Airtight rubber of all-steel radial tyre and preparation method thereof

A radial tire and inner liner rubber technology, which is used in the preparation of inner liner rubber, can solve the problems of reducing air permeability, tire performance decline, uneven dispersion of carbon black and small materials, etc. Effect

Active Publication Date: 2009-04-29
JIANGSU GENERAL SCI TECH
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the airtightness of the tire innerliner has a good correlation with the thickness, increasing the thickness will increase the airtightness or reduce the air permeability, so in order to further improve the airtightness of the innerliner, the general method is to increase the airtightness The thickness of the inner layer, but the increase of the thickness of the inner inner layer will bring three adverse effects: one is the increase of the cost of the tire; second, the increase of the thickness should avoid air bubbles in the molding process; The increase in tire weight will reduce the heat dissipation performance of the tire, the high-speed performance and the fuel consumption of the car
In addition, the pure bromobutyl rubber formula also has many disadvantages in production and use: uneven dispersion of carbon black and small materials, poor adhesion with the transition layer, and easy to appear bubbles when laminating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Described all-steel radial tire (with inner tube series) airtight layer formula comprises the following components by weight: natural rubber is 60 parts by weight, styrene-butadiene rubber is 40 parts by weight, reinforcing agent carbon black N660 is 40 parts by weight, The activator zinc oxide is 3 parts by weight, the stearic acid is 1 part by weight, the tackifier 204 resin is 2.5 parts by weight, the leveling agent UB4000 is 2 parts by weight, the anti-aging agent 4020 is 0.5 parts by weight, and the anti-aging agent RD is 0.5 parts by weight , 1 part by weight of protective wax, 2 parts by weight of aromatic oil as a softening plasticizer, 0.5 part by weight of sulfur as a vulcanizing agent, and 1.0 part by weight of accelerator NS.

[0019] The preparation method of the above-mentioned all-steel radial tire (with inner tube series) inner liner adhesive comprises the steps:

[0020] One-stage mixing: Start the internal mixer, set the rotor speed of the internal mix...

Embodiment 2

[0025] Described all-steel radial tire (with inner tube series) airtight layer formula comprises the following components by weight: natural rubber is 80 weight parts, styrene-butadiene rubber is 20 weight parts, reinforcing agent carbon black N660 is 55 weight parts, The activator zinc oxide is 4 parts by weight, the stearic acid is 2.5 parts by weight, the tackifier 204 resin is 3.5 parts by weight, the leveling agent 40MSF is 3 parts by weight, the anti-aging agent 4020 is 1.0 parts by weight, and the anti-aging agent RD is 1.0 parts by weight , the protective wax is 1.5 parts by weight, the softening plasticizer aromatic oil is 2.5 parts by weight, the vulcanizing agent sulfur is 0.8 parts by weight, and the accelerator NS (TBBS) is 2.0 parts by weight.

[0026] The preparation method of the above-mentioned all-steel radial tire (with inner tube series) inner liner adhesive comprises the steps:

[0027] One-stage mixing: Start the internal mixer, set the rotor speed of the...

Embodiment 3

[0032] Described all-steel radial tire (inner tube series) airtight layer formula comprises the following components by weight: natural rubber is 70 parts by weight, styrene-butadiene rubber is 30 parts by weight, reinforcing agent carbon black N660 is 65 parts by weight, The activator zinc oxide is 7 parts by weight, the stearic acid is 4 parts by weight, the tackifier 204 resin is 5 parts by weight, the leveling agent UB4000 is 5 parts by weight, the anti-aging agent 4020 is 2.0 parts by weight, and the anti-aging agent RD is 2.0 parts by weight , the protective wax is 3 parts by weight, the softening plasticizer aromatic oil is 4 parts by weight, the vulcanizing agent sulfur is 1.0 parts by weight, and the accelerator TBBS is 3.0 parts by weight.

[0033] The preparation method of the above-mentioned all-steel radial tire (with inner tube series) inner liner adhesive comprises the steps:

[0034] One-stage mixing: Start the internal mixer, set the rotor speed of the interna...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an air-barrier glue for all-steel-wire truck radial tires, as well as a preparation method thereof. The glue comprises the following components in weight portion: 60 to 80 portions of natural glue, 20 to 40 portions of butadiene-styrene rubber, 40 to 65 portions of carbon black N660 as a reinforcing agent, 3 to 7 portions of zinc oxide as an activator, 1 to 4 portions of stearic acid, 2.5 to 5 portions of 204 resin as a tackifier, 2 to 5 portions of homogenizing agent UB4000 or 2 to 5 portions of homogenizing agent 40MSF, 0.5 to 2 portions of antiager 4020, 0.5 to 2 portions of antiager RD, 1 to 3 portions of protective wax, 2 to 4 portions of aromatic oil as a softening plasticizer, 0.5 to 1.0 portions of sulfur as a vulcanizing agent and 1.0 to 3.0 portions of accelerator NS or 1.0 to 3.0 portions of accelerator TBBS.

Description

technical field [0001] The invention discloses an inner liner adhesive of an all-steel wire load radial tire, and also discloses a preparation method of the inner liner adhesive of an all-steel load radial tire. Background technique [0002] Generally, the inner liner of radial tires uses natural rubber / chlorinated butyl rubber, natural rubber / brominated butyl rubber in combination, or chlorinated butyl rubber and brominated butyl rubber are used alone. The airtightness is quite good. Since the airtightness of the tire innerliner has a good correlation with the thickness, increasing the thickness will increase the airtightness or reduce the air permeability, so in order to further improve the airtightness of the innerliner, the general method is to increase the airtightness The thickness of the inner layer, but the increase of the thickness of the inner inner layer will bring three adverse effects: one is the increase of the cost of the tire; second, the increase of the thi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08K13/02B29B7/28C08K3/22C08K5/09C08K3/06
Inventor 顾瑞
Owner JIANGSU GENERAL SCI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products