Low-temperature scouring and bleaching adjuvant composition and method for producing the same

A technology of low-temperature scouring and bleaching auxiliaries and compositions, which is used in bleaching products, textiles and papermaking, fiber processing, etc., can solve the problems of long time, low hydrogen peroxide efficiency, and increased dosage of oxidants, and achieves reduced strength loss and less damage. , The effect of convenient transportation

Active Publication Date: 2009-07-22
NINGBO GUANG YUAN FABRIC
View PDF0 Cites 55 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there have been attempts at low-temperature processes in dyeing and finishing innovations, such as: low-temperature cold pad-batch pretreatment and bleaching processes for cotton fabrics. In the absence of low-temperature oxidation activators, conventional hydrogen peroxide / NaOH systems are used for low-temperature bleaching. When bleaching, it is necessary to increase the amount of oxidant and prolong the treatment time. Although certain effects can be obtained in this way, due to the low efficiency of hydrogen peroxide at low temperatures, the process always has problems in removing cottonseed hulls, poor fabric whiteness and water absorption, and the drawback of taking too long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] In the powder mixer, 70% by weight of 100-200 mesh diatomite, 3% by weight of tetraacetylethylenediamine TAED, 0.5% by weight of manganese gluconate, 15% by weight of ethylenediaminetetramethylene phosphoric acid, and 6% by weight of borate, mixed for 45 minutes until uniform, then 2% by weight of sodium α-alkenyl sulfonate, C 12 (CH 2 CHO) 5 (CH 3 CH 2 CH 2 O) 2 3.5% by weight, then stirred for 15 minutes, and discharged, and it was a solid powder product.

Embodiment 2

[0037] In a powder mixer, add 60% by weight of 100-200 mesh kaolin, 5% by weight of tetraacetylethylenediamine TAED, 15% by weight of tetrasodium ethylenediaminetetraacetic acid, and 10% by weight of percarbonate, and mix for 45 minutes to Evenly, add 2% by weight of sodium α-olefin sulfonate, C 12 (CH 2 CHO) 5 (CH 3 CH 2 CH 2 O) 2 8% by weight, then stirred for 15 minutes, and discharged, which was a solid powder product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a low-temperature scouring and bleaching promoter composition and a preparation method thereof. The composition comprises 2.5-5.5% of Tetra acetyl ethylene diamine (TAED), 0-0.5% of hydrogen peroxide decomposition catalyst, 5-15% of bleaching potentiator, 10-15% of chelating agent, 77-54.5% of carrier and 5-10% of surfactant, according to the weight percentage. The preparation method comprises the steps as follows: the carrier, the TAED, the hydrogen peroxide decomposition catalyst, the chelating agent and the bleaching potentiator are sequentially added in a powder mixer and mixed uniformly for 45-60min; subsequently, the surfactant is added and all mixtures are mixed for 15-30min and then discharged, thus obtaining the composition. The low-temperature scouring and bleaching promoter composition belongs to the environment-protective promoter composition, contains no phosphor and other substances harmful to the environmental protection, has no AOX problem, achieves the object that one promoter replaces more than four promoters, and facilitates processing and quality control.

Description

technical field [0001] The invention belongs to the field of environment-friendly low-temperature scouring and bleaching auxiliaries and the preparation thereof, and in particular relates to a low-temperature scouring and bleaching auxiliaries composition and a preparation method thereof. Background technique [0002] Cotton knitted fabrics are composed of cotton fibers. Cotton fiber contains 0.4-1.2% pectin, 0.4-1.2% oil wax, 1.0-1.9% nitrogen-containing substances, 0.7-1.6% ash and a small amount of pigment and other natural impurities (called cotton fiber symbionts), and cottonseed hulls (called companions). Symbiosis mainly exists in the cuticle and primary rubber wall of cotton fiber. Their existence makes cotton fiber hydrophobic, affects water absorption, and hinders the penetration and diffusion of dyes in the dyeing process. Cotton seed hulls affect the appearance of fabrics. Therefore, the symbiotic and accompanying organisms must be removed in the dyeing and ble...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06L3/02D06M11/50D06M13/262D06L4/12D06L4/13
Inventor 傅红萍吴日高
Owner NINGBO GUANG YUAN FABRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products