Colorful ceramic tile joint mixture and preparation technology thereof

A technology for colored ceramic tiles and caulking agent, applied in the field of colored ceramic tile caulking agent, can solve the problems of easy cracking and poor waterproofness, and achieve the effects of increasing compactness, improving workability, and increasing waterproof function.

Inactive Publication Date: 2011-08-31
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD +2
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tile grout can not only effectively solve the problems of easy cracking and poor waterproofness of traditional grouting materials, but also solve the long-term hydrophobic effect of common tile grouts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorful ceramic tile joint mixture and preparation technology thereof
  • Colorful ceramic tile joint mixture and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

no. 1 example

[0037] Based on the above range, the present invention provides the first embodiment, and the specific weight ratio of each component is as follows:

[0038] 32.5# white Portland cement 350.0

[0039] 200 mesh quartz powder 600.0

[0040] HPMC 75HD 40000 1.5

[0041] 8031H 15.0

[0042] PWC500 2.0

[0043] Polypropylene fiber 3mm 0.5

[0044] 602 2.0

[0045] F10 2.0

[0046] P750 2.0

[0047] S306 25.0

[0048] Based on the above range, the present invention provides a second embodiment, and the specific weight ratio of each component is as follows:

[0049] 32.53# Ordinary Portland cement 500.0

[0050] 200 mesh quartz powder 450.0

[0051] HPMC 75HD 75000 0.5

[0052] 8031H 30.0

[0053] PWC500 3.0

[0054] Polypropylene fiber 5mm 0.5

[0055] 602 1.0

[0056] 1641F 1.0

[0057] P750 1.0

[0058] S370 13.0

[0059] Based on the above range, the present invention provides a third embodiment, and the specific weight ratio of each component is as follows:

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a colorful ceramic tile joint mixture which comprises the raw materials based on weight percentage as follows: 35%-50% of white portland cement, 45%-60% of quartz powder, 0.05%-0.3% of hydroxypropyl carboxymethyl hydroxypropyl cellulose, 0.055-0.25% of water repellent and 1%-3% of pigment. After the colorful ceramic tile joint mixture is used, the constructability is greatly improved, the deformability is improved, the water resistance is realized, the compactedness is increased, the cracking resistance is improved, and the color is more durable and gorgeous.

Description

technical field [0001] The invention relates to a colored ceramic tile sealant used for filling gaps between indoor and outdoor ceramic tiles of buildings. Simultaneously, the invention also relates to a preparation process of the colored tile grout. Background technique [0002] At present, tiles have become one of the most commonly used materials in architectural decoration. There are certain gaps between tiles and tiles, which need to be filled with building materials. Initially, the filling material used was white cement and sand mixed on site in a certain proportion, but this filling material does not have waterproof and crack resistance properties, and often cracks and powder falls, so rainwater can easily enter the interior. Circulation causes phenomena such as alkali return and tile falling off. In response to these problems, domestic scholars have also conducted research. Through analysis, the main method adopted is to solve the above problems by adding polyviny...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/06C04B24/38
Inventor 田凤兰段文锋韩朝辉熊卫锋彭俊
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com