Slurry fuel coal tar pitch water slurry and preparation method thereof
A coal tar and fuel technology, applied in the field of slurry fuel coal tar tar pitch water slurry and its preparation, can solve the problems of intractable treatment, high pollution, residue and waste water pollution, etc., and achieve energy saving, low pollutant discharge, atomization good performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] The medium-temperature coal tar pitch fragments with a softening point of 84 °C were frozen at -30 °C for 24 hours, crushed and sieved with a 60-mesh standard sieve to obtain coal tar pitch powder.
[0027] Add 0.5g of sodium dodecylbenzenesulfonate to 34.5g of untreated coking wastewater whose COD is 1852mg / L, ammonia nitrogen is 96mg / L, cyanide is 21mg / L, and volatile phenol is 368mg / L. Then add 65g of coal tar pitch powder under high-speed stirring, and stir evenly to prepare coal tar pitch water slurry. The apparent viscosity of the coal tar pitch water slurry is 810mPa s (the shear rate is 100s -1 ), the low calorific value is 21.4MJ / Kg.
Embodiment 2
[0029] The medium-temperature coal tar pitch fragments with a softening point of 89 °C were frozen at -30 °C for 24 hours, crushed and sieved with a 60-mesh standard sieve to obtain coal tar pitch powder.
[0030] Add 1.0g of sodium lauryl sulfate to 32g of untreated coking wastewater with a COD of 1852mg / L, ammonia nitrogen of 96mg / L, cyanide of 21mg / L, and volatile phenol of 368mg / L, stirring and dissolving, and then Add 67g of coal tar pitch powder under stirring, and stir evenly to prepare coal tar pitch water slurry. The apparent viscosity of the coal tar pitch water slurry is 945mPa s (the shear rate is 100s -1 ), the low calorific value is 23.6MJ / Kg.
Embodiment 3
[0032] The high-temperature coal tar pitch fragments with a softening point of 104°C were frozen at -30°C for 24 hours, crushed and sieved with a 60-mesh standard sieve to obtain coal tar pitch powder.
[0033] Add 1.5g of sodium petroleum sulfonate to 30.5g of pre-biochemical coking wastewater with COD of 1247mg / L, ammonia nitrogen of 67mg / L, cyanide of 12mg / L, and volatile phenol of 142mg / L, stir and dissolve, and then add it under high-speed stirring 68g of coal tar pitch powder was stirred evenly to prepare a coal tar pitch water slurry. The apparent viscosity of the coal tar pitch water slurry is 1014mPa s (the shear rate is 100s -1 ), the low calorific value is 24.2MJ / Kg.
PUM
Property | Measurement | Unit |
---|---|---|
Apparent viscosity | aaaaa | aaaaa |
Apparent viscosity | aaaaa | aaaaa |
Softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com