Reclaimed polypropylene (PP)-based wood-plastic composite material and preparation method thereof

A wood-plastic composite material and premix technology, which is applied in the field of wood-plastic composite materials to achieve the effects of easy control, good wood imitation effect and energy saving

Inactive Publication Date: 2012-11-28
SINOPLAST NEW MATERIAL
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In situ reactive compatibilization of natural plant fibers and plastic matrices by melt grafting has not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reclaimed polypropylene (PP)-based wood-plastic composite material and preparation method thereof
  • Reclaimed polypropylene (PP)-based wood-plastic composite material and preparation method thereof
  • Reclaimed polypropylene (PP)-based wood-plastic composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A recycled PP-based wood-plastic composite material, which is made of the following raw materials in parts by weight: 70 parts of recycled PP; 30 parts of walnut shell powder, the sum of the weight parts of recycled PP and walnut shell powder is 100; dicumyl peroxide 0.1 part; 2 parts of glycidyl methacrylate; 1 part of styrene.

[0056] A preparation method for reclaiming PP-based wood-plastic composite material, the method comprising the following steps:

[0057] (1), walnut shells are pulverized, ground into powder, the particle size is 150 mesh, placed in a vacuum oven for drying treatment, the temperature of the oven is controlled at 120 ° C, dried for 6 hours, and then cooled to room temperature;

[0058] (2), dicumyl peroxide, glycidyl methacrylate, and styrene are dissolved in diluent ethanol, and placed for subsequent use;

[0059] (3) Mix the dried walnut shell powder and recycled PP evenly in proportion, pour the mixed solution in step (2) into the mixture o...

Embodiment 2

[0064] A recycled PP-based wood-plastic composite material is prepared from the following raw materials in parts by weight: 60 parts of recycled PP; 40 parts of walnut shell powder, the sum of the weight parts of recycled PP and walnut shell powder is 100; 0.2 parts of dicumyl peroxide parts; 4 parts of glycidyl methacrylate; 2 parts of styrene.

[0065] A preparation method for reclaiming PP-based wood-plastic composite material, the method comprising the following steps:

[0066] (1), walnut shells are pulverized, ground into powder, the particle size is 150 mesh, placed in a vacuum oven for drying treatment, the temperature of the oven is controlled at 120 ° C, dried for 6 hours, and then cooled to room temperature;

[0067] (2), dicumyl peroxide, glycidyl methacrylate, and styrene are dissolved in diluent ethanol, and placed for subsequent use;

[0068] (3) Mix the dried walnut shell powder and recovered PP evenly in proportion, pour the mixed solution in step (2) into th...

Embodiment 3

[0073] A recycled PP-based wood-plastic composite material is prepared from the following raw materials in parts by weight: 50 parts of recycled PP; 50 parts of walnut shell powder, the sum of the weight parts of recycled PP and walnut shell powder is 100; parts; 6 parts of glycidyl methacrylate; 3 parts of styrene.

[0074] A preparation method for reclaiming PP-based wood-plastic composite material, the method comprising the following steps:

[0075] (1), walnut shells are pulverized, ground into powder, the particle size is 150 mesh, placed in a vacuum oven for drying treatment, the temperature of the oven is controlled at 120 ° C, dried for 6 hours, and then cooled to room temperature;

[0076] (2), dicumyl peroxide, glycidyl methacrylate, and styrene are dissolved in diluent ethanol, and placed for subsequent use;

[0077] (3) Mix the dried walnut shell powder and recovered PP evenly in proportion, pour the mixed solution in step (2) into the walnut shell powder and reco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a reclaimed polypropylene (PP)-based wood-plastic composite material and a preparation method thereof. The wood-plastic composite material comprises the raw materials by weight: 50 to 70 parts of reclaimed PP, 30 to 50 parts of natural plant fiber, 0.1 to 0.3 part of initiator, 0.1 to 6 parts of glycidyl methacrylate and 0.1 to 3 parts of styrene, wherein the sum of the weight parts of the reclaimed PP and the natural plant fiber is 100. By double monomer melt grafting in-situ reactive compatibilization, the compatibility of the reclaimed PP and the natural plant fiber is effectively improved, the interface bounding force between two phases is enhanced and the comprehensive performance of the material is improved. Various sectional materials can be extruded by different dies, so that industrialized production of the materials such as automobile internal lining panels, windows, doors and the like is realized.

Description

technical field [0001] The invention belongs to the field of wood-plastic composite materials, in particular to a recycled PP-based wood-plastic composite material and a preparation method thereof. Background technique [0002] Wood-plastic composite (WPC) is a new type of environmentally friendly composite material made by using wood powder, bamboo powder, crop straw powder, fruit shell powder and other natural plant fibers and plastic resin or waste plastic as the main raw materials, mixed at high temperature, and formed. composite material. Increasing the application of this material can improve the comprehensive utilization level of natural plant fibers, reduce white pollution, and reduce waste caused by improper disposal of waste resources. Therefore, more and more people pay attention to it. [0003] When the hydrophilic natural plant fiber and the lipophilic plastic matrix are combined, the interface interaction strength is small, the dispersion of the natural plant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/06C08L97/02C08F255/02C08F220/32C08F212/08B29C47/92B29C48/92
Inventor 朱怀才王忠强
Owner SINOPLAST NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com