Method for preparing chrome-containing protein filling and retanning agent by using chrome shavings as raw materials

A technology for chrome-tanned leather scraps and a retanning agent is applied in the field of preparing a chrome-containing protein-filled retanning agent, which can solve problems such as discoloration of vinyl-based resins, achieve excellent performance, simple and easy-to-operate extraction process, and solve pollution problems. effect of the problem

Inactive Publication Date: 2011-08-03
SHAANXI UNIV OF SCI & TECH
View PDF1 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a method for preparing a chromium-containing protein-filled retanning agent with high collagen content, simple process, and effectively solving the problem of discoloration of vinyl resins by using chrome tanned leather scraps as raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0018] (1) Preparation of tanning waste-chrome tanned leather shavings hydrolyzate:

[0019] Weigh 35.10g of chrome-tanned leather shavings (dry weight), add 223.02g of distilled water into a 500mL three-neck flask, stir and raise the temperature, when the system temperature reaches 100°C, add 41.88g of formic acid (85%) dropwise, and the dropwise addition is completed within 10 minutes , heat preservation reaction for 2.0h (including the dropping time); after the reaction, stir and cool to room temperature, adjust the pH value of the system to 5.0±0.5 with 40% sodium hydroxide solution; then centrifuge the hydrolyzate (speed=3000r / min, Time = 10min), the upper clear night is the required chrome tanned leather shavings hydrolyzate, save it for later use;

[0020] (2) Preparation of chromium-containing protein-filled retanning agent for leather:

[0021] Weigh vinyl monomers (acrylic acid, acrylamide, ethyl acrylate = 5:1:1.5, molar ratio) and polymerization inhibitor (0.3%, b...

Embodiment example 2

[0025] (1) Preparation of tanning waste-chrome tanned leather shavings hydrolyzate:

[0026] Weigh 70.20g of chrome-tanned leather shavings (dry weight), add 446.04g of distilled water into a 1000mL three-neck flask, stir and raise the temperature, when the system temperature reaches 95°C, add 83.76g of formic acid (85%) dropwise, and the dropwise addition is completed within 10 minutes , heat preservation reaction for 2.5h (including dropping time); after the reaction, stir and cool to room temperature, adjust the pH value of the system to 5.0±0.5 with 40% sodium hydroxide solution; then centrifuge the hydrolyzate (speed=3000r / min, Time = 10min), the upper clear night is the required chrome tanned leather shavings hydrolyzate, save it for later use;

[0027] (2) Preparation of chromium-containing protein-filled retanning agent for leather:

[0028] Weigh vinyl monomers (acrylic acid, acrylamide, ethyl acrylate = 5:1:1.5, molar ratio) and polymerization inhibitor (0.3%, based...

Embodiment example 3

[0032] (1) Preparation of tanning waste-chrome tanned leather shavings hydrolyzate:

[0033]Weigh 35.10g of chrome-tanned leather shavings (dry weight), add 223.02g of distilled water into a 500mL three-neck flask, stir and raise the temperature, when the temperature of the system reaches 90°C, add 41.88g of formic acid (85%) dropwise, and the dropwise addition is completed within 10 minutes , heat preservation reaction for 1.5 h (including the dropping time); after the reaction, stir and cool to room temperature, adjust the pH value of the system to 5.0±0.5 with 40% sodium hydroxide solution; then centrifuge the hydrolyzate (speed=3000r / min, Time = 10min), the upper clear night is the required chrome tanned leather shavings hydrolyzate, save it for later use;

[0034] (2) Preparation of chromium-containing protein-filled retanning agent for leather:

[0035] Weigh vinyl monomers (acrylic acid, acrylamide, ethyl acrylate = 5:1:1.5, molar ratio) and polymerization inhibitor (0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing chrome-containing protein filling and retanning agent by using chrome shavings as raw materials. In the chrome-containing protein filling and retanning agent prepared by the prior art, the collagen content in an active material is low. The chrome-containing protein filling and retanning agent prepared by the prior art cannot overcome the off shade drawback of ethenyl resin tanning agents effectively. The preparation method comprises the steps of preparing leather residue-chrome shaving hydrolysis solution and preparing chrome-containing protein filling and retanning agent for leather. In the invention, a process for hydrolyzing chrome shavings without removing chrome is adopted, so a collagen extraction process is simpler and easy in operation; and the obtained chrome shaving hydrolysis solution has high collagen content, and the prepared chrome-containing protein filling, retanning agent can overcome the off shade drawback caused by single ethenyl resin and improve the selective filling of the ethenyl resin, the existing Cr<3+> ions can improve the tanning effect of the ethenyl resin, and at the same time, a chrome pollution problem is solved.

Description

technical field [0001] The invention belongs to the field of leather production, and in particular relates to a preparation method of using chrome-tanned leather shavings as a raw material to prepare a chromium-containing protein filled retanning agent. Background technique [0002] The leather industry is closely related to human life and national economic development. it is in our national [0003] It occupies an important position in the economy. According to statistics, in recent years, the number of pig, cattle, and sheep leather processed has reached 170 million pieces, and the output accounts for 20% of the world's total, ranking first in the world [Lin Wei, Mu Changdao, Tang Jianhua. Tannery Sludge treatment and resource utilization [J]. Leather Science and Engineering, 2005, 15(4): 57-61.]. According to the statistics of the General Administration of Customs of China, the export of my country's leather and its products has been ranking first in the light industry ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F289/00C14C3/02C14C3/08C14C3/22
Inventor 马建中陈柱平高党鸽吕斌武文玲
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap