400-420mm large-thickness low-alloy high-strength constructional steel and production method thereof

A low-alloy, high-strength, production method technology, applied in the field of improving industrial steelmaking performance, can solve problems such as inability to guarantee normal operation of the project, inability to guarantee flaw detection, performance, and low market supply, so as to reduce the content of molten steel inclusions, reduce Metallurgical cost, the effect of improving comprehensive performance

Active Publication Date: 2011-05-18
NANYANG HANYE SPECIAL STEEL CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are very few iron and steel enterprises that can produce ultra-thick Q345B steel. In addition, in the domestic market, Q345B steel with specifications above 300mm cannot guarantee flaw detection and performance, and the market supply is very small. If you rely on imports, not only the price is expensive, Moreover, the purchase cycle is long, and the normal operation of the project cannot be guaranteed.
Moreover, there is no manufacturer at home and abroad that can produce this low-alloy high-strength structural steel with a thickness of more than 400mm.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The actual composition of the ultra-thick low-alloy high-strength Q345B steel plate in the present invention is: C: 0.147%, Si: 0.35%, Mn: 1.52%, P: 0.012%, S: 0.001%, Als: 0.025%. Its mechanical properties are: yield strength 305MPa, tensile strength: 500MPa, elongation: 25%, impact energy at 20°C: 192J, 166J, 233J.

[0016] Production method of the present invention is as follows:

[0017] (1) Smelting process: During converter smelting, ensure that the tapping carbon is ≥ 0.06%, and the tapping P is ≤ 0.018%; After the molten steel is smelted, it is sent to the LF refining furnace for refining, and a large amount of slag is used for slagging to ensure that the retention time of white slag is controlled at more than 15 minutes. VD vacuum refining pressure holding time is controlled at 20-25min;

[0018] (2) Pouring process: 48 tons of ingot molds are used for pouring, the pouring temperature is 1555°C, the main body is poured for 14-18min, and the riser is poured fo...

Embodiment 2

[0025] The actual composition of the ultra-thick low-alloy high-strength Q345B steel plate in the present invention is: C: 0.176%, Si: 0.27%, Mn: 1.48%, P: 0.012%, S: 0.001%, Als: 0.015%, and the thickness of the rolled steel plate It is 420mm, and its mechanical properties are: yield strength 350MPa, tensile strength: 555MPa, elongation: 23%, impact energy at 20°C: 160J, 187J, 205J.

[0026] Production method of the present invention is as follows:

[0027] (1) Smelting process: During converter smelting, ensure that the tapping carbon is ≥ 0.06%, and the tapping P is ≤ 0.018%; After the molten steel is smelted, it is sent to the LF refining furnace for refining, and a large amount of slag is used for slagging to ensure that the retention time of white slag is controlled at more than 15 minutes. VD vacuum refining pressure holding time is controlled at 20-25min;

[0028] (2) Pouring process: 48 tons of ingot molds are used for pouring, the pouring temperature is 1555°C, the...

Embodiment 3

[0034] The actual composition of the ultra-thick low-alloy high-strength Q345B steel plate in the present invention is: C: 0.160%, Si: 0.31%, Mn: 1.50%, P: 0.012%, S: 0.001%, Als: 0.020%, and the thickness of the rolled steel plate It is 420mm, and its mechanical properties are: yield strength 360MPa, tensile strength: 530MPa, elongation: 26%, impact energy at 20°C: 180J, 178J, 220J.

[0035] Production method of the present invention is as follows:

[0036] (1) Smelting process: During converter smelting, ensure that the tapping carbon is ≥ 0.06%, and the tapping P is ≤ 0.018%; After the molten steel is smelted, it is sent to the LF refining furnace for refining, and a large amount of slag is used for slagging to ensure that the retention time of white slag is controlled at more than 15 minutes. VD vacuum refining pressure holding time is controlled at 20-25min;

[0037] (2) Pouring process: 48 tons of ingot molds are used for pouring, the pouring temperature is 1555°C, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses 400-420mm large-thickness low-alloy high-strength constructional steel and a production method thereof. The 400-420mm large-thickness low-alloy high-strength constructional steel comprises the following chemical components in percentage by weight: not more than 0.18% of C, 0.20-0.40% of Si, 1.30-1.55% of Mn, not more than 0.015% of P, not more than 0.003% of S, 0.010-0.035% of Als and the balance of Fe and unavoidable impurities. In the invention, refined grain elements of Nb, V, Ti and the like are not added so that the cost of metallurgy and the content of molten steel inclusions are reduced; the processes of normalizing and wind-cooling refined grains are utilized so as to ensure the quality of the products to match the standard and the use requirements. The production processes are simple, and the constructional steel can be produced in batch. In addition, the applied strengthening mechanisms comprise a structure strengthening mechanism, a fine grains strengthening mechanism, a precipitation strengthening mechanism and a solution strengthening mechanism.

Description

technical field [0001] The invention relates to the technical field of improving industrial steelmaking performance, in particular to a 400-420mm large-thickness low-alloy high-strength structural steel and a production method thereof. Background technique [0002] At present, the extra-thick plate Q345B is generally used in vehicles, cranes, mining machinery, power stations, bridges and other dynamic load-bearing structures, mechanical parts, building structures, and general metal structural parts. At present, there are very few iron and steel enterprises that can produce ultra-thick Q345B steel. In addition, in the domestic market, Q345B steel with specifications above 300mm cannot guarantee flaw detection and performance, and the market supply is very small. If you rely on imports, not only the price is expensive, Moreover, the purchase cycle is long, and the normal operation of the project cannot be guaranteed. Moreover, there is no manufacturer at home and abroad that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C33/04C21D8/02
Inventor 杨东朱书成许少普张立新崔冠军康文举唐郑磊李红洋张涛徐昭庞林朱先兴
Owner NANYANG HANYE SPECIAL STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com