Anhydrous zinc tartrate ferroelectric function material and preparation method thereof

A ferroelectric functional material, the technology of zinc tartrate, applied in the preparation of carboxylate, organic chemistry, etc., can solve the problem of limiting the use temperature range of metal-organic functional complexes, etc. good stability

Inactive Publication Date: 2010-02-24
NINGBO UNIV
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] During the self-assembly process of metal-organic complexes, crystal water molecules or coordinated water molecules are easily formed in the complex structure, which greatly limits the use temperature range of metal-organic functional complexes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anhydrous zinc tartrate ferroelectric function material and preparation method thereof
  • Anhydrous zinc tartrate ferroelectric function material and preparation method thereof
  • Anhydrous zinc tartrate ferroelectric function material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Weigh 0.02mol L-(+)-tartaric acid (C 4 h 6 o 6 ) was dissolved in 100mL deionized water, and prepared into a solution with a concentration of 0.2mol / L for later use; zinc nitrate (Zn(NO 3 )·6H 2 0), slowly add zinc nitrate to the prepared L-(+)-tartaric acid solution while stirring, after stirring for 30 minutes, zinc nitrate is also added and fully dissolved, and the insoluble matter is removed by filtration, and the obtained filtrate is zinc tartrate solution, and then adjust the pH of the filtrate to 4.0 with 0.5mol / L ammonia solution, stir the filtrate at a constant temperature of 50°C for 3 hours, and filter with suction to obtain white powder crystals; dehydrate the crystals in an oven at 80°C for 8 hours to obtain white powder The body was ground in an agate mortar and passed through a 100-mesh sieve to obtain anhydrous zinc tartrate ferroelectric powder with ferroelectric properties.

Embodiment 2

[0026] Weigh 0.06mol tartaric acid (C 4 h 6 o 6 ) was dissolved in 100mL deionized water, and prepared into a solution with a concentration of 0.6mol / L for use. Weigh zinc nitrate (Zn(NO 3 ) 2 ·6H 2(2), while stirring, zinc nitrate is slowly added to the pre-configured tartaric acid solution, stirred for 40min, zinc nitrate has also been added and fully dissolved, and the insolubles are removed by filtration, and the gained filtrate is zinc tartrate solution. Then use 1mol / L NaOH solution to adjust the pH of the filtrate to 6.0, stir the filtrate at a constant temperature of 50°C for 1h to form a white turbid liquid, cool it to room temperature and age it for 2h, then filter it with suction to obtain a white powder crystal, which is removed by filtration Insoluble matter, the resulting filtrate is zinc tartrate solution. It was dehydrated in an oven at 120°C for 6 hours to obtain a white powder, which was ground and passed through a 100-mesh sieve to obtain white [Zn(C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
remanent polarizationaaaaaaaaaa
saturated polarizationaaaaaaaaaa
saturated polarizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anhydrous zinc tartrate ferroelectric function material, the molecular formula of which is Zn(C4H4O6), and the ferroelectric function material can pass through white powderwith purity of no less than 99 percent of 100 meshes, the heat quantitative temperature of the white powder is 350 DEG C, parameters of the ferroelectric properties of the ferroelectric function material is respectively as follows: Ps=0.43 mu C.cm<-2>, 2Pr=0.73 mu C.cm<-2>, 2Ec=0.47 kV.cm<-1>; thereby, the anhydrous zinc tartrate ferroelectric function material has better ferroelectric propertiesand thermalstability; the invention also discloses a preparation method of the ferroelectric function material, which can realize the nucleus formation and growth processes of the prophase product ofthe anhydrous zinc tartrate through controlling the concentration and proportion of the materials, the adding speed of the reactants, the stirring time, the temperature of the reaction system, pH control of the solution and the like, in addition, dehydration treatment is then carried out, and anhydrous zinc tartrate ferroelectric power with higher purity and good performance can be obtained.

Description

technical field [0001] The invention relates to ferroelectric functional materials, in particular to anhydrous zinc tartrate ferroelectric functional materials and a preparation method thereof. Background technique [0002] Ferroelectric functional materials (ferroelectrics) refer to a class of functional materials whose crystal structure has spontaneous polarization when no external electric field is applied, and the direction of spontaneous polarization can be reversed or reoriented by an external electric field. Due to their excellent ferroelectric, dielectric, pyroelectric, and piezoelectric properties, ferroelectric materials are widely used in modern electronic technologies and micromechanical technologies such as ferroelectric memories, infrared detectors, surface acoustic waves, and integrated optoelectronic devices. In terms of solid-state devices, research on ferroelectric materials and their applications has become one of the most popular research topics in the fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C59/255C07C51/41
Inventor 郑岳青刘文林建利许伟
Owner NINGBO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com