Cunninghamia lanceolata cultivation compound substrate and preparation method for same

A technology of composite matrix and Chinese fir, which is applied in the direction of fertilizer mixture, preparation of organic fertilizer, organic fertilizer, etc., can solve the problems of waste of resources, and achieve the effects of benefiting growth, less total nutrient loss, and improving survival rate

Inactive Publication Date: 2014-07-30
GUANGXI FORESTRY RES INST
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] During the processing of fir, a large amount of bark and sawdust are produced, among which the sawdust is mostly used to grow mushrooms, and the bark is completely discarded, resulting in a waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cunninghamia lanceolata cultivation compound substrate and preparation method for same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Mix 100 parts by weight of 3-mesh fir bark powder, 200 parts by weight of tung bran, 10 parts by weight of calcium magnesium phosphate fertilizer, 0.05 part by weight of slaked lime powder, 0.04 part by weight of enzyme agent, and 0.1 part by weight of corn flour, mix well, add water, cover Plastic film stacking and retting for 15 days to obtain fermented Chinese fir bark powder for subsequent use.

[0025] Mix 100 parts by weight of 8-mesh fir bark powder, 2 parts by weight of urea, 0.02 parts by weight of slaked lime powder, and 0.01 parts by weight of 95% dexon wettable powder, mix well, replenish water, cover plastic film and stack retting for 20 days to obtain adsorption Fir bark powder for later use.

[0026] Mix 10 parts by weight of rice bran, 0.01 part by weight of milk boletus agent and 0.01 part by weight of boletus fructus agent, mix well, add water, and cultivate for 10 days to obtain amplified ectomycorrhizal fungus for use.

[0027] Mix 2 parts by weight...

Embodiment 2

[0029] Mix 100 parts by weight of 5-mesh fir bark powder, 200 parts by weight of tung bran, 10 parts by weight of calcium magnesium phosphate fertilizer, 0.05 part by weight of slaked lime powder, 0.04 part by weight of enzyme agent, and 0.1 part by weight of corn flour, mix well, replenish water, cover Plastic film stacking and retting for 18 days to obtain fermented Chinese fir bark powder for subsequent use.

[0030] Mix 100 parts by weight of 10-mesh fir bark powder, 2 parts by weight of urea, 0.02 parts by weight of slaked lime powder, and 0.01 parts by weight of 95% dexon wettable powder, mix well, replenish water, cover plastic film and stack retting for 25 days to obtain adsorption Fir bark powder for later use.

[0031] Mix 10 parts by weight of rice bran, 0.01 part by weight of milk boletus agent and 0.01 part by weight of boletus fructus agent, mix well, replenish water, cultivate for 13 days, and obtain amplified ectomycorrhizal fungus for use.

[0032] Mix 3 part...

Embodiment 3

[0034] Mix 100 parts by weight of 4 mesh fir bark powder, 200 parts by weight of tung bran, 11 parts by weight of calcium magnesium phosphate fertilizer, 0.06 parts by weight of slaked lime powder, 0.05 parts by weight of enzyme agent, and 0.2 parts by weight of corn flour, mix well, replenish water, cover Plastic film stacking and retting for 20 days to obtain fermented Chinese fir bark powder for subsequent use.

[0035] Mix 100 parts by weight of 9-mesh fir bark powder, 2.5 parts by weight of urea, 0.02 parts by weight of slaked lime powder, and 0.01 parts by weight of 95% dexon wettable powder, mix well, replenish water, cover plastic film and stack retting for 30 days to obtain adsorption Fir bark powder for later use.

[0036] Mix 10 parts by weight of rice bran, 0.01 part by weight of milk boletus agent and 0.01 part by weight of boletus fructus agent, mix well, replenish water, cultivate for 15 days, and obtain amplified ectomycorrhizal fungus for use.

[0037] Mix 4 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cunninghamia lanceolata cultivation compound substrate and a preparation method for the same. The substrate comprises the following raw materials in parts by weight: 200 parts of cunninghamia lanceolata skin powder, 200-220 parts of tung bran, 0.1-1.2 parts of corn flour, 10-11 parts of rice bran, 0.07-0.08 parts of slaked lime powder, 0.04-0.05 parts of enzyme microorganism agent, 0.01-0.02 parts of suillus bovines agent, 0.01-0.02 parts of coletus luridus, 10-11 parts of calcium magnesium phosphate fertilizer, 2.0-2.5 parts of urea, and 0.01 part of 95% dexon wettable powder. The preparation method comprises the following steps of: crushing cunninghamia lanceolata skins, performing fermentation and adsorption treatments, performing ectotrophic mycorrhiza amplification, compounding, and thus obtaining the cunninghamia lanceolata cultivation compound substrate. With the adoption of the substrate, wood processing remains can be adequately utilized, thus being environment-friendly and reducing seedling culture cost; the use of quick-acting fertilizers and pesticides is reduced, thus reducing pollution, avoiding soil hardening and salinization, enhancing the biological activity of soil system, and building up fertility; seedlings are fast in growth, nursery stocks are good in quality, and the survival rate of afforestation is high; and the substrate is good in economic benefits, social benefits and ecological benefits.

Description

technical field [0001] The invention belongs to the technical field of plant cultivation, and relates to a fir cultivation composite substrate and a preparation method thereof. Background technique [0002] Chinese fir (Cunninghamialanceolata) grows rapidly, has excellent materials, is easy to process, and has a wide range of uses. It is one of the important fast-growing timber tree species in South China. The existing Chinese fir forest area in Guangxi exceeds 1.25 million hectares, and more than 500,000 mu of forests are renewed every year, requiring a large number of afforestation seedlings. [0003] During the processing of Chinese fir, a large amount of bark and sawdust are produced. Most of the sawdust is used to grow mushrooms, while the bark is completely discarded, resulting in a waste of resources. Some studies have found that bark powder can be used as a growing substrate. Such as: fir light matrix net bag container seedling cultivation technology, is to apply 6...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C05G3/00C05F17/00
CPCY02W30/40
Inventor 黄开勇蓝肖韦华郝海坤戴俊劳广杰何振革谭文婧
Owner GUANGXI FORESTRY RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products