Welding wire processing technology

A processing technology and welding wire technology, applied in metal processing equipment, welding media, manufacturing tools, etc., can solve the problems of low effect, many processes and high cost, and achieve the effect of saving process steps, simple process and low cost

Inactive Publication Date: 2012-07-25
JIANGSU ZHONGJIANG WELDING WIRE
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] When the existing welding wire is processed, the φ5.5mm welding wire is first roughly drawn to φ3.5mm, peeled, annealed, pickled, limed, then drawn to φ1.8mm, then drawn to φ0.6mm, and limed At the same time, the rough-drawn welding wire must be packaged first, the process is complicated and there are many procedures, the cost is high, and the effect is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] A welding wire processing technology, the process steps are:

[0012] (1) The raw material φ5.5mm welding wire is first peeled, pickled and dried;

[0013] (2) drawing the welding wire of φ5.5mm obtained in step (1) to φ0.9mm;

[0014] (3) Draw the welding wire of φ0.9mm to 0.6mm again.

[0015] The drying temperature is controlled within the range of 90°±5°.

[0016] The current used for the pickling is controlled above 100A.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a welding wire processing technology, which comprises the following steps that: (1) shucking, acid pickling and drying are carried out on raw material which is a welding wire with the diameter phi being 5.5mm; (2) the welding wire with the diameter phi being 5.5mm obtained in the step (1) is drawn to be the welding wire with the diameter phi being 0.9mm; and (3) the welding wire with the diameter phi being 0.9mm is drawn again to be the welding wire with the diameter being 0.6mm. The welding wire processing technology has the advantages that the cost is low, the technology is simple, the operation is easy, and the efficiency is high.

Description

technical field [0001] The invention relates to a welding wire processing technology. Background technique [0002] When the existing welding wire is processed, the φ5.5mm welding wire is first roughly drawn to φ3.5mm, peeled, annealed, pickled, limed, then drawn to φ1.8mm, then drawn to φ0.6mm, and limed At the same time, the rough-drawn welding wire must be packaged first. The process is complicated and has many procedures, high cost and low effect. Contents of the invention [0003] The object of the present invention is to provide a welding wire processing technology with low cost, simple technology, easy operation and high efficiency. [0004] The technical solution of the present invention to achieve the above object is a welding wire processing technology, the innovation of which is: the process steps are: [0005] (1) The raw material φ5.5mm welding wire is first peeled, pickled and dried; [0006] (2) drawing the welding wire of φ5.5mm obtained in step (1) to φ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/40
Inventor 嵇文斌费小平张伟杰张雷
Owner JIANGSU ZHONGJIANG WELDING WIRE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com