Intermixture briquette obtained by direct alloying of V2O5 and application method thereof

A V2O5, mixed agent technology, applied in the field of direct alloying additives

Active Publication Date: 2012-10-31
WUHAN UNIV OF SCI & TECH
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this patented technology can obtain a higher yield, there are many types of solvents, regulators and reducing agents added, and the amount of reagents is relatively large; during the reaction process, the amount of slag generated is large; in actual production In the process, the reagent needs to be added at the end of the oxidation period and the end of the reduction period, that is, two steps are required to complete the production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] a V 2 o 5 Directly alloyed mixture compacts and methods of use thereof. The raw materials and content of the mixture briquette are: V 2 o 5 Powder is 10~15wt%, reducing agent is 5~10wt%, additive is 65~75wt%, water glass is 5~10wt%.

[0026] In this embodiment: the chemical composition and content of the reducing agent are: aluminum powder is 70-80wt%, and magnesium powder is 20-30wt%.

[0027] V 2 o 5 The preparation method of the mixed agent briquette for direct alloying of powder is: according to the above-mentioned raw materials and their contents, V 2 o 5 Powder, reducing agent and additives are mixed, then water glass is added, stirred evenly, compacted, dried, and V 2 o 5 Mixture compacts for direct alloying.

[0028] V prepared in this example 2 o 5 The method of using the direct alloyed mixture compact is:

[0029] The non-quenched and tempered steel 40Mn2V is smelted on a 5-ton electric arc furnace, and the vanadium content of the non-quenched and...

Embodiment 2

[0031] a V 2 o 5 Directly alloyed mixture compacts and methods of use thereof. The raw materials and content of the mixture briquette are: V 2 o 5 Powder is 13~19wt%, reducing agent is 8~14wt%, additive is 52~62wt%, water glass is 10~15wt%.

[0032] In the present embodiment: the chemical composition and content thereof of reducing agent are with embodiment 1; V 2 o 5 The preparation method of the powder direct alloyed mixture briquette is the same as in Example 1.

[0033] V prepared in this example 2 o 5 The method of using the direct alloyed mixture compact is:

[0034] The non-quenched and tempered steel 36Mn2V is smelted on a 5-ton electric arc furnace, and the vanadium content of the non-quenched and tempered steel is 0.11-0.16wt%. Using the V prepared in this example 2 o 5 Mixture compacts for direct alloying of powders as a source of vanadium. At the end of the reduction period of smelting, V is added to the ladle after slag removal 2 o 5 Mixture compacts...

Embodiment 3

[0036] a V 2 o 5 Directly alloyed mixture compacts and methods of use thereof. The raw materials and content of the mixture briquette are: V 2 o 5 Powder is 15~22wt%, reducing agent is 10~18wt%, additive is 57~67wt%, water glass is 8~13wt%.

[0037] In the present embodiment: the chemical composition and content thereof of reducing agent are with embodiment 1; V 2 o 5 The preparation method of the powder direct alloyed mixture briquette is the same as in Example 1.

[0038] V prepared in this example 2 o 5 The method of using the direct alloyed mixture compact is:

[0039] The structural steel 20MnV is smelted on a 5 ton electric arc furnace, and the vanadium content of the structural steel is 0.07~0.12wt%. Using the V prepared in this example 2 o 5 Mixture compacts for direct alloying of powders as a source of vanadium. At the end of the reduction period of smelting, V is added to the ladle after slag removal 2 o 5 Mixture compacts for powder direct alloying, V ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an intermixture briquette obtained by direct alloying of V2O5 and an application method thereof. The technical scheme is as follows: the raw materials and the contents of the intermixture briquette are as follows: 10-25 wt% of V2O5 powder, 5-20 wt% of reducing agent, 50-75 wt% of additive and 5-15 wt% of water glass. A preparation method of the intermixture briquette obtained by direct alloying of V2O5 comprises the following steps of: adding the V2O5 powder, the reducing agent and the additive according to the raw materials and the contents, adding water glass, uniformly stirring, briquetting and drying to obtain the intermixture briquette obtained by direct alloying of V2O5. According to the invention, the prepared intermixture briquette has the advantages of quick V2O5 reduction speed, high yield of vanadium, simple and easy operation, capability of obtaining the required middle-low carbon vanadium-containing micro-alloy steel at a single step, and remarkable economic benefit.

Description

technical field [0001] The technical field of the direct alloying additive of the present invention, particularly relates to a kind of V 2 o 5 Directly alloyed mixture compacts and methods of use thereof. Background technique [0002] At present, there are three main ways to produce vanadium-containing alloy steel: the first is to add vanadium-ferroalloy in the steelmaking furnace, which is the most common method, and it is the main method for producing vanadium alloy steel at this stage; the second is to directly add vanadium in the steelmaking furnace Vanadium slag (containing V 2 o 5 15~20wt%) and reducing agent for alloying; the third is to add V 2 o 5 and reducing agent, and then add a depleting agent during the reducing period for alloying. [0003] When ferrovanadium is used as raw material for alloying, it is necessary to use special production equipment to smelt ferrovanadium alloy. The smelting process of ferrovanadium alloy is relatively complicated, and ele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/04C22C38/12C21C7/00B22D1/00
Inventor 刘静戴明杰甘章华袁泽喜周欢杨文钗
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com