Oil-proof PVC sheath material for earphone wire

A sheath material and earphone cable technology, applied in the directions of earphones/earphone accessories, etc., can solve the problems of losing the softness of the earphone cable, being easily corroded by oil products, and having poor oil corrosion resistance, and achieving a bright and smooth appearance and easy outer diameter. Control, the effect of early plasticization time

Inactive Publication Date: 2009-11-25
浙江富舜科技股份有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the formula is: SH-200 (PVC resin) 45-50 parts, TOTM (triisooctyl trimellitate plasticizer) about 35 parts, HD2500 (heavy calcium carbonate filler) 20-25 parts, Yingtian (Stabilizer) The PVC sheath material for headphone wires made from 2-3 parts of raw materials. Although the headphone wires made of this PVC sheath material have good softness, they are poor in oil corrosion resistance and soft and stable. Poor resistance, easy to be corroded by oil, resulting in thinner earphone cable, increased hardness, and lost the softness that the earphone cable should have

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-proof PVC sheath material for earphone wire
  • Oil-proof PVC sheath material for earphone wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0010] The oil-resistant grade PVC sheath material for earphone cables consists of 48 parts of WS-1300, 25 parts of W-2050, 22 parts of a mixed filler composed of HD2500 and CCR-603 in a weight ratio of 1:1, 3 parts of YC-300, 1.5 parts 1 part of LOCK and 0.3 part of UV-201 are used as raw materials, uniformly mixed, extruded and granulated by a twin-screw extruder to obtain a PVC sheath material.

[0011] In the above examples, WS-1300 can also be 45 parts or 50 parts, etc.; W-2050 can also be 25 parts, 28 parts, 32 parts or 35 parts, etc.; the mixed filler can also be 20 parts or 25 parts, etc., wherein The weight ratio of HD2500 and CCR-603 can also be 1:2, etc.; YC-300 can also be 2 or 5 parts; LOCK can also be 2 or 0.5 parts; UV-201 can also be 0.1 or 0.5 Parts, etc.; not one by one examples here.

[0012] The PVC sheath material of the present invention is carried out mechanical property measurement test and obtains the result as table 1, can find out from table 1 that ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses an oil-proof PVC sheath material for earphone wire, which is obtained by evenly mixing and then, in a double screw extruder, extrusion-granulating the following raw materials, based on weight part, of: 45-50 parts of WS-1300, 25-35 parts of W-2050, 20-25 parts of mixed filler, 2-5 parts of YC-300 and 0.5-2.0 parts of LOCK, the mixed filler is formulated by HD-2500 and CCR-603 in accordance with weight ratio of 1:1-2; the sheath material is not liable to be extracted by organic solvent like oil product after being processed to the earphone wire, has preferable corrosive resistance to organic solvent like oil product, and still has good elasticity and softness after being immersed in organic solvent like oil product. Therefore, the invention is oil-proof PVC sheath material for earphone wire that has preferable oil product resistance and softness stability.

Description

technical field [0001] The invention relates to a cable sheath material, in particular to an oil-resistant PVC sheath material for earphone wires. Background technique [0002] The sheath material of the outermost layer of the cable is an important protective layer, which has properties such as sun resistance, radiation resistance, wear resistance, heat resistance, aging resistance, and chemical corrosion resistance; for example, the publication number is CN101407612A, and the publication date is April 2009 On the 15th, the name of the invention application is a soft thermoplastic sheath material for mobile power and control cables, and it is disclosed that it is composed of chlorinated polyethylene, silane coupling agent, polyethylene wax plasticizer, anti-aging agent, stabilizer, barrier The raw material formula composed of fuel and reinforcing agent is extruded and granulated by a screw extruder. At present, the commonly used raw material formulations for the production ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02H04R1/10
Inventor 吴建波韦亚峰何文求易雄飞
Owner 浙江富舜科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com