Method of preparing baking-free load-bearing bricks through steam curing of semidry desulfurization residues

A semi-dry desulfurization, load-bearing brick technology, applied in solid waste management, sustainable waste treatment, climate sustainability, etc. Risks can not be ignored and other issues to achieve the effect of avoiding adverse effects, short maintenance time, and reducing product costs

Inactive Publication Date: 2012-06-13
HUNAN UNIV OF SCI & TECH
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of mortar also has the following problems: ① Its early strength is low, which limits its application; ② The amount of desulfurization slag in the mortar is too low, which makes the cost of this kind of dry-mixed mortar relatively high, and It is not conducive to the large-scale treatment and utilization of desulfurization slag; ③The long-term durability of this kind of construction mortar has not been verified. Experiments show that due to the influence of delayed formation of ettringite, its long-term strength may be seriously reduced or even cracked due to expansion. The risk of its application cannot be ignored

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of preparing baking-free load-bearing bricks through steam curing of semidry desulfurization residues
  • Method of preparing baking-free load-bearing bricks through steam curing of semidry desulfurization residues
  • Method of preparing baking-free load-bearing bricks through steam curing of semidry desulfurization residues

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described in detail below in conjunction with specific experimental examples.

[0019] (1) Example of semi-dry static pressing: Table 1 lists the technical parameters of the preparation example of semi-dry static pressing at a water-cement ratio of 0.1-0.33. Raw materials used in the experiment: semi-dry desulfurization slag, the desulfurization slag is off-white to light gray-yellow fine powder, with good dispersibility and fluidity, the average particle size is 4-10um, and the BET specific surface area is 2-10m 2 / g, its composition is: the mass percent content is the CaO of 40-50%, the SO of 8-16% 3 , 10-18% SO 2 , 1-3% MgO, 1-2% TFe, 0.2-1.0% SiO 2 , 0.4-0.6% Al 2 o 3 , 1-5% K 2 O, 0.1-0.5% Na 2 O, 1-5% chloride, 15-25% loss on ignition, its radionuclide content complies with GB6566-2010 building main material nuclide content index, namely I Ra ≤1.0B q / Kg, I γ ≤1.0B q / Kg (testing method is GB11743-89) requirements; S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method of preparing baking-free load-bearing bricks through steam curing of semidry desulfurization residues, belonging to the technical fields of environmental engineering and preparation of construction material. According to the invention, a gelling agent is prepared from semidry desulfurization slag and multi-component powder and is uniformly mixed with inert sandy aggregate in a mixer, water accounting for 10 to 46% of the mass of solid powder is added and uniformly mixed with the solid powder, an obtained mixture undergoes pressure forming and demolding so as to obtain green bricks, and the green bricks are subjected to steam curing at a temperature of 40 to 90 DEG C for 1 to 7 d so as to obtain baking-free bricks with sufficient strength; the baking-free bricks can meet different strength requirements for load-bearing bricks of a model number in a range of MU10 to MU30, have excellent water resistance and can be used as exterior wall tiles. According to the invention, the problem that comprehensive utilization of semidry desulfurization gypsum is not easy due to complex composition of the semidry desulfurization gypsum is overcome; effective usage of solid waste in production of the baking-free bricks which cost less than conventional sintered clay bricks do has great significance to energy conservation and environmental protection.

Description

technical field [0001] The invention belongs to the technical field of environmental protection engineering and preparation of building materials, and in particular relates to a method for preparing fire-free load-bearing bricks by steaming and curing semi-dry desulfurization waste residue. Background technique [0002] Desulfurization and purification of coal-fired flue gas before discharge into the atmosphere is a rapidly developing environmental protection technology at home and abroad. It has been widely used in various major industrial fields. When lime or slaked lime is used as the desulfurization medium, a large amount of desulfurization gypsum will be produced. Early desulfurization technologies were mainly wet and dry. Wet desulfurization produced a large amount of sludge-like desulfurization gypsum, while dry desulfurization products were generally discharged together with fly ash or slag, and desulfurization gypsum would not be discharged separately . Wet desulfu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/30
CPCY02W30/91
Inventor 彭美勋蒋建宏
Owner HUNAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com