylon fiber. It is formed of cross-linked polyet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antistatic nylon textile. A coating resin layer is covered on the single-fiber surface of the textile, and the coating resin layer is formed by polyether type polyurethane resin and fluorine-based resin, which perform cross-linking reaction with a terminal group of nylon fiber. The initial friction-charged electrostatic potential of the textile is below 2000V, the water repellent degree is above grade 4, and the oil repellent degree is above grade 4; and the friction-charged electrostatic potential after 20 times of family washing is below 2500V, the water repellent degree is above grade 3, and the oil repellent degree is above grade 3. The antistatic nylon textile disclosed by the invention fills in the blank that the nylon textile can not integrate the antistatic performance and the water-repellent and oil-repellent performance simultaneously.

Description

technical field [0001] The invention relates to a nylon textile with antistatic properties, in particular to a nylon textile with antistatic, water-repellent and oil-repellent properties and excellent washing durability. Background technique [0002] Nylon textiles have properties such as friction resistance, bending deformation resistance, low wrinkle resistance, and quick drying after moisture absorption, and are widely used in various fields such as clothing, carpets, towels, artificial leather, fishing nets, and fishing lines. However, its poor antistatic property and water and oil repellency have brought a lot of inconvenience to use. [0003] It is very difficult to have two opposite properties of antistatic and water repellency and oil repellency at the same time and have washing durability, and it is extremely difficult to keep both properties within a good performance range. Nylon textiles currently on the market only have one of antistatic or oil-repellent and wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/568D06M15/00D06M101/34
Inventor 刘春燕符晔清水壮夫
Owner TORAY IND INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com