Spraying-free high-transparent high-glossy acrylonitrile butadiene styrene (ABS) material and preparation method thereof

An ABS material and spray-free technology, which is applied in the field of ABS alloy materials, can solve the problems of increasing cost price, waste, and restricting the use of materials, and achieve the effects of improving color saturation, reducing production costs, and high impact strength

Active Publication Date: 2012-11-07
LONGJAR SHANGHAI IND
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The spray-free high-gloss ABS resin currently used in the market is basically made by adding PMMA resin and compatibilizer MBS to ABS resin. However, the high-gloss ABS resin produced by this process has the following defects in actual production: 1. ) Due to the incompatibility between PMMA and free acrylonitrile in ABS resin, there is a phase separation phenomenon between PMMA resin and ABS resin on the microscopic phase. Color spots appear, so the material has a low product qualification rate during injection molding, which causes a lot of waste in actual production
2) Due to the opacity of the ABS resin itself, the alloy material is also opaque, resulting in the need to add more toner ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spraying-free high-transparent high-glossy acrylonitrile butadiene styrene (ABS) material and preparation method thereof
  • Spraying-free high-transparent high-glossy acrylonitrile butadiene styrene (ABS) material and preparation method thereof
  • Spraying-free high-transparent high-glossy acrylonitrile butadiene styrene (ABS) material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The weight percentage PMMA (CM205) 42.5%, AS (DN50) 42.5%, MBS (EXL-2668) 10%, compatibilizer (L-5330) 3%, lubricant (EBS) 1.7%, antioxidant-1010 The percentage content is 0.3%. The mixed materials are put into the hopper of the twin-screw extruder, melted, mixed and extruded, extruded and granulated into alloy materials. Among them, the twin-screw processing technology is: the processing technology is as follows: Twin-screw extruder zone 190-220 ° C, zone 2 200-220 ° C, zone 3 temperature 200-220 ° C, zone 4 200-220 ° C, zone 5 200- 220°C, 200-220°C in the sixth zone, 200-220°C in the seventh zone, 200-220°C in the eighth zone, 200-220°C in the ninth zone, 200-210°C in the machine head, the material stays in the barrel for 1-2min, and then After pelletizing and drying, a spray-free, high-gloss transparent ABS alloy material is obtained.

Embodiment 2

[0036] The weight percentage PMMA (CM205) 40%, AS (DN50) 40%, MBS (EXL-2668) 15%, compatibilizer (L-5330) 3%, lubricant (EBS) 1.7%, antioxidant-1010 The percentage is 0.3%. The mixed materials are put into the hopper of the twin-screw extruder, melted, mixed and extruded, extruded and granulated into alloy materials. Among them, the twin-screw processing technology is: the processing technology is as follows: Twin-screw extruder zone 190-220 ° C, zone 2 200-220 ° C, zone 3 temperature 200-220 ° C, zone 4 200-220 ° C, zone 5 200- 220°C, 200-220°C in the sixth zone, 200-220°C in the seventh zone, 200-220°C in the eighth zone, 200-220°C in the ninth zone, 200-210°C in the machine head, the material stays in the barrel for 1-2min, and then After pelletizing and drying, a spray-free, high-gloss transparent ABS alloy material is obtained.

Embodiment 3

[0038] The weight percentage PMMA (CM205) 35%, AS (DN50) 35%, MBS (EXL-2668) 25%, compatibilizer (L-5330) 3%, lubricant (EBS) 1.7%, antioxidant-1010 The percentage is 0.3%. The mixed materials are put into the hopper of the twin-screw extruder, melted, mixed and extruded, extruded and granulated into alloy materials. Among them, the twin-screw processing technology is: the processing technology is as follows: Twin-screw extruder zone 190-220 ° C, zone 2 200-220 ° C, zone 3 temperature 200-220 ° C, zone 4 200-220 ° C, zone 5 200- 220°C, six zones 200-220°C, seven zones 200-220°C, eight zones 200-220°C, nine zones 200-220°C head 200-210°C, the material stays in the barrel for 1-2min, and then passes through After dicing and drying, a spray-free, high-gloss transparent ABS alloy material can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a spraying-free high-transparent high-glossy acrylonitrile butadiene styrene (ABS) alloy material and a preparation method thereof. The ABS alloy material comprises, by weight, 30-45% of polymethyl methacrylate (PMMA), 30-45% of acrylonitrile styrene (AS), 10-30% of flexibilizer, 1-5% of compatilizer, 0.3% of antioxidant and 0.7-2% of lubricant. The material has good transparency and high impact strength, modulus, surface glossy and surface scraping resistance, retains good processability and toughness of the ABS alloy material, and simultaneously has the advantages of good weather resistance, surface hardness, chemical resistance and glossy and the like of the PMMA and AS resin. The spraying-free high-transparent high-glossy ABS alloy material and the preparation method expand an application range of the ABS material in transparent materials. The preparation method includes the following steps: mixing raw materials according to the ratio, adding mixed resin into a plastic extruding machine, controlling the temperature to be 190-225 DEG C and granulating to obtain the spraying-free high glossy transparent ABS alloy material.

Description

[technical field] [0001] The invention relates to the technical field of ABS alloy materials, in particular to a new method for obtaining spray-free high-gloss transparent ABS alloy materials through twin-screw extruder extrusion. [Background technique] [0002] ABS resin: chemical name acrylonitrile-butadiene-styrene plastic has a wide range of sources, low price, excellent impact resistance, low temperature resistance, chemical resistance and excellent electrical properties. It also has the characteristics of easy processing and stable product size. . However, the scratch resistance of ABS material is poor. Therefore, before ABS alloy materials are applied in the terminal field, most ABS materials need to be sprayed to obtain sufficient scratch resistance. The thickness of ABS plastic coating is generally 15-20μm, and usually requires spraying 2~3 Tao can be completed. After one coat, it needs to be allowed to dry before a second coat. Surfaces that require a high gloss...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/12C08L33/12C08L51/04B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704B29C2948/92895
Inventor 赵斌赵学军
Owner LONGJAR SHANGHAI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka