Method for preparing environment friendly ceramic gaged brick by Yellow River sediment

A technology of clear water bricks and sand, applied in the field of building materials, can solve the problem of low effective utilization rate, and achieve the effect of improving the decoration grade, broadening the application scope and increasing the added value.

Inactive Publication Date: 2012-07-25
WUHAN UNIV OF TECH
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Controlling the sediment of the Yellow River has become the focus and difficulty of controlling the Yellow River, but its effective utilization rate is still very low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for preparing environmentally friendly ceramic clear water bricks by utilizing the sediments of the Yellow River, which comprises the following steps:

[0027] 1) Billet preparation: excavate the Yellow River sediment in the Binzhou section of Shandong from the riverbed, and stack it by the river for 15 years to become the Yellow River sedimentary sediment (fully weathered); when used, if the moisture content exceeds 5wt%, the Yellow River sedimentary sediment The sand is dried on a chain plate dryer to a moisture content of less than 5wt% (weight); the coal gangue and the flux are respectively crushed to 1mm with a jaw crusher, and the clinker is crushed to 1mm for use;

[0028] By weight percentage: 60% of sediment deposited in the Yellow River, 10% of fly ash, 10% of coal gangue, 10% of flux, and 10% of clinker; material, spare;

[0029] Add the sediment, fly ash, coal gangue, flux and clinker deposited by the Yellow River into the twin-shaft mixer, and the...

Embodiment 2

[0038] A method for preparing environmentally friendly ceramic clear water bricks by utilizing the sediments of the Yellow River, which comprises the following steps:

[0039] 1) Billet preparation: The Yellow River sediment in the East A section of Shandong Province was dug out from the river bed and stacked on the riverside for 12 years to become the Yellow River sedimentary sediment (fully weathered); when used, if the moisture content exceeds 5wt%, the Yellow River sedimentary sediment The sand is dried on a chain plate dryer to a moisture content of less than 5wt% (weight); the coal gangue and flux are respectively crushed to less than 1mm with a roller crusher, and the clinker is crushed to 1.5mm for use;

[0040] By weight percentage: 80% of sediment deposited in the Yellow River, 5% of fly ash, 5% of coal gangue, 5% of flux, and 5% of clinker; material, spare;

[0041] Add the sediment, fly ash, coal gangue, flux and clinker deposited by the Yellow River into the twin...

Embodiment 3

[0050] A method for preparing environmentally friendly ceramic clear water bricks by utilizing the sediments of the Yellow River, which comprises the following steps:

[0051] 1) Billet preparation: The Yellow River sediment was dug out of the river bed, and was stacked on the riverside for 20 years to become the Yellow River sedimentary sediment (fully weathered); then the Yellow River sedimentary sediment was dried on a chain plate dryer to a moisture content of 4wt% ( weight); use jaw crusher to crush coal gangue and flux to 0.8mm respectively, and crush clinker to 1mm for standby;

[0052] By weight percentage: 70% of sediment deposited in the Yellow River, 8% of fly ash, 8% of coal gangue, 7% of flux, and 7% of clinker; material, spare;

[0053] Add the sediment, fly ash, coal gangue, flux and clinker deposited by the Yellow River into the twin-shaft mixer, and then add water to mix and stir. 21% of the weight; use a vacuum mud machine to practice mud, and cut into mud ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of building materials, and provides a method for preparing an environment-friendly ceramic plain brick by sediment of the Yellow River. The method is characterized by comprising the following: 1) a step of blank preparation, in which, the sediment of the Yellow River is dug up from riverbed, and is deposited for more than 10 years to be deposited sediment of the Yellow River; the blank comprises the following compositions in weight percentage: 60 to 80 percent of the deposited sediment of the Yellow River, 5 to 10 percent of pulverized fuel ash, 5 to 10 percent of coal refuse, 5 to 10 percent of fluxing agent, and 5 to 10 percent of grog refractory; the compositions are selected for standby; water is added to the mixture for mixing and stirring, wherein the amount of the water is 20 to 22 percent of gross weight of the deposited sediment of the Yellow River, the pulverized fuel ash, the coal refuse, the fluxing agent and the grog refractory; mud is milled by a vacuum pugmill, and is cut into mud cakes; after the mud cakes are aged for 3 days, the blank is produced for standby; 2) a step of glaze preparation; 3) a step of shaping; 4) a step of glazing; 5) a step of drying; and 6) a step of maturing, thereby producing the environment-friendly ceramic plain brick with water content ratio of between 6 and 8 weight percent. The plain brick prepared by the method has the characteristics of high regularity, high strength and strong decoration, and can be directly used for walls bricklaying without external decorating.

Description

technical field [0001] The invention belongs to the technical field of building materials, and particularly relates to a preparation method of ceramic clear water bricks. Background technique [0002] Ceramic facing brick is a sintered wall material that integrates decoration, heat preservation, load-bearing and other functions. Because the ceramic facing brick wall has the breathing function of absorbing and expelling moisture, it naturally adjusts humidity, temperature, and has thermal and sound insulation effects. it is good. People feel comfortable living in this environment. The buildings and landscapes built with ceramic clear water bricks have the characteristics of matte natural, elegant style, solemn and durable, beautiful and generous, and distinctive personality. It is generally believed that the regularity of ceramic clear water bricks is high (the error is within ±1mm), the water absorption rate is low (6-8%), and the compressive strength is high (above 30MPa)...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/34
Inventor 徐晓虹邓大侃吴建锋李坤刘强
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com