Urushiol phosphorous-series flame retardant resin and preparation method thereof

A flame retardant resin, urushiol phosphorus-based technology, applied in the field of urushiol phosphorus flame retardant resin and its preparation, can solve the problems of inability to overcome the problem of sensitization of raw lacquer, failure to maintain the excellent performance of raw lacquer, etc., and achieve excellent medium resistance performance , the effect of excellent flame retardant performance

Inactive Publication Date: 2013-04-03
中华全国供销合作总社西安生漆涂料研究所
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the existing flame-retardant coatings fail to maintain the excellent performance of raw lacquer, cannot overcome the sensitization problem of raw lacquer, and have certain limitations in use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Urushiol phosphorous-series flame retardant resin and preparation method thereof
  • Urushiol phosphorous-series flame retardant resin and preparation method thereof
  • Urushiol phosphorous-series flame retardant resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The preparation method of the above-mentioned urushiol phosphorus-based flame-retardant resin includes: separating and extracting urushiol from raw lacquer according to a conventional method, then adding a formulated amount of solvent to obtain an urushiol solution, and then adding a formulated amount of amine compounds to the urushiol solution , aldehyde compounds and catalysts, heated to 60-100°C, reacted for 2-6 hours, raised the temperature to remove the small molecule product water; ℃, react for 1 to 4 hours, stop heating and cool down to room temperature to obtain the urushiol phosphorus-based flame-retardant resin.

[0018] The urushiol is extracted from lacquer produced in Ankang, Hanzhong, Chengkou, Maoba, Qinling or other areas, with a frying fraction of more than 65% and a urushiol content of more than 50%.

[0019] The phosphorus compound is one or more of phosphorus oxide, phosphorus oxychloride, and phosphate ester.

[0020] The amine compound is one or m...

Embodiment 1

[0024] The weight percent of urushiol phosphorus flame retardant resin raw material of the present invention is as follows:

[0025]

[0026] The urushiol is extracted from lacquer produced in Ankang, Hanzhong, Chengkou, Maoba, Qinling or other areas according to conventional methods, the frying fraction is more than 65%, and the urushiol content is more than 50%.

[0027] Add formula amount of xylene to urushiol extracted from raw lacquer to obtain urushiol solution, heat urushiol solution to 60°C, add formula amount of formaldehyde and ammonia water to react for 1-3 hours, heat up and dehydrate, wait until the temperature of the system rises to At 110°C, add the formulated amount of phosphoric acid ester, react for 1-3 hours, and cool down to room temperature after the reaction, to obtain the urushiol phosphorus-based flame-retardant resin.

Embodiment 2

[0029] The raw material and weight percent of urushiol phosphorus flame retardant resin of the present invention are as follows:

[0030]

[0031] The urushiol is extracted from lacquers produced in Ankang, Hanzhong, Chengkou, Maoba, Qinling or other areas according to conventional methods.

[0032] To the urushiol extracted from raw lacquer, add the formulated amount of xylene to obtain the urushiol solution, heat the urushiol solution to 60°C, add the formulated amount of aniline, furfural and sodium hydroxide to react for 2-5 hours, heat up and dehydrate, and wait for the system The temperature rises to 90°C, and the formulated amount of phosphorus oxide is added, reacted for 2-4 hours, and after the reaction is completed, the temperature is lowered to room temperature, and the urushiol phosphorus-based flame-retardant resin is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses urushiol phosphorous-series flame retardant resin. The resin consists of the following raw materials in percentage by mass: 20 to 40 percent of urushiol, 0 to 20 percent of amine compound, 4 to 10 percent of aldehyde compound, 0.5 to 6 percent of phosphorous-series compound, 0 to 5 percent of epoxy resin, 0.5 to 3 percent of catalyst and 40 to 55 percent of solvent. A method for preparing the urushiol phosphorous-series flame retardant resin comprises the following steps of: obtaining raw lacquer from a lacquer tree; separating and extracting the urushiol from the raw lacquer, heating the urushiol and reacting the heated urushiol with the amine compound, the aldehyde compound, the solvent and the catalyst for synthesizing; and adding the epoxy resin, the phosphorous-series compound and the solvent into the complex, heating and reacting for synthesizing, stopping heating and cooling to room temperature after reaction is finished. The resin has high flame retardant property, water resistance and chemical resistance and is suitable for fields such as public fire safety, chemical industry, light industry, building materials, electronic apparatuses, mining and the like.

Description

Technical field [0001] The present invention involves a flame retardant coating, especially a flame -retardant resin and its preparation of lacquer phenol phosphorus. Background technique [0002] my country has abundant raw lacquer resources. There are many varieties of coatings made of raw paint. With the rapid development of socio -economic development, people's requirements for flame retardant performance of coatings have increased. The use of flame retardant materials in the national economy is in line with the central government's instructions on the "prevention of preventing problems before they occur." It is a prerequisite for ensuring people's lives and national resources and security. There is no doubt about the demand for burn products.However, most of the existing flame retardant coatings have not maintained the excellent performance of paint paint, cannot overcome the sensitivity problem of raw paint, and there are certain limitations in use.Therefore, the use of uni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G14/12C08G8/28C09D161/34C09D161/14
Inventor 张飞龙贺娜
Owner 中华全国供销合作总社西安生漆涂料研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More