Ceramic bond gross blow hole repairing grinding wheel and manufacturing method thereof

A technology of ceramic bond and large pores, which is used in ceramic products, grinding/polishing equipment, abrasives, etc., can solve problems such as inability to enter actual grinding, avoid weak bonding, ensure use strength, and increase discharge. The effect of chip speed

Active Publication Date: 2015-07-15
江苏新砺河磨具科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the porosity of the vitrified bond macroporous grinding wheel developed in my country can only reach 45%, and the pore size is mostly below 0.3mm. When grinding rails, the workpiece is burned by greasy iron, which exceeds the allowable force range of the grinding control system. However, the grinding is automatically stopped, and it is impossible to enter the actual grinding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic bond gross blow hole repairing grinding wheel and manufacturing method thereof
  • Ceramic bond gross blow hole repairing grinding wheel and manufacturing method thereof
  • Ceramic bond gross blow hole repairing grinding wheel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing a vitrified large-pore grinding wheel, the preparation steps are as follows: (1) First prepare a vitrified bond, put 18 parts of clay powder, 63 parts of feldspar powder and 14 parts of boron glass powder in a ceramic pot In the ball mill, add Φ10-15mm ceramic balls accounting for 15% of the mass of the mixture, and then perform ball milling at a speed of 960r / min for 4 hours, and pack the material into bags for later use; Pretreatment: Put the walnut shell particles into the countercurrent mixer, then add liquid phenolic resin PF2127, the mass ratio of walnut shell particles and liquid phenolic resin PF2127 is 100:15, then stir for 5 minutes to mix well, until the walnut shell particles are completely wetted Evenly placed in a metal container, dried at 80°C for 20 minutes, then passed through a 12-mesh sieve, and finally hardened in an oven at 180°C for 20 minutes, and sealed for later use after cooling; (3) Processing process: core: 100 parts of ...

Embodiment 2

[0024] A method for preparing a vitrified large-pore grinding wheel, the preparation steps are as follows: (1) First prepare a vitrified bond, put 20 parts of clay powder, 65 parts of feldspar powder and 15 parts of boron glass powder in a ceramic pot In the ball mill, add Φ10-15mm ceramic balls accounting for 18% of the mass of the mixture, and then perform ball milling at a speed of 960r / min for 5 hours, and pack the material into bags for later use; Pretreatment: Put the walnut shell particles into the countercurrent mixer, then add liquid phenolic resin PF2127, the mass ratio of walnut shell particles and liquid phenolic resin PF2127 is 100:18, then stir for 8 minutes to mix well, until the walnut shell particles are completely wetted Evenly placed in a metal container, dried at 90°C for 25 minutes, then passed through a 12-mesh sieve, and finally hardened in an oven at 180°C for 25 minutes, and sealed for later use after cooling; (3) Processing process: core: 100 parts of ...

Embodiment 3

[0026]A method for preparing a vitrified large-pore grinding wheel, the preparation steps are as follows: (1) First prepare a vitrified bond, put 22 parts of clay powder, 67 parts of feldspar powder and 16 parts of boron glass powder in a ceramic pot In the ball mill, add Φ10-15mm ceramic balls accounting for 20% of the mass of the mixture, and then perform ball milling at a speed of 960r / min for 6 hours, and pack the material into bags for use; Pretreatment: Put the walnut shell particles into the countercurrent mixer, then add liquid phenolic resin PF2127, the mass ratio of walnut shell particles and liquid phenolic resin PF2127 is 100:20, then stir for 10 minutes to mix well, until the walnut shell particles are completely wetted Evenly placed in a metal container, dried at 100°C for 30 minutes, then passed through a 12-mesh sieve, and finally hardened in an oven at 180°C for 30 minutes, and sealed for later use after cooling; (3) Processing process: core: 100 parts of parti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic bond gross blow hole repairing grinding wheel and a manufacturing method thereof. The gas hole ratio of the grinding portion of a grinding wheel can be more than 50%, so that the scrap discharging speed in steel rail grinding can be increased, and a burn phenomenon on the surface of a steel rail is avoided. The grinding wheel is not broken in a rotating testing speed of 60 m / s, namely the strength of the grinding wheel is greater than a using speed of 35 m / s by 1.7 times. The using strength of the grinding wheel is guaranteed, the grinding condition of undulations in repairing and grinding of the steel rail is obtained, and the grinding efficiency of a steel rail milling car and the durability of the grinding wheel are improved.

Description

technical field [0001] The invention relates to a dressing grinding wheel and a preparation method thereof, in particular to a vitrified bond macroporous grinding wheel and a preparation method thereof, belonging to the technical field of special abrasive tool manufacturing. Background technique [0002] When grinding the rails along the railway line, the milling and grinding car is usually used to mill the rail surface first and then grind it. That is, the milling cutter disc composed of milling cutters is used to rough the surface of the rail, and then the grinding wheel is used for precise grinding. Most of the special grinding wheels for rail grinding in the prior art are resin-bonded coarse grinding wheels, which belong to the grinding method of vertical shaft grinding, that is, the grinding wheel faces the rail tread for grinding. The domestic grinding wheel industry has conducted in-depth research on resin-bonded vertical grinding wheels, and has basically mastered t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D3/14B24D18/00C04B38/06C04B28/26
Inventor 仲怀民袁春晓
Owner 江苏新砺河磨具科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com