Preparation method of phthalocyanine colored cement intermediate and phthalocyanine colored cement intermediate

A technology of colored cement and a manufacturing method, which is applied to the manufacturing field of phthalocyanine colored cement intermediates and phthalocyanine colored cement intermediates, can solve the problems of high use difficulty, high use cost, poor weather resistance, etc., and achieves low cost and economical use. Cost, operability and strong effect

Active Publication Date: 2011-12-14
BEIJING KANGZHIWEI SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Phthalocyanine has bright color and high coloring rate, but it is difficult to use (it is not easy to disperse uniformly in cement) and has poor weather resistance; cobalt blue is stable, positive in color, and has good weather resistance, but the use cost is extremely high; chrome green is stable and has good weather resistance , but the coloring rate is low, and the cost of use is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1, the phthalocyanine colored cement intermediate of the present invention is fully mixed with 100 kg of white cement, 1 kg of talcum powder, 1 kg of phthalocyanine and 0.3 kg of cement dispersant. For thorough mixing, phthalocyanine, cement dispersant, and talcum powder are mixed first, then added to white cement for mixing, and finally added to a ball mill for grinding.

Embodiment 2

[0021] Embodiment 2, the phthalocyanine colored cement intermediate of the present invention is fully mixed with 100 kilograms of white cement, 3 kilograms of talcum powder, 5 kilograms of phthalocyanine and 5 kilograms of cement dispersant. For thorough mixing, phthalocyanine, cement dispersant, and talcum powder are mixed first, then added to white cement for mixing, and finally added to a ball mill for grinding.

Embodiment 3

[0022] Embodiment 3, the phthalocyanine colored cement intermediate of the present invention is fully mixed with 100 kg of white cement, 1 kg of talcum powder, 5 kg of phthalocyanine and 0.3 kg of cement dispersant. For thorough mixing, phthalocyanine, cement dispersant, and talcum powder are mixed first, then added to white cement for mixing, and finally added to a ball mill for grinding.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a kind of manufacturing method of phthalocyanine color cement intermediate and phthalocyanine color cement intermediate, in order to solve the problem that phthalocyanine is not easy to disperse in cement, the method is to mix phthalocyanine, white cement, cement dispersant, talcum powder After mixing, add it into a ball mill and grind it. Mixing is to mix phthalocyanine, cement dispersant and talcum powder first, and then add them to white cement for mixing. The phthalocyanine colored cement intermediate is fully mixed with white cement, talc powder accounting for 1-3% of the weight of white cement, phthalocyanine accounting for 1-5% of the weight of white cement, and cement dispersant accounting for 30-100% of the weight of phthalocyanine . The method is to subdivide and blend phthalocyanine and white cement to the greatest extent under the action of additives and ball milling to form a uniform intermediate. The method has the advantages of simple operation, strong operability, low process cost, and can ensure the dispersion degree of phthalocyanine. The intermediate completely overcomes the defect that phthalocyanine is not easy to disperse in cement. When using it, it only needs to be mixed into the concrete material in proportion. When it is applied to concrete, it can achieve the effect of uniform dispersion and long-lasting concrete color, and save a lot of use cost. . It has the advantages of bright color, high coloring rate, good dispersion, good stability and low cost.

Description

technical field [0001] The invention relates to colored cement, in particular to a method for manufacturing a phthalocyanine colored cement intermediate, a method for manufacturing a phthalocyanine colored cement intermediate, and a phthalocyanine colored cement intermediate. Background technique [0002] In the colorful world, blue-green plays an important role and is mostly loved by people. People enjoy the pleasure brought by blue-green from paint, printing, etc., but they are not satisfied. In modern times, colored concrete has been developed, and blue-green is also applied to colored concrete as people explore. [0003] The blue-greens recognized by most people mainly include phthalocyanine, cobalt blue, chrome green and so on. Phthalocyanine has bright color and high coloring rate, but it is difficult to use (it is not easy to disperse uniformly in cement) and has poor weather resistance; cobalt blue is stable, positive in color, and has good weather resistance, but t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/42C04B7/38
CPCC04B2111/802C04B2111/82C04B28/02
Inventor 陈向前郭洪喜
Owner BEIJING KANGZHIWEI SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products