Molecularly imprinted membrane for chiral separation and preparation method thereof

A molecularly imprinted membrane, chiral separation technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of affinity elution and recombination cannot be effectively controlled, the size of affinity regulation and other problems, to achieve production Low cost, simple preparation method and good desorption effect

Inactive Publication Date: 2013-03-13
TIANJIN POLYTECHNIC UNIV
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for certain molecularly imprinted membranes and template molecules, the magnitude of this affinity is difficult to adjust according to needs, so that the influence of affinity on elution and recombination cannot be effectively controlled.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034](1) Prepare a 2.5mol / L KOH alkali solution, add 2g / L tetrabutylammonium bromide to it, put the PVDF hollow fiber membrane into the prepared alkali solution and treat it at 40°C for 5min, after alkali treatment , soak the membrane in absolute ethanol for use;

[0035] (2) Preparation of pre-polymerization solution:

[0036] 1) D-naproxen is added in dehydrated alcohol and fully stirred to make it to dissolve completely, is configured into the solution that D-naproxen concentration is 0.1mol / L, and the mass ratio of described D-naproxen and PVDF is 0.05:1;

[0037] 2) Add functional monomer N-isopropylacrylamide (NIPAAm) to the solution in step 1), stir thoroughly for 4 hours, and prepare a solution with a concentration of N-isopropylacrylamide of 1 mol / L;

[0038] 3) Slowly add the cross-linking agent ethylene glycol dimethacrylate (EGDMA) to the solution in step 2), blow nitrogen gas for 10 minutes while stirring, and configure a solution with a concentration of ethyle...

Embodiment 2

[0043] (1) Prepare a 2.5mol / L KOH alkali solution, add 2g / L tetrabutylammonium bromide to it, put the PVDF hollow fiber membrane into the prepared alkali solution and treat it at 75°C for 8min, after alkali treatment , soak the membrane in absolute ethanol for use;

[0044] (2) Preparation of pre-polymerization solution:

[0045] 1) D-naproxen is added in dehydrated alcohol and fully stirred to make it to dissolve completely, is configured into the solution that D-naproxen concentration is 0.2mol / L, and the mass ratio of described D-naproxen and PVDF is 0.25:1;

[0046] 2) Add functional monomer N-isopropylacrylamide (NIPAAm) to the solution in step 1), stir thoroughly for 9 hours, and prepare a solution with a concentration of N-isopropylacrylamide of 1 mol / L;

[0047] 3) Slowly add the cross-linking agent ethylene glycol dimethacrylate (EGDMA) to the solution in step 2), blow nitrogen gas for 10 minutes while stirring, and configure a solution with a concentration of ethyl...

Embodiment 3

[0052] (1) Prepare a 2.5mol / L KOH alkali solution, add 4g / L tetrabutylammonium bromide to it, put the PVDF hollow fiber membrane into the prepared alkali solution and treat it at 50°C for 5min, after alkali treatment , soak the membrane in absolute ethanol for use;

[0053] (2) Preparation of pre-polymerization solution:

[0054] 1) D-naproxen is added in dehydrated alcohol and fully stirred to make it to dissolve completely, is configured into the solution that D-naproxen concentration is 0.15mol / L, and the mass ratio of described D-naproxen and PVDF is 0.15:1;

[0055] 2) Add functional monomer N-isopropylacrylamide (NIPAAm) to the solution in step 1), stir thoroughly for 6 hours, and prepare a solution with a concentration of N-isopropylacrylamide of 1 mol / L;

[0056] 3) Slowly add the cross-linking agent ethylene glycol dimethacrylate (EGDMA) to the solution in step 2), blow nitrogen gas for 10 minutes while stirring, and configure a solution with a concentration of ethy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a molecularly imprinted membrane with a selective-separation chiral drug and a preparation method of the membrane. According to the invention, D-naproxen is taken as template molecules, a PVDF (Polyvinylidene Fluoride) hollow fiber separation membrane is taken as a base material, and the D-naproxen imprinted molecules are packaged in a fenestra grafting gel layer in a surface finish process to prepare the D-naproxen imprinted PVDF hollow fiber membrane. The molecularly imprinted separation membrane prepared by the method has good adsorption and separation functions to naproxen chiral drug molecules, has a desorption rate up to 90%-95.78%, can realize the intelligent regulation and control on combination and release of D-naproxen and solves the problem of uncontrollability on the shape and size of cavities and the affinity of template molecules of the conventional molecularly imprinted membrane. According to the invention, the mature PVDF hollow fiber membrane on the market is taken as a base membrane of the molecularly imprinted membrane, and an N-isopropyl acrylamide monomer (NIPAAm) of the conventional thermo-sensitive hydrogel is taken as a functional monomer; and the preparation method is simple, low in production cost as not needing special equipment, and suitable for industrialized application.

Description

technical field [0001] The invention belongs to the field of functional polymer materials, and in particular relates to a molecularly imprinted membrane capable of selectively separating chiral drugs and a preparation method thereof. The membrane can be applied to the field of separating chiral drugs of naproxen. Background technique [0002] Naproxen is a non-steroidal anti-inflammatory, antipyretic, and analgesic drug. It is mainly used for the treatment of rheumatoid arthritis, rheumatic spondylitis, and postoperative pain relief. It is one of the most widely used prescription drugs in the world. one. Naproxen exists a pair of optically active enantiomers (D-naproxen and L-naproxen), wherein D-naproxen has therapeutic effect, while L-naproxen can bring great pain of. However, during the synthesis of naproxen, D-naproxen and L-naproxen are often mixed together, and the anti-inflammatory activity of D-naproxen in the body is more than 30 times that of L-naproxen. It is o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/29B01J20/30
Inventor 赵义平张未来王霞李金苓陈莉申向
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap