A kind of process method of dolomite producing high-purity basic magnesium carbonate

A process method, the technology of magnesium carbonate, applied in the direction of magnesium carbonate, etc., can solve the problems such as the difficulty of completely separating calcium and magnesium, and achieve the effect of abundant raw materials, high yield, and easy industrial production

Inactive Publication Date: 2011-12-14
内蒙古昶泰资源循环再生利用科技开发有限责任公司 +2
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that it is difficult to completely separate calcium and magnesium in the existing carbonization production, the invention provides a process for producing high-purity basic magnesium carbonate from dolomite. By adding oxalic acid or soluble oxalate during carbonization, the Improve the yield of basic magnesium carbonate produced by the dolomite carbonization method, and solve the technical problem that calcium and magnesium are difficult to completely separate in the dolomite carbonization method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of process method of dolomite producing high-purity basic magnesium carbonate
  • A kind of process method of dolomite producing high-purity basic magnesium carbonate
  • A kind of process method of dolomite producing high-purity basic magnesium carbonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1: The chemical composition of dolomite is MgO content 20.96%, CaO content 30.06%, broken to 2~5cm. Calcined at 900°C for 3 hours to obtain calcined white. The calcined white is mixed according to the mass ratio of water: calcined white is 50:1, the digestion temperature is controlled at 60°C, and the heat preservation is digested for 1 hour to obtain the emulsion. The emulsion is passed through a 60-mesh sieve to obtain refined magnesium emulsion. After cooling to room temperature, CO 2 , CO 2 The flow rate is 0.5L / min, and the pH value of the carbonization system is tracked and tested. When the carbonization system is at pH=8.5, add ammonium oxalate to make the concentration of oxalate in the system 0.002mol / L, continue carbonization to pH=6.5, and stop carbonization. The carbonized system is separated from solid to liquid, the solid phase is light calcium carbonate, and the liquid phase is heavy magnesium water. The obtained heavy magnesium water was pyr...

Embodiment 2

[0033]Example 2: The chemical composition of dolomite is MgO content 20.96%, CaO content 30.06%, broken to 2~5cm. Calcined at 950°C for 2.5h to obtain calcined white. Mix calcined white according to the mass ratio of water: calcined white is 40:1, stir and heat to 70°C, heat-preserve and digest for 1.5h to obtain emulsion. The emulsion is passed through a 60-mesh sieve to obtain refined magnesium emulsion. After cooling to room temperature, CO 2 , CO 2 The flow rate is 0.8L / min, and the pH value of the carbonization system is tracked and tested. When the carbonization system is at pH=9.0, add oxalic acid to make the concentration of oxalate in the system 0.005mol / L, continue carbonization to pH=6.8, and stop carbonization. The carbonized system is separated from solid to liquid, the solid phase is light calcium carbonate, and the liquid phase is heavy magnesium water. The obtained heavy magnesium water was pyrolyzed at 100°C for 2 hours, solid-liquid separation after cool...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process for producing high-purity basic magnesium carbonate from dolomite, which adopts a carbonization method and uses dolomite as a raw material. The method comprises the following steps: grinding, calcining, digesting the calcined dolomite, filtering, carbonizing magnesium emulsion, pyrolyzing a heavy magnesium solution, and drying to obtain basic magnesium carbonate.The carbonization process of the magnesium emulsion is as follows: after the magnesium emulsion is cooled, carbon dioxide is introduced; when the pH value reaches 7.5-9.5, oxalic acid or soluble oxalate is added to ensure that the concentration of oxalate groups in the system is 0.001-0.01mol / L; and after the system is mixed evenly, carbonization is performed continuously until the pH value is 6.5-7.0, filtration is performed, the filtrate is the refined heavy magnesium solution, and the residue is light calcium carbonate. By adding oxalic acid in the digesting process, the technical problem of the dolomite carbonization method that calcium and magnesium are difficult to separate thoroughly can be solved. The process is simple, is easy to control and has high magnesium oxide extraction rate and high product purity.

Description

[0001] technical field [0002] The invention relates to a process for mineral processing and utilization, in particular to a process for preparing high-purity magnesium carbonate from dolomite. Background technique [0003] The molecular formula of basic magnesium carbonate is xMgCO 3 ·yMg(OH) 2 ·zH 2 O, the value of x is 3~5, the value of y is approximately 1, and the value of z is 3~7. As an important inorganic chemical product, basic magnesium carbonate is not only used as a raw material for preparing high-purity magnesia and magnesium salt series products, but also can be used as an additive or improver for rubber, medicine, insulating materials, food and various chemical products , a wide range of applications. At present, the production process of basic magnesium carbonate is mainly carbonization method, and the main raw materials are magnesite, serpentine and dolomite. Although the reserves of magnesite are abundant, the country has limited protection policies f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01F5/24
Inventor 余红发武金永吴成友董金美李颖
Owner 内蒙古昶泰资源循环再生利用科技开发有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com