Coating size composition for thermosensitive discoloring and energy storing textile and coating preparation method

A thermal discoloration, textile technology, applied in textiles and papermaking, microsphere preparation, microcapsule preparation and other directions, can solve the problem of no dual function textiles, etc., achieve the effect of easy operation, overcome the high temperature of discoloration, and simple process

Active Publication Date: 2012-10-31
TIANJIN POLYTECHNIC UNIV
View PDF3 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are only pure color-changing and pure energy storage textiles on the market at present, and there are no textiles with dual functions at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating size composition for thermosensitive discoloring and energy storing textile and coating preparation method
  • Coating size composition for thermosensitive discoloring and energy storing textile and coating preparation method
  • Coating size composition for thermosensitive discoloring and energy storing textile and coating preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Weigh 8.884g of tetradecyl alcohol and 1.116g of cetyl alcohol as energy storage materials and place them in a container, dissolve them at 80°C, then add 0.2g of dispersed cationic pink, 0.6g of crystal violet lactone and 3.0g of bisphenol A and seal it well, stir in a water bath at 80°C for 60 minutes to make a core material solution;

[0041] (2) Take 2.00g of melamine, 3.86g of formaldehyde solution and 22.5ml of distilled water, mix and stir evenly at a temperature of 70°C, adjust the pH value of the mixture to 8.5-9 with triethanolamine, and then react for 30 minutes until it is colorless and transparent shape, that is, to make a prepolymer, take it out and store it at 50°C for later use;

[0042] (3) Take 1.38g styrene-maleic anhydride copolymer and 25ml distilled water in a three-necked flask, add 0.2gNaOH, mix well, then adjust the pH value of the solution to 4-5 with 10% citric acid, and put Stirring and reacting at a temperature of ℃ for 1 h; then adding ...

Embodiment 2

[0051] (1) The preparation method of thermosensitive discoloration and energy storage microcapsule powder is the same as in Example 1;

[0052] (2) Mix 50g of water-based PU and 15.45g of heat-sensitive discoloration and energy storage microcapsule powder evenly, then gradually add associative water-based polyurethane thickener to adjust the viscosity of the mixture to 13 centipoise (25°C), and stir evenly Afterwards, the coating slurry is prepared;

[0053] (3) Fix the polyester / cotton blended fabric on the coating machine, and then apply the above-mentioned coating slurry evenly on the surface of the textile with a scraper, and the coating amount is 65g / m 2 , and then pre-baked at a temperature of 80° C. for 3 minutes, and then baked at a temperature of 140° C. for 3 minutes, so that the heat-sensitive color-changing and energy-storage textile is prepared.

[0054] After testing, the series of color difference values ​​before and after the heat-sensitive and energy-storage ...

Embodiment 3

[0056] (1) The preparation method of thermosensitive discoloration and energy storage microcapsule powder is the same as in Example 1;

[0057] (2) Mix 50g of water-based PU and 11.30g of heat-sensitive discoloration and energy storage microcapsule powder evenly, then gradually add associative water-based polyurethane thickener to adjust the viscosity of the mixture to 13 centipoise (25°C), and stir evenly Afterwards, the coating slurry is prepared;

[0058] (3) The cotton fabric is clamped on the coating machine, and then the above-mentioned coating slurry is evenly scraped and coated on the surface of the textile by a scraper, and the coating amount is 55g / m 2 , followed by pre-baking at a temperature of 80° C. for 3 minutes, and then baking at a temperature of 160° C. for 3 minutes, so that the heat-sensitive color-changing and energy-storage textile is produced.

[0059] After testing, the series of color difference values ​​before and after the heat-sensitive and energy-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
discoloration temperatureaaaaaaaaaa
discoloration temperatureaaaaaaaaaa
discoloration temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating size composition for a thermosensitive discoloring and energy storing textile and a coating preparation method. The coating size composition comprises the following components in parts by weight: 100 parts of waterborne polyurethane or polyacrylate adhesive and associative polyurethane thickener or polyacrylic acid synthetic thickener for adjusting viscosity, and 5 to 50 parts of thermosensitive discoloring and energy storing microcapsule powder. The coating preparation method comprises that the thermosensitive discoloring and energy storing microcapsule powder is used as a raw material, the waterborne polyurethane or polyacrylate adhesive is used as a coating finishing agent, and the thicker is adopted to adjust the viscosity, so that the coating size can be prepared; and then the coating size is uniformly coated on the surface of the textile in a way of direct blade coating, and the textile is subject to pre-baking and baking processes so as to obtain the thermosensitive discoloring and energy storing textile. The prepared textile has dual functions of thermosensitive discoloring and energy storing, thus having relatively wide application prospect.

Description

technical field [0001] The invention belongs to the technical field of functional textiles, and in particular relates to a coating slurry composition for functional textiles with dual responsiveness to ambient temperature and a coating preparation method. The textiles can change color as the external ambient temperature changes. Reversible changes, and endothermic and exothermic reactions can also occur when the temperature changes, so as to achieve the purpose of adjusting the temperature. Background technique [0002] With the development of science and technology and the improvement of people's living standards, great changes have taken place in people's aesthetics, so they show different needs from traditional ones in clothing, food, housing, transportation and other aspects. People not only pursue the comfort and aesthetic features of traditional clothing, but also hope that the clothing itself can endow it with distinctive functions and characteristics, thus promoting ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M15/263D06M23/12B01J13/02
Inventor 马晓光郑喜玲吴智磊杨文芳郑振荣
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com