Frosted hardened film for in-mold decoration

A technology of in-mold decoration and hardening film, which is applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problems of impermeability, incorrect color of printed patterns, and influence of light transmission performance of hardening film, etc., to achieve Solve the effect of color distortion

Active Publication Date: 2012-06-20
HEFEI LUCKY SCI & TECH IND
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the added anti-glare particles and the coating resin material are different substances, there is a certain difference in their refractive index, and the anti-glare particles will cause a certain degree of refraction, large-angle scattering and absorption of the transmitted light, making the cured film The light transmission performance will be affected, which directly causes poor clarity of the IMD printed pattern. Simply put, the printed pattern is not correct and opaque, such as the black background is not black, gray and black, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Frosted hardened film for in-mold decoration

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] DH-408 35.0 parts,

[0019] EM2411 1.0 parts,

[0020] 184 2.0 copies,

[0021] Levaslip 410 2.0 servings,

[0022] Butanone 30.0 parts,

[0023] 30.0 parts of ethyl cellosolve,

[0024] To 35 parts of aliphatic urethane acrylate prepolymer (manufactured by Shenzhen Dinghao Photochemical Technology Co., Ltd., trade name: DH-408) and 1.0 parts of ethoxylated pentaerythritol tetraacrylate monomer (manufactured by Changxing Chemical Industry Co., Ltd. , trade name: EM2411), add 2.0 parts of leveling agent with polydimethylsiloxane skeleton structure (manufactured by Deqian (Shanghai) Chemical Co., Ltd.; trade name: Levaslip 410), and add 2.0 parts of A photoinitiator (manufactured by Tianjin Tianjiao Chemical Co., Ltd.; trade name: 184) was diluted with 60 parts of a mixed solvent containing butanone and ethyl cellosolve in a relative weight amount of 1:1 to obtain a coating material.

[0025] The prepared coating material is applied to one side of a polyethylene tere...

Embodiment 2

[0027] UXE1000 40.0 servings,

[0028] EM2411 8.0 parts,

[0029] 1173 6.0 copies,

[0030] Levaslip 410 1.0 servings,

[0031] Butanone 22.5 parts,

[0032] 22.5 parts of ethyl cellosolve,

[0033] To 40.0 parts of urethane acrylate prepolymer (manufactured by Huayao Chemical (Wuxi) Co., Ltd., trade name: UXE1000) and 8.0 parts of ethoxylated pentaerythritol tetraacrylate monomer (manufactured by Changxing Chemical Industry Co., Ltd., trade name: EM2411), add 1.0 parts of leveling agent with polydimethylsiloxane skeleton structure (manufactured by Deqian (Shanghai) Chemical Co., Ltd.; trade name: Levaslip 410), and add 6.0 parts of photoinitiator ( Manufactured by Tianjin Tianjiao Chemical Co., Ltd.; trade name: 1173), diluted with 45 parts of a mixed solvent containing butanone and ethyl cellosolve in a relative weight amount of 1:1 to obtain a coating material.

[0034] The prepared coating material is applied to one side of a polyethylene terephthalate film with a thi...

Embodiment 3

[0036] UX-5000 50.0 servings,

[0037] DPCA-60 10.0 parts,

[0038] 184 7.0 copies,

[0039] BYK 307 1.5 parts,

[0040] Butanone 15 parts,

[0041] 15 parts of methyl isobutyl ketone,

[0042] To 50.0 parts of polyurethane acrylate prepolymer (manufactured by Huayao Chemical (Wuxi) Co., Ltd., trade name: UX-5000) and 10.0 parts of endide-modified dipentaerythritol 6 acrylic resin (Chemical Chemical (Wuxi) Co., Ltd. Company manufacture, trade name: DPCA-60), add 1.5 parts of leveling agent with polydimethylsiloxane skeleton structure (manufactured by BYK Chemicals; trade name: BYK 307), and add 7.0 parts of photoinitiator (manufactured by Tianjin Tianjiao Chemical Co., Ltd.; trade name: 184), 30 parts by weight of a mixed solvent containing methyl ethyl ketone and methyl isobutyl ketone with a relative weight ratio of 1:1 was diluted to obtain a coating material.

[0043] The prepared coating material is applied to one side of a polyethylene terephthalate film with a thic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a frosted hardened film for in-mold decoration, comprising a support body and a transparent hardened layer, wherein convex-concave veins are stamped on the transparent hardened layer through stamping and secondary ultraviolet curing; the thickness of the transparent hardened layer is 10-20 microns; and the transparent hardened layer comprises the following components in parts by weight: 35-50 parts of polyurethane acrylic prepolymer, 1-10 parts of grafted modified acrylic monomer, 0.5-7 parts of light initiator, 0.05-2 parts of flatting agent and 30-60 parts of solvent. According to the product provided by the invention, a frosting effect is generated, and the problems that printed patterns of the existing product do not have right colors and are not transparent are solved; and furthermore, the requirements on molding and tensile performances of the IMD (In-mold Decoration) can be met. The frosted hardened film for the in-mold decoration can be widely applied to surface decoration of the products.

Description

technical field [0001] The invention belongs to the technical field of in-mold decoration (IMD), in particular to a frosted hardened film for in-mold decoration. Background technique [0002] In-mold decoration (IMD) refers to the process of forming a decorative pattern on the surface of the product when the product is injected into the mold. Generally, a film with a decorative pattern is formed in advance, and then the film with a decorative pattern is heated. Compression molding to form a predetermined shape, the film is cut and then placed in the cavity of the injection molding mold, preferably molten material is injected into the cavity, the film combines with the molten material and forms a product with a decorative pattern. The appearance of products made by in-mold decoration has a stronger sense of reality than products that are patterned by painting after injection molding, and the pattern does not have any adverse phenomena such as fading or falling off. It is wide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B3/30B32B27/06B32B27/18
Inventor 王志坚于佩强刘玉磊刑成君郑文耀王旭亮
Owner HEFEI LUCKY SCI & TECH IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap