Composite ecological wood

A technology of ecological wood and wood powder, which is applied in the field of composite ecological wood, can solve the problems of reducing cost, reducing product weight, reducing the stiffness of composites, etc., and achieves the effects of simple and personalized shape, good energy saving and prolonging service life

Inactive Publication Date: 2009-09-16
孙玉武
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, substituting these organic fillers for inorganic fillers can significantly reduce the weight of the article and reduce the cost without reducing the stiffness of the composite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of composite ecological wood of the present invention comprises the raw material ratio of following parts by weight:

[0036] Wood flour: 35%, PVC: 45%, calcium carbonate: 2%, foam regulator: 5%,

[0037] Stabilizer: 5%, impact ACR: 5%, processing aid ACR: 1%,

[0038] Toner, internal lubricant, external lubricant: 0.3%,

[0039] Foaming agent: 0.45%, coupling agent: 1.25%,

[0040] The particle size of the above-mentioned wood flour is 300 mesh, PVC is selected as 700, and calcium carbonate is active light calcium carbonate.

[0041] Among them, the two contents of wood powder and PVC account for 80% of the total composition, and the stabilizer is a lead salt composite stabilizer.

Embodiment 2

[0043] A kind of composite ecological wood of the present invention comprises the raw material ratio of following parts by weight:

[0044] Wood flour: 40%, PVC: 40%, calcium carbonate: 3%,

[0045] Foam regulator: 6%, stabilizer: 5%, impact ACR: 4%,

[0046] Processing aid ACR: 0.5%, toner, internal lubricant, external lubricant: 0.4%,

[0047] Foaming agent: 0.75%, coupling agent: 0.35%,

[0048] The particle size of the above-mentioned wood powder is 150 mesh, PVC is selected as type 7, and calcium carbonate is active light calcium carbonate.

[0049] Among them, wood powder and PVC account for 80% of the total composition, and the stabilizer is a calcium-zinc composite stabilizer.

Embodiment 3

[0051] A kind of composite ecological wood of the present invention comprises the raw material ratio of following parts by weight:

[0052] Wood flour: 35%, PVC: 49%, calcium carbonate: 2%,

[0053] Foam regulator: 4%, stabilizer: 4%, impact ACR: 4%

[0054] Processing aid ACR: 0.5%,

[0055] Toner, internal lubricant, external lubricant: 0.2%,

[0056] Foaming agent: 0.25%, coupling agent: 1.05%,

[0057] The particle size of the above-mentioned wood powder is between 150-300 mesh, PVC is selected to be 7 or 700, and the calcium carbonate is active light calcium carbonate.

[0058] Among them, the two contents of wood powder and PVC account for 84% of the total composition, and the stabilizer is a lead salt composite stabilizer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides composite ecological wood. The wood comprises the following compositions in percentage by weight: 35 to 40 percent of wood meal, 40 to 49 percent of PVC, 2 to 3 percent of calcium carbonate, 4 to 6 percent of a foaming regulator, 4 to 6 percent of a stabilizing agent, 4 to 6 percent of impact-resistant ACR, 0.5 to 1.5 percent of a processing additive ACR, 0.2 to 0.4 percent of toner, an internal lubricant and an external lubricant, a foaming agent accounting for 0.1 to 1 percent of the PVC and a coupling agent accounting for 3 to 5 percent of the wood meal; and when a product is used outdoors, the product also comprises an antioxidant, an ultraviolet absorbent and a light stabilizing agent which have 0.1 to 0.5 percent of weight portions respectively. Compared with the prior art, the composite ecological wood thoroughly overcomes the disadvantages of raw wood, improves the shortage of the raw wood and keeps the particular wooden texture of the raw wood; simultaneously, for the addition of the antioxidant, the ultraviolet absorbent and the light stabilizing agent, the composite ecological wood also prevents photooxidation, fading, cracking and the like caused by ultraviolet irradiation, increases the weather resistance and prolongs the service life.

Description

(1) Technical field [0001] The invention relates to a building material, in particular to a compound ecological wood of a certain shape, which is made by mixing resin and wood fiber material in a certain proportion, and then making it into a certain shape through high temperature, extrusion, molding and other processes. (2) Technical background [0002] With the rapid development of high-rise buildings in our country, various fireproof materials such as indoor suit door materials and composite materials continue to emerge. However, most of the existing plastic reinforcing fillers on the market are calcium carbonate and glass fiber, accounting for 40% and 31% respectively, and some other inorganic fillers such as talcum powder, glass microspheres, etc., these traditional fillers make the composite very difficult. Large performance variations, and the cost of these fillers is relatively high. In the past few years, some natural organic reinforcing fillers such as cellulose fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08K3/26
Inventor 孙玉武
Owner 孙玉武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products