Method for preparing zinc oxide nano sheet array

A zinc oxide nano- and nano-flaky technology, which is applied in the direction of zinc oxide/zinc hydroxide, nanotechnology, etc., can solve the problems that the commercial prospects of ZnO nanowires are not optimistic, and achieve the effect of high specific surface area and good repeatability

Inactive Publication Date: 2012-07-04
TIANJIN UNIV
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it has been reported recently that metal oxide chemical vapor deposition using organometallic zinc precursors [2] The reaction temperature has been lowered to 4500C, but the commercial prospect of growing ZnO nanowires by vapor phase method is still not promising

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing zinc oxide nano sheet array
  • Method for preparing zinc oxide nano sheet array
  • Method for preparing zinc oxide nano sheet array

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Preparation of ZnO seeds. First, under the condition of water bath at 60°C, 125mL of methanol solution of zinc acetate dihydrate with a concentration of 0.01M was prepared in the flask, and the vigorous stirring was accompanied by the whole reaction process; secondly, 65mL of methanol solution of potassium hydroxide (0.03M) was added dropwise Drop into the above solution; finally, the mixed solution was continuously stirred at 60° C. for 2 hours, and the preparation of the seed solution was completed.

[0022] The synthesized ZnO seeds were spin-coated onto coverslip (2 cm x 2 cm) substrates. Place the coverslip on the SC-1B homogenizer, add two drops of ZnO seed solution onto the surface of the coverslip at a speed of 2000 r / min, and spin-coat for 60 seconds; repeat the spin-coating three times.

[0023] Prepare the reaction solution for the growth of ZnO nanosheets. In a 50ml beaker, prepare 30ml of zinc nitrate (0.05M) and hexamethylenetetramine (0.05M) of equimola...

Embodiment 2

[0026] Preparation of ZnO seeds. First, under the condition of water bath at 60°C, 125mL methanol solution of zinc acetate dihydrate with a concentration of 0.013M was prepared in the flask, and the vigorous stirring was accompanied by the whole reaction process; secondly, 65mL methanol solution of potassium hydroxide (0.05M) was added dropwise Drop into the above solution; finally, the mixed solution was continuously stirred at 70° C. for 5 hours, and the preparation of the seed solution was completed.

[0027] The synthesized ZnO seeds were spin-coated onto coverslip (2 cm x 2 cm) substrates. Place the coverslip on the SC-1B homogenizer, add two drops of ZnO seed solution onto the surface of the coverslip at a speed of 2000 r / min, and spin-coat for 60 seconds; repeat the spin-coating three times.

[0028] Prepare the reaction solution for the growth of ZnO nanosheets. In a 50ml beaker, prepare 30ml of zinc nitrate (0.05M) and hexamethylenetetramine (0.05M) of equimolar con...

Embodiment 3

[0031] Preparation of ZnO seeds. First, under the condition of water bath at 60°C, 125mL methanol solution of zinc acetate dihydrate with a concentration of 0.026M was prepared in the flask, and the vigorous stirring was accompanied by the whole reaction process; secondly, 65mL methanol solution of potassium hydroxide (0.095M) was added dropwise Drop into the above solution; finally, the mixed solution was continuously stirred at 65° C. for 6 hours, and the preparation of the seed solution was completed.

[0032] The synthesized ZnO seeds were spin-coated onto coverslip (2 cm x 2 cm) substrates. Place the coverslip on the SC-1B homogenizer, add two drops of ZnO seed solution onto the surface of the coverslip at a speed of 2000 r / min, and spin-coat for 60 seconds; repeat the spin-coating three times.

[0033] Prepare the reaction solution for the growth of ZnO nanosheets. In a 50ml beaker, prepare 30ml of zinc nitrate (0.05M) and hexamethylenetetramine (0.05M) of equimolar co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a zinc oxide nano sheet array, which comprises the following steps that: zinc oxide (ZnO) seed crystal solution is firstly prepared, spin coating is completed on a base, then a reaction liquid for ZnO nanosheets to grow is prepared, the base which is spin-coated with the seed crystal solution is put into the reaction liquid and is sealed, so the zinc oxide nano sheet array grows. The invention has the characteristics of quickness and convenience, has good repeatability, and can produce the zinc oxide nano sheet array on any base in a large area, expansive instruments, complicated technological conditions and harsh experimental parameters are prevented from being used, and the reaction time is finely regulated to observe the microstructure of the surface of a cover glass.

Description

technical field [0001] The invention relates to the preparation technology of nanometer materials, in particular to a simple preparation method of ZnO nano sheet array. Background technique [0002] Since the first report on the UV excitation effect of ZnO nanowires, a lot of effort has been devoted to the study of synthetic methods for 1D ZnO nanomaterials. Among the various synthetic techniques reported in the existing literature, the evaporation and condensation synthesis process is the most popular, because this method is simple and can obtain high-quality products. But these gas phase processes usually require temperatures of 800-900°C. Although it has been reported recently that metal oxide chemical vapor deposition using organometallic zinc precursors [2] The reaction temperature has been lowered to 4500C, but the commercial prospect of growing ZnO nanowires by vapor phase method is still not promising. In 2003, Yang Peidong and others successfully used the low tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G9/02B82Y40/00
Inventor 鲁从华王少武
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com