Process for producing meshed double-faced spraying and painting advertisement cloth
A production process and advertising cloth technology, which is applied in fiber types, textiles and papermaking, fiber processing, etc., can solve problems that affect product aesthetics and performance, difficult to perfectly interpret double-sided display patterns, uneven force mesh cloth, etc. , to achieve the effect of excellent printing effect, uniform force and uniform mesh
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032]After the 40D polyester FDY yarn is woven by a three-bar warp knitting machine and adopts the weaving method of 19 holes and 1 weaving method, it is impregnated with water-soluble and environmentally friendly double-permeable bleaching pulp, and then subjected to high temperature setting. The weight composition of the pulp is epoxy Resin curing agent 10%, fluorescent whitening agent KCB 1.5%, silicone oil emulsion type defoamer 0.15%, ethyl p-hydroxybenzoate 2%, rutile nano-titanium dioxide 2%, colorant 0.03%, and the rest is water; , During the setting process, the cloth speed is controlled at 14m / min, and the setting temperature is 210°C; during the process of soaking the mesh and setting the shape, the tension of the base fabric material is controlled in real time by a precision tension controller, and the tension is controlled at 130N, and the sending is adjusted. The speed ratio between the frame and the preheating roller is 1:1.04.
[0033] The various performance ...
Embodiment 2
[0037] After the 50D polyester FDY yarn is woven by a three-bar warp knitting machine and the weaving method of 19 holes and 1 is used, it is impregnated with a water-soluble and environmentally friendly double-permeable bleaching slurry, and then subjected to high temperature setting. The weight of the slurry is composed of epoxy Resin curing agent 12%, fluorescent whitening agent KCB 2%, silicone oil emulsion type defoamer 0.2%, ethyl p-hydroxybenzoate 2.5%, rutile nano-titanium dioxide 2.5%, colorant 0.03%, and the rest is water; During the setting process, the cloth speed is controlled at 12m / min, and the setting temperature is 215°C; during the process of soaking the mesh cloth and setting the shape, the tension of the base fabric material is controlled in real time by a precision tension controller, and the tension is controlled at 140N. The speed ratio between the preheating rollers is 1:1.05.
[0038] The various performance indicators of the mesh type double-sided ink...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com