Test piece-hanging frame for testing high-pressure kettle

A technology for autoclave and testing, which is applied in the field of test piece racks for autoclave testing, which can solve problems such as inconvenience, interference, and melting, and achieve the effects of reliable performance, simple structure, and ease of use

Inactive Publication Date: 2010-07-21
CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, during the test, some are hung with iron wires, and some are hung with self-made glass hooks. The former will cause the reaction between the iron wire and the test piece or cause the iron ions to dissolve in the medium solution during the test. The latter often cannot stand the high temperature and partly occurs melt
Not only is it inconvenient, but also the consistency of test conditions cannot be guaranteed, which brings unnecessary test interference environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Test piece-hanging frame for testing high-pressure kettle
  • Test piece-hanging frame for testing high-pressure kettle
  • Test piece-hanging frame for testing high-pressure kettle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] See attached figure 2 , this figure provides a detailed schematic diagram of the autoclave structure, and 5 in the figure indicates the lid of the autoclave. The present invention is used in an autoclave, and the hanger is fixed by the lid of the kettle, so that the corrosion research test pieces are immersed in different positions of the kettle barrel, and the kettle barrel withstands a test environment as high as 350°C and 19.0MPa.

[0010] See attached figure 1 , the top of the ceramic column 6 is provided with a groove 1, the groove is hung on the top cover of the autoclave, the circular support rod 2 in the middle passes through the circular hole 4 in the middle of the ceramic column and is fixed, and the circular support rod 5 at the bottom passes through the ceramic column The round hole 3 at the bottom is fixed; the two round rods are used to hang the test piece for corrosion test respectively, and each round rod can hang two test pieces for parallel test rese...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a test piece-hanging frame for testing a high-pressure kettle, which comprises an alumina ceramic column and two alumina ceramic round struts. The top of the ceramic column (6) is provided with a groove (1) to be hung on a top cover of a high-pressure kettle, the middle round strut (2) penetrates through and is fixed in a round hole (4) in the middle of the ceramic column (6), the bottom round strut (5) penetrates through and is fixed in a round hole (3) at the bottom of the ceramic column (6), the two round struts are respectively used for hanging test pieces of a corrosion test, two test pieces can be hung on either round strut for parallel test research, and the round struts are designed in positions of different heights so that the test pieces are arranged in different medium areas during the test. The invention provides the test piece-hanging frame which is convenient to test the high-pressure kettle under test conditions of 350 DEG C and approximate 19.0 MPa and must use an alumina ceramic material to resist high temperature and high pressure. The test piece-hanging frame has the advantages of convenient use, simple structure and reliable performance.

Description

technical field [0001] The invention relates to a test piece hanger for high temperature corrosion test, in particular to a test piece hanger for autoclave test. Background technique [0002] At present, autoclave is used for high temperature and high pressure corrosion test, and there is no special corrosion test piece hanger, and the test conditions of autoclave are as high as 350 ° C and nearly 19.0 MPa. Therefore, during the test, some are hung with iron wires, and some are hung with self-made glass hooks. The former will cause the reaction between the iron wire and the test piece or cause the iron ions to dissolve in the medium solution during the test. The latter often cannot stand the high temperature and partly occurs melt. Not only is it inconvenient, but also the consistency of test conditions cannot be guaranteed, which brings unnecessary test interference environment. Contents of the invention [0003] The technical problem to be solved by the present inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G01N17/00
Inventor 张芳袁曹龙余菲
Owner CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products