Cation type aqueous colored pavement crack sealing material and preparation process thereof

A pavement crack, cationic technology, applied in the direction of roads, roads, pavement details, etc., can solve the problems of easy cracking again, low bonding strength, environmental pollution, etc., to achieve good adhesion, not easy to fade, and simple equipment.

Active Publication Date: 2012-06-20
河南金欧特实业集团股份有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the commonly used maintenance method in China is: use paint of the same color for repair, but if solvent-based paint is used for filling, the cost will be high and the environment will be seriously polluted; if water-based paint is used for filling, the bonding strength will be small, especially for acid stones. The potting effect of colored pavement is even worse, and it is easy to crack again when it encounters water; therefore, there is an urgent need for a fast setting, high viscosity, low cost, no pollution, long service life, and good adhesion to acidic stones. Cationic water-based colored pavement crack sealant capable of maintaining the same color and binder properties as the colored pavement and its preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cation type aqueous colored pavement crack sealing material and preparation process thereof
  • Cation type aqueous colored pavement crack sealing material and preparation process thereof
  • Cation type aqueous colored pavement crack sealing material and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The raw materials used to produce 100kg cationic water-based colored pavement crack sealant are as follows:

[0023]

[0024] Its preparation process is as follows:

[0025] Preparation of material A: first clean up the mixing equipment, then add furfural oil with a weight of 30kg and petroleum resin with a weight of 30kg in the mixing equipment. During the addition process, the mixing equipment is constantly stirring, and the mixture is heated to 170°C, stirring at 170°C for 60 minutes to prepare 60kg of material A cement after shearing;

[0026] The preparation of B material: the cationic CR latex that weight is 4kg, the methyl cellulose that weight is 0.4kg as emulsifier and the pigment that weight is 0.28kg, weight is the cetyltrimethylammonium bromide of 1.2kg, Mix and stir water with a weight of 34.12kg to prepare 40kg of material B soap;

[0027] First will follow the steps The prepared 60kg material A is heated to 140°C, follow the steps The prepa...

Embodiment 2

[0029] The raw materials used to produce 100kg cationic water-based colored pavement crack sealant are as follows:

[0030]

[0031] Its preparation process is as follows:

[0032] Preparation of material A: first clean up the mixing equipment, then add furfural oil with a weight of 33kg and petroleum resin with a weight of 27kg in the mixing equipment. During the addition, the mixing equipment is constantly stirring, and the mixture is heated to 170°C, stirring at 170°C for 60 minutes to prepare 60kg of material A cement after shearing;

[0033] The preparation of B material: be that the cetyltrimethylammonium bromide that is 0.8kg by weight is the pigment that is 0.28kg by weight, the cationic CR latex that is 4.8kg by weight, the methyl cellulose that is 0.4kg by weight , the water mixing and stirring that weight is 33.72kg prepares 40kg of B material soap liquid;

[0034] First will follow the steps The prepared 60kg material A is heated to 140°C, follow the s...

Embodiment 3

[0036] The raw materials used to produce 100kg cationic water-based colored pavement crack sealant are as follows:

[0037]

[0038] Its preparation process is as follows:

[0039] Preparation of material A: first clean up the mixing equipment, then add furfural oil with a weight of 31.8kg and petroleum resin with a weight of 28.2kg to the mixing equipment. Heat to 170°C, stir at 170°C for 60 minutes, and prepare 60kg of material A cement after shearing;

[0040] The preparation of B material: with the cetyltrimethylammonium bromide that is 0.8kg by weight as emulsifier and the pigment that is 0.28kg by weight, the cationic CR latex that is 4kg by weight, the methylcellulose that is by 0.4kg by weight, 40kg of B material soap liquid is prepared by mixing and stirring water with a weight of 34.52kg;

[0041] First will follow the steps The prepared 60kg material A is heated to 140°C, follow the steps The prepared 40kg material B was heated to 60°C, and then the mat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cation type aqueous colored pavement crack sealing material used during treatment of problems of colored pavement, such as potholes and the like, in road engineering and the preparation process of the crack sealing material. The material is prepared by shearing material A and material B with the weight ratio of 60-70%:30-40% by use of a colloid mill, wherein the material A is prepared by mixing the following components according to parts by weight: 50-55 parts of furfural extract oil and 45-50 parts of petroleum resin; the material B is prepared by mixing the following components according to parts by weight: 10-12 parts of cation CR latex, 2-3 parts of cetyl trimethyl ammonium bromide, 0.7 parts of paint, 1 part of methylcellulose and 84.3-86.3 parts of water; and the cation CR latex is prepared by emulsifying duprene rubber through cationic surfactant, and the solid content is 40%. The sealing material has the advantages that the solidification rate is high, the viscosity is high, the cost is low, the sealing material is pollution-free, the service life is long, and the sealing material has good adhesive capability to acidic stone, and simultaneously can be the same with the color of the colored pavement and the property of binder.

Description

technical field [0001] The invention belongs to the technical field of road engineering, and in particular relates to a kind of material which has good adhesion to acid stones and can maintain the color and binder properties of the colored road surface, which is used in the process of road engineering treatment of pits and other diseases on the colored road surface. The same cationic water-based colored pavement crack sealing material and its preparation process. Background technique [0002] With the continuous progress of society and the continuous improvement of people's living standards, people's requirements for the living environment are also gradually increasing. As a paving material with beautifying environment, colored asphalt has entered the stage of experimentation and promotion. Many cities have tried to use colored asphalt concrete. Lay roads in cities like Shanghai, Beijing, Tianjin, Changsha, Shenyang and Xiamen. There are many colors of colored asphalt mixtu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L57/02C08L11/02C08L1/26C08L95/00C08K13/02C08K5/01C08K3/22C08K3/24C08K3/30E01C11/02
Inventor 周凯
Owner 河南金欧特实业集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap