Concrete sealing and curing agent used for low-temperature refrigeration house

A technology of sealing and curing agent and low-temperature cold storage, which is applied in the field of concrete sealing and curing agent, which can solve the problems of poor permeability, slow strength improvement, and insufficient wear resistance, and achieve strong permeability, improved hardness and wear resistance, and is not easy to wear effect

Inactive Publication Date: 2012-06-27
TIANJIN BOHAI LITUO TECH
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Concrete sealing and curing agents in the prior art have many defects, such as: poor permeability, insufficient wear resistance, slow strength improvement, short service life, etc. How to completely solve the problems encountered by traditional concrete sealing and curing agents when dealing with complex concrete floors? In particular, how to provide a concrete sealing and curing agent with strong permeability and good sealing and curing effect for low-temperature cold storage has become an urgent demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: a kind of concrete sealing and curing agent for low-temperature cold storage, it is prepared by heating and reacting 2 hours in the reaction kettle by the raw material of following parts by weight: 20 parts of silicon dioxide, 3 parts of lithium, 3 parts of titanium, 40 parts of water.

Embodiment 2

[0011] Embodiment 2: a kind of concrete sealing and curing agent for low-temperature cold storage, it is prepared by heating and reacting 2 hours in the reaction kettle by the raw material of following parts by weight: 30 parts of silicon dioxide, 10 parts of lithium, 10 parts of titanium, 50 parts of water.

Embodiment 3

[0012] Embodiment 3: a kind of concrete sealing curing agent for low-temperature cold storage, it is prepared by heating and reacting 2 hours in the reaction kettle by the raw material of following parts by weight: 40 parts of silicon dioxide, 15 parts of lithium, 15 parts of titanium, 60 parts of water.

[0013] The preparation process of the concrete sealing and curing agent for low-temperature cold storage of the present invention is as follows: adding silicon dioxide, lithium, titanium and water into a reaction kettle, and heating and reacting in the reaction kettle for 2 hours.

[0014] The construction conditions of the concrete sealing and curing agent used in the low-temperature cold storage of the present invention: time requirement: 7-10 days after the construction of the concrete wear-resistant floor; construction temperature: above 0 ℃; Installation color: concrete color, with a certain luster; grass-roots treatment: before construction, clean and remove sundries, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a concrete sealing and curing agent used for a low-temperature refrigeration house, which is prepared from the following raw materials in parts by weight through a heating reaction for 2 h in a reaction kettle: 20-40 parts of silicon dioxide, 3-15 parts of lithium, 3-15 parts of titanium and 40-60 parts of water. The concrete sealing and curing agent is an environment-friendly colorless, odorless, non-toxic and non-combustible high-tech aqueous chemical compacting agent and has the advantages of strong permeability, good sealing and curing effects, high cost performance and the like. The concrete sealing and curing agent is super hard and resistant to wear, the ground is not easy to wear but the polishing effect is realized, and the longer the ground is used, the appearance effect is better. The floor on which the concrete sealing and curing agent is used has the advantages of sealing, seepage prevention, mould prevention, high temperature resistance, weathering prevention and dust prevention, is very easy to clean and becomes more beautiful and has permanent and attractive gloss just like marble when the floor is used longer and longer. The floor has beautiful appearance and long service, and worry-free life is realized through one time investment.

Description

technical field [0001] The invention belongs to the technical field of curing agents, and in particular relates to a concrete sealing and curing agent for low-temperature cold storage. Background technique [0002] Concrete sealing and curing agents in the prior art have many defects, such as: poor permeability, insufficient wear resistance, slow strength improvement, short service life, etc. How to completely solve the problems encountered by traditional concrete sealing and curing agents when dealing with complex concrete floors? In particular, how to provide a concrete sealing and curing agent with strong permeability and good sealing and curing effect for low-temperature cold storage has become an urgent demand for people. Contents of the invention [0003] In order to overcome the shortcomings of the prior art, the invention provides a concrete sealing and curing agent with strong permeability and good sealing and curing effect for low-temperature cold storage. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/24
Inventor 陶敏
Owner TIANJIN BOHAI LITUO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products