Martensitic stainless steel with high Mn content

A martensitic stainless steel, content technology, applied in high hardness and high corrosion resistance martensitic stainless steel, high strength field, can solve the problems of increasing production cost, increasing the difficulty of manufacturing, etc., to achieve corrosion resistance will not decrease, Good toughness and low production cost

Active Publication Date: 2010-03-31
BAOSTEEL DESHENG STAINLESS STEEL
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the addition of Ti, Nb, B, W and other elements to this steel type, on the one hand, the production cost is increased, and on the other hand, the difficulty of manufacturing is increased.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Martensitic stainless steel with high Mn content
  • Martensitic stainless steel with high Mn content

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Table 1 Similar Patent Steel Composition Control Comparison (Wt%)

[0033] Patent No

C

Si

mn

P

S

Cr

Ni

Mo

Cu

Ti

Nb

CN1697889

0.03-0.1

≤0.5

1-2.5

-

-

10-15

-

-

-

0.01-0.5

0.01-1.0

Wo2007029626

0.05-0.1

0.1-1.0

0.2-2

≤0.04

≤0.01

11-14

0.5-2

1-2

0.5-2

≤0.1

0.03-0.3

this invention

0.03-0.1

0.2-0.8

1.2-3.0

≤0.03

≤0.02

12-14

[0034] Patent No

V

Zr

Al

Ta

Hf

N

CN1697889

0.01-0.5

0.01-1.0

-

≤0.5

≤0.5

0.005-(Ti+V)×14 / 50+(Nb+Zr)×14 / 90

Wo2007029626

-

-

≤0.1

0.01-0.025

this invention

0.008-0.03

[0035] Among them, the 13Cr martensitic stainless ste...

Embodiment 2

[0040] According to the chemical composition range designed by the present invention, 5 furnaces of steel were smelted on the vacuum induction furnace, which we named as No. 1 furnace, No. 2 furnace, No. 3 furnace, No. 4 furnace, and No. 5 furnace respectively. The chemical composition is shown in Table 2.

[0041] All the 5 furnaces of molten steel were poured into small steel ingots, and the steel ingots were sand-cooled with molds, and demoulded after cooling to room temperature. After demoulding, the surface of the ingot is ground and forged, and finally heated to 1200°C and hot-rolled into a plate. Sample processing is carried out on the plate according to the requirements of the national standard. The steel was annealed at 760°C and quenched at 1000°C respectively, and its strength, hardness, plasticity and corrosion resistance were tested. The corrosion resistance test adopts the salt spray corrosion method, and the corrosion period is 120 hours. The test results are ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a martensitic stainless steel with high Mn content, which comprises the following chemical compositions in percentage by weight: 0.03-0.1% of C, 0.20-0.80% of Si, 1.2-3.0% of Mn, 12-14% of Cr, 0.008-0.03% of N, the balance Fe and unavoidable impurities. By improving Mn content in steel, adding proper amount of N and utilizing Mn and N to strengthen, the invention improves the strength and the rigidity of the martensitic stainless steel. Compared with other alloys, the cost of Mn is lower and the resource is richer. The low-carbon martensitic stainless steel after being strengthened by utilizing Mn and N only needs quenching heat treatment to obtain martensitic stainless steel materials with favorable strength, tenacity and corrosion resistance, and has more convenient use and superior performance compared with commonly used tempered martensitic stainless steel.

Description

technical field [0001] The invention relates to a martensitic stainless steel, in particular to a martensitic stainless steel with high Mn content, high strength, high hardness and high corrosion resistance. Background technique [0002] Martensitic stainless steel is generally used after quenching and tempering heat treatment. The purpose of tempering is to eliminate quenching stress and obtain a stable structure. However, when Cr13 type martensitic stainless steel is tempered at 375-590 °C, there is temper brittleness. After research, this temper brittleness is caused by local overaging of grain boundary carbides. Due to the disadvantages of brittleness, welding, etc., the use of traditional martensitic stainless steel is limited. Therefore, the development of cost-effective high-strength, high-hardness and high-corrosion martensitic stainless steel has become an urgent problem to be solved. [0003] The 13Cr martensitic stainless steel applied by the European "The Thoms...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/38C22C38/18C21D1/18
Inventor 翟瑞银程晓波郑宏光常锷张昧茗
Owner BAOSTEEL DESHENG STAINLESS STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com