High performance impregnant for braided packing and impregnation process thereof

A technology of weaving filler and impregnating agent, applied in textile material processing, liquid/gas/vapor textile processing, textile and papermaking, etc. Leakage and other problems, to achieve the effect of simple method, reasonable reliability and good creep resistance

Active Publication Date: 2011-03-09
浙江国泰萧星密封材料股份有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a high-performance impregnating agent and impregnating method for braided packing, which mainly solves the problem in the prior art that the impregnating liquid used in the preparation method of the existing packing makes the thermal conductivity of the packing poor, so When used in occasions with granular media and high linear speed, it is easy to produce creep, and at the same time, the product wears a lot, which reduces the dimensional stability, softness and extrusion resistance of the product, resulting in the technology of running, popping, dripping, leaking, etc. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1: A high-performance impregnating agent for braided packing in this example, its composition and mass percentage are: 15% distilled water, 65% graphite emulsion, and 20% polyacrylate binder.

[0024] The packing impregnation method using the above impregnating agent in this example:

[0025] a. First carry out the impregnating agent ratio, put the PTFE fiber packing braided wire into the impregnating agent for the first impregnating treatment, and the impregnating time is 3 minutes;

[0026] b. Take out the packing braided wire and carry out the first drying, the drying temperature is 120°C, the drying time is 12 minutes, and the dried packing braided wire is braided into packing;

[0027] c. Put the packing into the impregnating agent for the second impregnation treatment, and the impregnation time is 15 minutes;

[0028] d. After taking out the braided wire of the packing, carry out the second drying, the drying temperature is 80°C, and the drying time i...

Embodiment 2

[0031] Example 2: A high-performance impregnating agent for braided packing in this example, its composition and mass percentage are: 15% distilled water, 75% graphite emulsion, and 10% polyacrylate binder.

[0032] The packing impregnation method using the above impregnating agent in this example:

[0033] a. First carry out the impregnating agent ratio, put the PTFE fiber packing braided wire into the impregnating agent for the first impregnating treatment, and the impregnating time is 4 minutes;

[0034] b. Take out the braided wire of the packing and carry out the first drying, the drying temperature is 160°C, and the drying time is 10 minutes, and weave the braided wire of the dried packing into a packing;

[0035] c. Put the packing into the impregnating agent for the second impregnation treatment, and the impregnation time is 20 minutes;

[0036] d. After taking out the braided wire of the packing, carry out the second drying, the drying temperature is 100°C, and t...

Embodiment 3

[0038] Example 3: A high-performance impregnating agent for braided packing in this example, its composition and mass percentage are: 20% distilled water, 70% graphite emulsion, and 10% polyacrylate binder.

[0039] The packing impregnation method using the above impregnating agent in this example:

[0040] a. First carry out the impregnating agent ratio, put the PTFE fiber packing braided wire into the impregnating agent for the first impregnating treatment, and the impregnating time is 3 minutes;

[0041] b. Take out the packing braided wire and carry out the first drying, the drying temperature is 120°C, the drying time is 12 minutes, and the dried packing braided wire is braided into packing;

[0042] c. Put the packing into the impregnating agent for the second impregnation treatment, and the impregnation time is 15 minutes;

[0043] d. After taking out the braided wire of the packing, carry out the second drying, the drying temperature is 80°C, and the drying time i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
friction coefficientaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high performance impregnant for braided packing and impregnation process thereof. The invention mainly solves the technical problems of poor thermal conductivity of existing packings prepared by the prior art, so that creep deformation is formed under the condition of higher linear velocity and granular media existed and performance degradation of products in size stability, pliability and extrusion resistance property is generated due to the large amount of abrasion loss, as well as water leakage. The impregnant provided by the invention comprises, by mass, 15%-25% of distilled water, 65%-75% of graphite emulsion and 10%-20% of polyacrylate adhesive.

Description

technical field [0001] The invention relates to an impregnating agent for braided packing, in particular to a high-performance impregnating agent for braided packing and a process method. Background technique [0002] At present, gaskets, gaskets and packings made of a single fluoroplastic (such as polytetrafluoroethylene, polyfluoroethylene propylene), asbestos rubber sheet or silicone rubber are mostly used as sealing materials. Gaskets, gaskets and packings made of asbestos rubber sheets and silicone rubber materials are randomly distributed, have strength only in certain directions, have poor creep resistance, are prone to aging, and have a short service life. A Chinese patent discloses a nano packing and its manufacturing method (authorized announcement number: CN 100341972C), which includes packing matrix materials and additives, the additives include special nano anti-wear and corrosion inhibitors, special nano anti-wear and corrosion inhibitors Accounting for 8%-46%...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/74D06M15/263D06B3/04D06B3/00D06B15/00D06M101/22
Inventor 孙锦龙
Owner 浙江国泰萧星密封材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com