Manometer aqueous high-temperature-resistant metal-baking coating

A high-temperature, water-based technology, applied in coatings and other directions, can solve problems such as health hazards and secondary air pollution, and achieve the effects of good chemical resistance, good material performance, and fast heat transfer.

Active Publication Date: 2010-01-06
SKSHU PAINT
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most home appliances, kitchen utensils, and ceramic products use a large number of organic coatings and solvent-based paints. Soft, causing secondary air pollution, causing great harm to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0050] The proportioning (% by weight) of embodiment two is as follows:

[0051] A component: water-based high temperature resistant nano resin 84

[0052] Water-based aluminum silver paste or pearlescent pigment 10

[0053] Dispersant 0.1

[0054] Leveling agent 0.1

[0055] Coalescent 2

[0056] PH value regulator 0.1

[0057] Purified water 3.7

[0058] B component: water-based curing agent

[0059] Among them, component A: component B = 3-4:1, use after aging for 0.5-2 hours, drying method: 160°C / 20 minutes.

Embodiment 3

[0060] The proportioning (% by weight) of embodiment three is as follows:

[0061] A component: water-based high temperature resistant nano-resin 90

[0062] Water-based aluminum silver paste or pearlescent pigment 4

[0063] Dispersant 0.3

[0064] Leveling agent 0.3

[0065] Coalescent 1

[0066] PH value regulator 0.3

[0067] Purified water 4.1

[0068] B component: water-based curing agent

[0069] Among them, component A: component B = 3-4:1, use after aging for 0.5-2 hours, drying method: 160°C / 20 minutes.

[0070] Wherein, the formula of a preferred embodiment of the present invention is as follows (by weight %)

[0071] A component: water-based high temperature resistant nano resin 80

[0072] Water-based aluminum silver paste or pearlescent pigment 4

[0073] Dispersant 0.5

[0074] Leveling agent 0.5

[0075] Coalescent 5

[0076] PH value regulator 0.1

[0077] Purified w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an aqueous coating, in particular to a nanometer aqueous high-temperature-resistant metal-baking coating which can be used for decorating the surfaces of building materials and household kitchenware, such as electric irons, cookers, high-temperature lamps, ceramic products, and the like and has high temperature (600-700 DEG C) resistance, weatherability longer than 30 years and high rigidity. The preparation process comprises the following steps: mixing aqueous aluminum paste or aqueous pearlescent pigment, water and a dispersant at a low speed to prepare a semi-finished product of aqueous aluminum paste or aqueous pearlescent pigment; sequentially adding aqueous high-temperature-resistant nanometer resin, a flatting agent, a film-forming additive and a pH value regulator at a medium speed; and filtering and packaging after the semi-finished product is detected to be qualified to obtain the nanometer aqueous high-temperature-resistant metal-baking coating. The invention contains no toxic organic solvent, is pollution-free and has the advantages of high temperature resistance, weatherability longer than 30 years, high rigidity, wide suitability, and the like.

Description

【Technical field】 [0001] The invention relates to a water-based high-temperature resistant nano-coating, in particular to a surface decoration that can be widely used in electric irons, cooking utensils, high-temperature lamps and ceramic products and other household appliances and kitchen utensils and building materials. It has high temperature resistance, weather resistance for more than 30 years, high Water-based high temperature resistant nano coating with hardness and wide applicability. 【Background technique】 [0002] At present, most home appliances, kitchen utensils, and ceramic products use a large number of organic coatings and solvent-based paints. Soft, causing secondary pollution of the air, causing great harm to human health. 【Content of invention】 [0003] The invention aims at the secondary pollution generated when the paint is dried on high-temperature appliances or used, and provides a nano-water-based high-temperature-resistant metal baking paint that c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D7/12C09D5/00
Inventor 洪杰
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com