Fiber surface PE protective film pressure sensitive adhesive and preparation method thereof

A fiber surface, protective film technology, applied in the direction of adhesive types, ester copolymer adhesives, etc., can solve the problems of low pressure-sensitive adhesive viscosity, PE film convex roll, etc., to achieve good viscosity and less coating amount Effect

Inactive Publication Date: 2009-11-11
广东华丽宝实业有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the low viscosity of the existing pressure-sensitive adhesive, in order to ensure the bonding quality, it is necessary to coat a large amount of pressure-sensitive adhesive on the PE film, but because the thickness of the PE film is relatively thin, when a large amount of pressure-sensitive adhesive is coated, The pressure-sensitive adhesive will shrink during the drying process, which will cause the PE film to roll, and when the protective film is peeled off, there will be residual glue on the protected surface, so a PE film with good use effect will be developed. Protective film pressure-sensitive adhesive has been put on people's research agenda

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A PE protective film pressure-sensitive adhesive used on the surface of fibers, made of the following raw materials: 2-ethylhexyl acrylate: 30-38 parts, vinyl acetate: 0-4 parts, hydroxyacrylate Ethyl ester: 0.4-2 parts, acrylic acid: 1.6-4 parts, solvent: 55-60 parts;

[0013] The optimum parts by weight of the PE protective film pressure-sensitive adhesive is: 2-ethylhexyl acrylate: 35 parts, vinyl acetate: 2 parts, hydroxyethyl acrylate: 1 part, acrylic acid: 3 parts, solvent : 60 servings.

[0014] A method for producing the above-mentioned PE protective film pressure-sensitive adhesive, the steps are as follows:

[0015] 1): Weigh various raw materials in proportion;

[0016] 2): Add 2-ethylhexyl acrylate, vinyl acetate, hydroxyethyl acrylate, and acrylic acid into the solvent and heat to 80°C for stirring. Polymerization reaction occurs inside, and the material can be discharged in 8 hours.

[0017] The PE protective film pressure-sensitive adhesive produced by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fiber surface PE protective film pressure sensitive adhesive, which is prepared from the following raw materials by mass portion: 30 to 38 portions of acrylic acid 2-ethylhexyl acrylate, 0 to 4 portions of vinyl acetate, 0.4 to 2 portions of hydroxy-ethyl acrylate, 1.6 to 4 portions of acrylic acid and 55 to 60 portions of solvent. The PE protective film pressure sensitive adhesive prepared by the process is good in viscosity, can achieve a pressure sensitive effect by coating in a small amount during use, avoids PE thin film protruding and winding during drying due to small coated amount and prevents residual adhesive on a protected surface when the protective film is stripped, thereby being widely used for the manufacturing of PE protective films.

Description

technical field [0001] The invention relates to a protective film pressure-sensitive adhesive, specifically a PE protective film pressure-sensitive adhesive used on the surface of fibers, and also relates to a preparation method of the protective film pressure-sensitive adhesive. Background technique [0002] At present, the protective film used on the fiber surface is made of PE film as the base material, rubber or acrylate polymer as the pressure-sensitive adhesive, and processed by coating and drying methods. [0003] Due to the low viscosity of the existing pressure-sensitive adhesive, in order to ensure the bonding quality, it is necessary to coat a large amount of pressure-sensitive adhesive on the PE film, but because the thickness of the PE film is relatively thin, when a large amount of pressure-sensitive adhesive is coated, The pressure-sensitive adhesive will shrink during the drying process, which will cause the PE film to roll, and when the protective film is pe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/06
Inventor 胡和金
Owner 广东华丽宝实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products