Method for preparing titanium-containing zeolite molecular sieve by natural zeolite modification

A technology of zeolite molecular sieve and natural zeolite, which is applied in the field of modification of natural zeolite materials, can solve the problems of oxidation-reduction properties, solid acidity and alkalinity, and catalytic performance that cannot meet industrial production and environmental protection, and achieve good oxidation-reduction properties and increase additional value, the effect of low preparation cost

Inactive Publication Date: 2008-05-21
ZHEJIANG UNIV
View PDF5 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Modification methods such as heat treatment, acid treatment and salt treatment are usually adopted. After these treatments, the purity of natural zeolite, the smoothness of the pores and the adsorption performance are significantly improved, but the redox performance, solid acidity and alkalinity and catalytic performance are still far from satisfactory. Requirements for industrial production and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] ●Put 30g of natural mordenite in a 500ml three-path bottle, add 300ml, 0.8M NH 4 The Cl solution was stirred at 80°C for 2 hours, washed with water, dried, and repeated twice;

[0020] Take 25g of natural mordenite treated by (1) in a 500ml three-path bottle, add 300ml, 6M HCl solution, stir at 100°C for 8 hours, wash with water, dry, and repeat the operation 3 times;

[0021] ●Take 3g of the sample treated by (2) into a quartz reaction tube, raise it from room temperature to 120°C at a rate of 5°C / min, treat it with nitrogen at 120°C for 2 hours, and then increase it from room temperature to 120°C at a rate of 2°C / min From 120°C to 400°C, use nitrogen to bring the vapor of titanium tetrachloride into the quartz reaction tube, and react at 400°C for 8 hours, stop passing the vapor of titanium tetrachloride, and continue purging with nitrogen at this temperature for 3 hours , cooling, washing, and drying to obtain a titanium-containing zeolite molecular sieve sample;

...

Embodiment 2

[0024] ●With embodiment 1;

[0025] ●Take 25g of the sample treated by (1), add 300ml of 8M HCl solution to a 500ml three-path bottle, stir at 100°C for 6 hours, wash with water, dry, and repeat the operation 3 times;

[0026] ●Take 3g of the sample treated by (1) and (2) into a quartz reaction tube, heat it from 30°C to 180°C at a heating rate of 3°C / min, maintain this temperature for 2 hours, and then heat it at a rate of 5°C / min Raise from 180°C to 500°C, use argon to bring the vapor of isopropyl titanate into the quartz tube, react at 500°C for 10 hours, continue purging with argon at this temperature for 3 hours, lower the temperature, wash, After drying, the titanium-containing zeolite molecular sieve sample is obtained; the titanium-containing mordenite sample is obtained; the sample is characterized and analyzed by XRD, ICP and UV-Vis, and the results show that the titanium in the prepared sample has successfully entered the framework of the natural zeolite, and the sa...

Embodiment 3-6

[0028] In different ion exchangers according to Example 1, the Si / Ti ratio of the titanium-containing zeolite molecular sieve sample prepared by dealumination agent is shown in Table 1

[0029] natural zeolite

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method used for preparing zeolite molecular sieve containing titanium by modification of natural zeolite, and uses the natural zeolite as a raw material and the zeolite molecular sieve containing titanium is obtained through ion exchange, chemical dealumnization treatment and gas-solid isomorphous substitution reaction. The mole ratio of Si and Ti of molecular sieve skeleton is 20 to 100. The invention brings metallic titanium which has special catalytic performance to the skeleton of the natural zeolite, which greatly promotes grade of natural zeolite products, widens the application range of the natural zeolite and provides a way with low cost, convenient operation and environment protection to prepare heteroatom zeolite molecular sieve.

Description

technical field [0001] The invention belongs to the technical field of modification of natural zeolite materials, and relates to a method for preparing heteroatom molecular sieves by modification of natural zeolite, in particular to a method for preparation of titanium-containing zeolite molecular sieves by modification of natural zeolite. Background technique [0002] Zeolites are a class of aluminosilicate crystals with a regular cage or pore structure. It is precisely because of this regular and open pore structure that zeolites are widely used in catalysis, adsorption, separation, and host-guest assembly. Zeolite can be divided into natural zeolite and synthetic zeolite. Compared with natural zeolite, synthetic zeolite has many advantages (such as high purity, uniform pore size, and good ion exchange performance), but the production investment of synthetic zeolite is large, the cost is high, and the mother liquor is difficult to recover, etc., and its large-scale applic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B39/06B01J29/89
Inventor 肖丽萍杨靖楼辉郑小明
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap