Coating tungsten product

A coating and coating layer technology, applied in the field of high-density tungsten substrates, can solve the problems of perspiration corrosion, poor oxidation resistance, dull color, etc., and achieve the effect of improving oxidation resistance, low cost, and simple preparation

Inactive Publication Date: 2008-06-11
CENT SOUTH UNIV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Uncoated tungsten has defects such as non-wear resistance, poor oxidation resistance, perspiration corrosion, and dull color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] TiN coated pure tungsten.

[0009] Using pure tungsten with a relative density of 99.9% of the theoretical density of pure tungsten as the base material, the TiN coating is coated by CVD or PVD, and the thickness of the coating is 3 μm.

Embodiment 2

[0011] Cu(balance)-(15-45)%Zn-(0.1-1.5)%Ni-(0.5-1)%Al 2 o 3 Alloy coated pure tungsten.

[0012] Use pure tungsten with a relative density of 99.9% of the theoretical density of pure tungsten as the substrate, and coat Cu (remainder)-(15-45)% Zn-(0.1-1.5)% Ni-(0.5-1)% by PVD method Al 2 o 3 Alloy coating, the thickness of the coating is: 30μm.

Embodiment 3

[0014] TiN coating W(balance)-2%Ni-1%Fe alloy.

[0015] The W (remainder)-2%Ni-1%Fe alloy whose relative density is 97% of the theoretical density of pure tungsten is used as the substrate, and the TiN coating is coated by CVD or PVD, and the thickness of the coating is 30 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating tungsten material, including tungsten substrate. A coating layer with the thickness of 3-30 mu m, comprising TiN or alloy with Cu (residue)-15-45% Zn-0.1-1.5% Ni-0.5-1% Al2O3 is coated on the tungsten substrate. The tungsten substrate is compose of pure tungsten or alloy with W (residue)-2% Ni-1% Fe. The relative density of the tungsten substrate is 97-99% as large as the theoretical density of the pure tungsten. The coating tungsten material of the invention effectively improves the comprehensive usage properties of the surface of the tungsten substrate, such as oxidation resistance, wear resistance, perspiration and corrosion resistance and color brilliance on the condition of keeping the high relative density of the tungsten substrate, and thereby the tungsten substrate with high density is applied widely. The invention has the advantages of simple product process, low cost, adaptability for regular manufacture technique.

Description

technical field [0001] The invention relates to a tungsten material, in particular to a coated high-density tungsten base material. Background technique [0002] High-density tungsten-based materials are widely used in the fields of national defense and military industry, machinery and electronics, aerospace, metallurgy and mining, petroleum and coal, clocks and accessories. Uncoated tungsten materials have defects such as non-wear resistance, poor oxidation resistance, perspiration corrosion, and dull color. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a coated tungsten material with high comprehensive performance such as oxidation resistance, wear resistance, perspiration corrosion resistance and bright color. [0004] In order to solve the above-mentioned technical problems, the coated tungsten material provided by the present invention includes a tungsten base material, and the composition of the tungsten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B15/04B32B5/14
Inventor 刘沙
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com