Manufacturing method for lightweight wall colorful asphalt brick

A production method and asphalt brick technology are applied in the field of building material wall tiles, which can solve the problems of inconvenient shipping and use, poor waterproof effect, deformation, etc., and achieve the effects of good waterproof effect, beautiful texture and convenient decoration.

Inactive Publication Date: 2013-06-12
杭州海博建材有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Traditional wall tiles are made of glaze, cement, terrazzo and marble, and ceramic tiles. Glazed wall tiles and ceramic tiles are fragile and fragile. It is easy to slip, and the wall tiles made of cement, as well as terrazzo and marble are bulky, heavy, and inconvenient to ship and use. However, the existing colored rubber floor tiles, especially the floor tiles made of waste rubber, are still in the color of waste rubber. The black color can only be painted with various colors on its surface, which affects the appearance. After the colored rubber floor tiles are synthesized and pressed, due to the poor combination between the particles, the wall tiles made lack a certain hardness and will be bent after bending. cracked, broken, deformed, and poor waterproof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: a kind of preparation method of light-weight wall surface colorful asphalt brick, its steps are as follows:

[0027] (1), first select the ratio of 10# asphalt and 100# asphalt, the weight ratio of each group of raw materials is: 10# asphalt 50%, 100# asphalt 50%;

[0028] (2) In the mixture of 10# asphalt and 100# asphalt after mixing, inject 250 degrees Celsius heat conduction oil and heat and stir to raise the temperature of the mixture to 230 degrees Celsius;

[0029] (3) Then add PP polymer plastic particles and SBS elastomer materials for strengthening treatment, heat preservation and stirring for 2 hours, then add calcium bicarbonate raw materials, heat preservation and stirring for 2 hours, when the temperature reaches 190 degrees Celsius, take it out and inject the temperature of oil inside In an oil pan at 200 degrees Celsius;

[0030] (4) Dip-coat the mixture taken out of the oil pan on the surface of the glass fiber mat after grilling at a hig...

Embodiment 2

[0032] Embodiment 2: a kind of preparation method of light-weight wall surface colorful asphalt brick, its steps are as follows:

[0033] A method for making light-weight wall surface colorful asphalt bricks, the steps are as follows:

[0034] (1), first select the ratio of 10# asphalt and 100# asphalt, the weight ratio of each group of raw materials is: 10# asphalt 55%, 100# asphalt 45%;

[0035] (2) In the mixture of 10# asphalt and 100# asphalt after mixing, inject 250 degrees Celsius heat conduction oil and heat and stir to raise the temperature of the mixture to 230 degrees Celsius;

[0036] (3) Then add PP polymer plastic particles and SBS elastomer materials for strengthening treatment, heat preservation and stirring for 2 hours, then add calcium bicarbonate raw materials, heat preservation and stirring for 2 hours, when the temperature reaches 190 degrees Celsius, take it out and inject the temperature of oil inside In an oil pan at 200 degrees Celsius;

[0037] (4) ...

Embodiment 3

[0039] Embodiment 3: a kind of preparation method of light-weight wall surface colorful asphalt brick, its steps are as follows:

[0040] A method for making light-weight wall surface colorful asphalt bricks, the steps are as follows:

[0041] (1), first select the ratio of 10# asphalt and 100# asphalt, the weight ratio of each group of raw materials is: 10# asphalt 60%, 100# asphalt 40%;

[0042] (2) In the mixture of 10# asphalt and 100# asphalt after mixing, inject 250 degrees Celsius heat conduction oil and heat and stir to raise the temperature of the mixture to 230 degrees Celsius;

[0043] (3) Then add PP polymer plastic particles and SBS elastomer materials for strengthening treatment, heat preservation and stirring for 2 hours, then add calcium bicarbonate raw materials, heat preservation and stirring for 2 hours, when the temperature reaches 190 degrees Celsius, take it out and inject the temperature of oil inside In an oil pan at 200 degrees Celsius;

[0044] (4) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Graininessaaaaaaaaaa
Graininessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method for a lightweight wall colorful asphalt bricks. The method comprises the steps of selecting 10 # asphalt and 100 # asphalt and proportioning the 10 # asphalt and the 100 # asphalt according to a weight ratio of 50%-60% of the 10 # asphalt and 40%-50% of the 100 # asphalt; injecting conduction oil to the selected 10 # asphalt and 100 # asphalt, heating to a temperature of 200 DEG C-230 DEG C with stirring; adding PP polymer plastic particles and SBS elastomer materials for reinforcement treatment, stirring for 1-2 hours, adding a calcium bicarbonate raw material, stirring for 1-2 hours, taking out when the temperature reaches 180 DEG C-190 DEG C and injecting to an oil pot; performing double-faced dip coating by using a glass fiber blanket as a base matrix after the asphalt is taken out; coating colorful sand particles on the front surface and scattering isolation ore sand on the back surface after dip coating; cooling and cutting into the lightweight wall colorful asphalt bricks. The lightweight wall colorful asphalt bricks manufactured by the method have light mass, are waterproof and have beautiful appearance. The lightweight wall colorful asphalt bricks solve the problems that conventional wall ground tiles have ponderous in shapes, poor waterproof effect and inaesthetic appearance, and are not suitable for decorations.

Description

[0001] technical field [0002] The invention relates to a building material wall brick, in particular to a method for making a light-weight colorful asphalt brick for the wall. [0003] Background technique [0004] Traditional wall tiles are made of glaze, cement, terrazzo and marble, and ceramic tiles. Glazed wall tiles and ceramic tiles are fragile and fragile. It is easy to slip, and the wall tiles made of cement, as well as terrazzo and marble are bulky, heavy, and inconvenient to ship and use. However, the existing colored rubber floor tiles, especially the floor tiles made of waste rubber, are still in the color of waste rubber. The black color can only be painted with various colors on its surface, which affects the appearance. After the colored rubber floor tiles are synthesized and pressed, due to the poor combination between the particles, the wall tiles made lack a certain hardness and will be bent after bending. Crack, break, deform, and poor waterproofing. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C70/40B29C70/54
Inventor 周春荣
Owner 杭州海博建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com