High-refractivity and low-dispersion lanthanide optical glass NZLaF30 and method for manufacturing same

A high-refractive-index, optical glass technology, applied in the high-refractive-index and low-dispersion lanthanide optical glass NZLaF30 and its manufacturing field, can solve the problems of bubbles and streaks, affecting product quality, etc.

Inactive Publication Date: 2008-12-31
上海新沪玻璃有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There are bubbles and streaks in the current heavy lanthanum flint optical glass, which affects the product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 4

[0014] The manufacture technique of example 4, metering component by weight is SiO 2 7.5, B 2 o 3 11.0, La 2 o 3 42.9、Ta 2 o 5 17.9, ZrO 2 5.9, Nb 2 o 5 0.90, Gd 2 o 3 13.9 Mix the components evenly and put them into a 300CC platinum crucible, heat and melt in a molybdenum wire rod electric furnace, keep the temperature at 1500°C for 4-5 hours, then lower it to 1360°C, pour it into a preheated iron mold, and put it into the Annealing is carried out in an annealing furnace heated by electric heating wire, kept at 690°C for 4 hours, cooled at 10°C / H to 350°C and turned off, and when it is close to room temperature, take out the glass, observe the quality of the glass, and then take samples to measure nd, nf-nc. At present, this brand can be put into 18 liter volume platinum crucible, smelted in a molybdenum rod heating electric furnace, and put into mass production.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-refractive index low-dispersion lanthanide optical glass NZLaF30, wherein, based on weight percentage, the glass comprises 5.5-10.0 percent of SiO2, 9.5-12.5 percent of B2O3, 41.0-54.0 percent of La2O3, 4.0-7.5 percent of ZrO2, 0.5-5.0 percent of Nb2O5, 11.0-19.5 percent of Ta2O5, 0-15.0 percent of Gd2O3, 0-3.0 percent of Y2O3, 0-3.0 percent of ZnO, and 0-1.0 percent of TiO2. The high-refractive index low-dispersion lanthanide optical glass NZLaF30 has good crystallization and molding properties, and the optical constants (nd, vd) of the glass are in line with the standard requirements; the bubble of the glass reaches grade a; the glass has no stripes.

Description

technical field [0001] The present invention is a grade in the category of heavy lanthanum flint glass, and is used to manufacture high-refractive-index and low-dispersion lanthanide optical glass such as high-grade cameras and high-grade precision instruments. Background technique [0002] There are bubbles and streaks in the current heavy lanthanum flint optical glass, which affects the product quality. Contents of the invention [0003] The object of the present invention is to provide a kind of crystallization property, formability is good, optical constant (nd, vd), air bubble, striae meet standard requirement high refractive index and low dispersion lanthanide optical glass. [0004] The present invention is calculated by weight percentage, wherein SiO 2 -5.5-10.0, B 2 o 3 -9.5-12.5, La 2 o 3 -41.00-54.00, ZrO 2 -4.0-7.5, Nb 2 o 5 -0.5-5.0, Ta 2 o 5 -11.0-19.5, Gd 2 o 3 -0-15.0, Y 2 o 3 -0-3.0, ZnO-0-3.0, TiO 2 -0-1.0. [0005] The present invention i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/068
Inventor 王佩珍翁泽安
Owner 上海新沪玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com