Manufacturing method of aluminium alloy workpiece with complex inner cavity body

A manufacturing method, aluminum alloy technology, applied in the direction of manufacturing tools, metal processing equipment, instruments, etc., can solve the problems of high manufacturing difficulty and low precision, and achieve the effect of low manufacturing difficulty, high precision and high production efficiency

Active Publication Date: 2012-10-31
SHANGHAI EAGTOP ELECTRONICS TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the defects and problems existing in the prior art that it is not suitable for manufacturing aluminum alloy workpieces with complex inner cavities, the manufacturing difficulty is high, and the precision is low, and to provide a method suitable for manufacturing aluminum alloy workpieces with complex inner cavities. Aluminum alloy workpieces, manufacturing methods for aluminum alloy workpieces with complex inner cavities with low manufacturing difficulty and high precision

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of aluminium alloy workpiece with complex inner cavity body
  • Manufacturing method of aluminium alloy workpiece with complex inner cavity body
  • Manufacturing method of aluminium alloy workpiece with complex inner cavity body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: It is aimed at an aluminum alloy workpiece with a semi-closed multi-layer staggered hole-like structure inner cavity, and the z-axis is the height axis. figure 1 A schematic diagram of its three-dimensional structure, figure 2 It is a schematic diagram of the structure of a single virtual slice after cutting. The thickness between the virtual slices is divided into two types: equidistant and unequal, and the rest of the structure is the same.

[0045] A method for manufacturing an aluminum alloy workpiece with a complex inner cavity, the method sequentially includes the following steps:

[0046] The first step: first analyze the real object or design drawing of the aluminum alloy workpiece with a complex inner cavity to be manufactured, and then draw a three-dimensional diagram of the aluminum alloy workpiece on the computer, and then take the height axis of the aluminum alloy workpiece as the direction, along the hole Perform oblique isometric or non-is...

Embodiment 2

[0050] Embodiment 2: It is aimed at an aluminum alloy workpiece with a closed multi-layer interlaced sheet structure inner cavity, and the z axis is the height axis. image 3 A schematic diagram of its three-dimensional structure, Figure 4 It is a schematic diagram of the structure of a single virtual slice after cutting. The thickness between the virtual slices is divided into two types: equidistant and unequal, and the rest of the structure is the same.

[0051] A method for manufacturing an aluminum alloy workpiece with a complex inner cavity, the method includes the following steps in sequence:

[0052] The first step: first analyze the real object or design drawing of the aluminum alloy workpiece with a complex inner cavity to be manufactured, and then draw a three-dimensional diagram of the aluminum alloy workpiece on the computer, and then take the height axis of the aluminum alloy workpiece as the direction, along the sheet Horizontally equidistant or non-equidistant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method of an aluminium alloy workpiece with a complex inner cavity body, comprising the following steps of: firstly analyzing a real object or design diagram of the to-be-manufactured aluminium alloy workpiece with the complex inner cavity body, then drawing a three-dimensional diagram of the aluminium alloy workpiece, carrying out equidistant or non-equidistant virtual segmentation on the aluminium alloy workpiece along the direction of the height axis of the aluminium alloy workpiece so as to obtain continuous virtual slices, numbering the virtual slices according to the sequence, carrying out facsimile reproduction respectively on the virtual slices on prepared processing plates according to the numbers, then assembling the processing plates after being processed according to the numbers of the corresponding virtual slices, then conveying the processing plates which are assembled and firmly pressed into a vacuum brazing furnace for vacuum brazing, finally carrying out finishing and clearing on assembled bodies after vacuum brazing, passing the qualification inspection, and then obtaining the to-be-manufactured aluminium alloy workpiece. The design not only is suitable for manufacturing the aluminium alloy workpiece with the complex inner cavity body, and has lower manufacturing difficulty, but also has higher accuracy and higher production efficiency and can ensure consistency of materials.

Description

technical field [0001] The invention relates to a method for manufacturing an aluminum alloy workpiece, in particular to a method for manufacturing an aluminum alloy workpiece with a complex inner cavity, and is particularly suitable for the manufacture of an aluminum alloy workpiece whose inner cavity is a closed or semi-closed multi-layer staggered structure . Background technique [0002] At present, in the processing of existing aluminum alloy workpieces with complex inner cavity structures, especially in the processing of realizing closed or semi-closed multi-layer interlaced structures inside the workpiece, if the traditional machining method is adopted, it will be affected by the processing technology and cutting tools. It is difficult to realize because of the limitation, and the precision is low; if aluminum alloy die-casting, pouring and other methods are used, it will be difficult to realize due to the difficulty of mold manufacturing. [0003] The Chinese patent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/00B23K1/008G06F17/50
Inventor 蔡曦
Owner SHANGHAI EAGTOP ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com