Method for finishing durable function of cellulose fabric

A technology for cellulose fabrics and functional finishing agents, which is applied in fiber processing, plant fibers, textiles and papermaking, etc., can solve the problems of high cost, insignificant effect, and poor production safety of silane coupling agents, and achieve easy industrialization, No toxic side effects, low cost effect

Inactive Publication Date: 2010-05-19
DONGHUA UNIV
View PDF0 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cost of silane coupling agent is high, and the effect is not obvious; at the same time, due to the solubility, ethanol or methanol must be used as a solvent when preparing the sol, and the production safety is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Prepare the aqueous solution of finishing solution A, wherein the polyepichlorohydrin dimethylamine derivative is 12g / L, the pH of the solution is adjusted to 10~12 with sodium hydroxide, and the cotton yarn card (20 s ×16 s , 128×60) in the finishing solution A, dipped twice and rolled twice, with a liquid-carrying rate of 70%, and dried at 80°C;

[0027] Add 5% triammonium citrate aqueous solution dropwise to the mixed system of 2% water glass and 1% cetyltrimethoxysiloxane in 50mL of mass percentage concentration until the pH of the solution The value reached 10.7, and then stirred for 30 minutes to obtain finishing solution B; the cotton yarn card that had been treated above was dipped and rolled twice in the obtained finishing solution B, the liquid-carrying rate was 70%, pre-baked at 80°C for 3 minutes, and baked at 160°C Bake for 3 minutes to obtain a cotton fabric with superhydrophobic function.

Embodiment 2

[0029] Prepare an aqueous solution of finishing solution A, wherein 2,4-dichloro-6-(2-pyridoethylamino)-s-triazine polyamide polymer is used as a cationic modifier in an amount of 5 g / L, and the Sodium adjusted the pH of the solution to 9.5, and the linen (14 s ×14 s , 54×52) soaked at 60°C for 30 minutes, then washed to neutral, and dried at 80°C;

[0030] To the mixed system of 2% water glass and 0.5% cetyltrimethylammonium chloride in the mass percent concentration of 50mL, add ammonium sulfate aqueous solution dropwise until the pH value of the solution reaches 10.7, after that Stir for 30 minutes to obtain finishing solution B; at 60°C, immerse the cationic-modified linen fabric in finishing solution B for 60 minutes, the bath ratio is 1:40, pre-bake at 80°C for 3 minutes, wash with water, and bake at 170°C for 2 minutes Minutes, get antibacterial linen fabric.

Embodiment 3

[0032] Prepare finishing liquid A aqueous solution, wherein with glycidyl trimethyl ammonium chloride as cationic modifier, consumption is 5g / L, adjust pH to about pH 7 with sulfuric acid, cotton gauze card (20 s ×16 s , 128×60) at 60°C for 30 minutes, with a bath ratio of 1:10, mixed thoroughly and evenly, after dipping, take it out and dry it in an oven at 50°C, and bake at 90°C for 30 minutes. Then take out to wash and dry.

[0033] Add ammonium chloride aqueous solution dropwise to 50mL of the mixed system of 2% water glass and 2% flame retardant FR-PN until the pH value of the solution reaches 10.7, then stir for 30 minutes , to obtain finishing solution B; at 60°C, the cationically modified cotton yarn was dipped twice in finishing solution B and rolled twice, with a liquid retention rate of 75%, prebaked at 80°C for 3 minutes, and baked at 160°C for 3 minutes to obtain Flammable cotton fabric.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for finishing the durable function of a cellulose fabric, which comprises the following steps: firstly, soaking or padding the cellulose fabric by using an aqueous solution of a cationic modifier namely a finishing liquor A; secondly, soaking or padding the cellulose fabric in a prepared finishing liquor B; thirdly, treating the cellulose fabric in a water-containing medium solution comprising sodium, potassium or lithium sodium silicate and a textile functional finishing agent; and finally, pre-baking the cellulose fabric at a temperature of between 80 and 100 DEG C, washing the cellulose fabric, and baking the cellulose fabric at a temperature of between 120 and 170 DEG C. The method is simple and safe, has low requirements on the performance of equipment, is easy for industrialization and is suitable for the cellulose fabric, and a fabric prepared by the method has lasting functionalities.

Description

technical field [0001] The invention belongs to the field of functional finishing methods for cellulose fabrics, in particular to a durable functional finishing method for cellulose fabrics. Background technique [0002] The application of sol-gel technology based on inorganic or organometallic compounds as precursors (starting materials) to the functional finishing of textiles has begun to emerge. The fabric is padded with the nano-sol of inorganic oxide, and then undergoes a heat treatment process. The nano-sol condenses with each other to form a transparent metal or non-metal oxide xerogel coating on the surface of the fabric. or film. By adding some functional finishing agents to the nano-sol to modify the nano-sol, the functional finishing agent can be evenly covered in the network structure of the three-dimensional metal oxide, thus endowing the fabric with different properties. These functional finishing agents can be anti-ultraviolet finishing agents, antibacterial...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/53D06M13/513D06M11/79D06M15/59D06M13/463D06M101/06
Inventor 邢彦军黄文琦刘金云戴瑾瑾
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com