Copper-clad aluminum varnished wire processing technique

A processing technology, copper-clad aluminum wire technology, applied in the direction of metal/alloy conductors, electrical components, circuits, etc., can solve the problem of large amount of enameled wire usage, achieve the effects of improving research and development level, saving production costs, and stable performance

Active Publication Date: 2012-11-21
苏州市吴江神州双金属线缆有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to technical problems, the field of large-scale wire used in large transformers has been blank in China, and the amount of enameled wire used in this field is very large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The preferred embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0017] The copper-clad aluminum enameled wire processing technology in this embodiment includes the following steps: drawing the copper-clad aluminum wire core 4 to 6 times to obtain a copper-clad aluminum wire with a certain diameter and required electrical properties.

[0018] Carry out 10 to 13 coats of paint on the copper-clad aluminum core after drawing, and each coat of paint includes the following steps: paint the wire core, paint with a mold, and paint the wire through the mold. Rely on the gap between the wire and the mold core hole to maintain a certain thickness. The painting device and the mold should be cleaned in place. It can move ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a copper-clad aluminum varnished wire processing technique which comprises the following steps: (a), drawing a copper-clad aluminum varnished wire core for 4-6 times; (b), painting the drawn wire core for 10-13 times, wherein each painting comprises the following steps: (b1), lacquering the wire core, (b2), placing the lacquered wire core into an annealing furnace for annealing, and (b3), placing the annealed wire core into a drying oven for drying; (c), winding up, wherein the speed of winding up is 5 plus or minus 1 m / minute; and (d), unwinding and packaging. The copper-clad aluminum varnished wire processing technique is the combination of copper and aluminum metallurgy, obtains a certain diameter of copper clad aluminum varnished wire with the required electrical property and is endowed with the required mechanical property through a heat treatment method, thereby providing a material capable of replacing an enameled copper wire for a large-scale transformer; and through replacing the enameled copper wire with the copper-clad aluminum varnished wire, the consumption of copper resources is greatly reduced, the production cost is saved, and the performance is stable.

Description

technical field [0001] The invention relates to a heating device, in particular to a copper-clad aluminum enameled wire processing technology for enameled wire production. Background technique [0002] Enameled wire is the most representative product among electronic wires. Enameled wire is a main variety of winding wire, including the core wire and the paint layer coated on the outside of the core wire. After the bare wire is annealed and softened, it is painted and baked many times. It has four major properties: mechanical properties, chemical properties, electrical properties, and thermal properties. Copper-clad aluminum enameled wire is a new type of electromagnetic wire that uses copper-clad aluminum material as the inner conductor. Its characteristics are between copper and aluminum, combining the advantages of copper's excellent conductivity and aluminum's light weight. Micro motor rotor coils and various electromagnetic wires are widely used. [0003] With the rapi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B13/00H01B1/02
Inventor 张建峰
Owner 苏州市吴江神州双金属线缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products