High-efficiency slagging and dephosphorization agent and preparation method thereof

A technology of slag dephosphorization agent and steel dephosphorization agent, which is applied in the field of metallurgy to achieve the effect of reducing dosage, shortening processing time and improving effect

Inactive Publication Date: 2012-11-21
LIAONING TIANHE TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the existing pre-melted calcium ferrite slag dephosphorization agent, its ferrous content is generally higher than 12.0% (weight percentage), which cannot meet the current development of the steelmaking industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-efficiency slagging and dephosphorization agent and preparation method thereof
  • High-efficiency slagging and dephosphorization agent and preparation method thereof
  • High-efficiency slagging and dephosphorization agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Preferred embodiments of the present invention will be described in detail below. What needs to be explained before this is that the terms or words used in this specification and claims should not be limited to be interpreted as the usual meaning or the meaning in the dictionary, but should be based on the best way for the inventor to explain his invention. The principle of appropriately defining the concepts of terms is interpreted as meanings and concepts consistent with the technical idea of ​​the present invention. Accordingly, the structures shown in the embodiments described in this specification are only one of the best embodiments of the present invention, and cannot fully represent the technical ideas of the present invention, so it should be understood that there may be alternatives for the present invention. Various equivalents and modifications.

[0014] The slag dephosphorization agent for steelmaking produced by the method of the present invention with fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention proposes a high-efficiency slagging and dephosphorization agent and a preparation method thereof. The preparation method of the slagging and dephosphorization agent comprises preparing raw materials, crushing, mixing with stirring, distributing materials in a batch-wise way, smelting at a high temperature of 1500 to 1550 DEG C, smelting and tapping, cooling crystallization, breaking to mold, and obtaining the slagging and dephosphorization agent for steel-making, wherein the agent is rich in CaO and Fe2O3, has a particle size of 3 to 40 mm, uses 2CaO.Fe2O3 as a main phase and has a melting point of less than or equal to 1280 DEG C. The dephosphorization agent has increased ferric oxide content due to reduced ferrous oxide, thereby enhancing oxidizability and further improving the slagging and dephosphorization effect of the agent. The agent facilitates reducing dosage of the dephosphorization agent, shortening processing time and improving working efficiency.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, in particular to a slag dephosphorization agent used for removing phosphorus in steel and reducing the phosphorus content in molten steel during the converter steelmaking process and a preparation method thereof. Background technique [0002] At present, as the demand for low-phosphorus steel continues to increase, the amount of dephosphorization materials is also increasing accordingly, and the types of dephosphorization agents are also increasing. There are also quite a few dephosphorization agents disclosed in the prior art with different components and compositions and prepared by different preparation methods. These dephosphorization materials all have a certain dephosphorization effect, and it is recognized that the material with the best dephosphorization effect of slag is pre-melted calcium ferrite. The reason why the pre-melted calcium ferrite slag dephosphorization agent has better ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C1/02C21C7/064
Inventor 陈云天
Owner LIAONING TIANHE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com