Method of preparing thermal insulating mortar from solid waste

A technology for solid waste and thermal insulation mortar, which is applied in the field of chemical building materials and comprehensive utilization of waste residues, can solve the problems of inability to meet the performance requirements of thermal insulation mortar, low bonding strength, poor crack resistance, etc., and achieves light bulk density and good bonding performance. , the use of good performance

Inactive Publication Date: 2007-09-12
SHANGHAI UNIV
View PDF0 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional thermal insulation mortar uses expanded perlite as the aggregate, but due to the high water absorption rate of expanded perlite, high brittleness, low bond strength, and poor crack resistance, it cannot meet the performance requirements of modern buildings for thermal insulation mortar, such as light weight, Sound insulation, heat insulation, environmental protection, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Prepare 100kg of Group A raw materials, and the weight of each component raw material is:

[0039] Slag powder 31.6kg

[0040] Fly ash 20kg

[0041] Portland cement 30kg

[0042] Calcium enhancer CaO 12kg

[0043] Waste polystyrene foam 4kg

[0044] Polypropylene fiber 0.10kg

[0045] Redispersible Emulsion Powder 1.8kg

[0046] Water retaining agent 0.25kg

[0047] Water reducer 0.17kg

[0048] Defoamer 0.08kg

[0049] Group B raw material quartz sand 100kg

[0050] First put the raw materials of Group A in the mixer, fully stir for about 15 minutes, after mixing evenly, then add quartz sand, continue stirring for about 15 minutes, after mixing evenly, you can get the insulation mortar; when using, add appropriate amount of water to adjust and then use .

Embodiment 2

[0052] Prepare 100kg of Group A raw materials, and the weight of each component raw material is:

[0053] Slag powder 23.2kg

[0054] Fly ash 25kg

[0055] Portland cement 32.4kg

[0056] Calcium enhancer CaO 10kg

[0057] Waste polystyrene foam 6kg

[0058] Polypropylene fiber 0.08kg

[0059] Redispersible Emulsion Powder 2.57kg

[0060] Water retaining agent 0.4kg

[0061] Water reducer 0.3kg

[0062] Defoamer 0.05kg

[0063] Group B raw material quartz sand 100kg

[0064] First put the raw materials of Group A in the mixer, fully stir for about 15 minutes, after mixing evenly, then add quartz sand, continue stirring for about 15 minutes, after mixing evenly, you can get the insulation mortar; when using, add appropriate amount of water to adjust and then use .

Embodiment 3

[0066] Prepare 100kg of Group A raw materials, and the weight of each component raw material is:

[0067] Slag powder 21kg

[0068] Fly ash 30kg

[0069] Portland cement 34.5kg

[0070] Calcium enhancer CaO 5kg

[0071] Waste polystyrene foam 7kg

[0072] Polypropylene fiber 0.12kg

[0073] Redispersible Emulsion Powder 1.38kg

[0074] Water retaining agent 0.5kg

[0075] Water reducer 0.4kg

[0076] Defoamer 0.10kg

[0077] Group B raw material quartz sand 100kg

[0078] First put the raw materials of Group A in the mixer, fully stir for about 15 minutes, after mixing evenly, then add quartz sand, continue stirring for about 15 minutes, after mixing evenly, you can get the insulation mortar; when using, add appropriate amount of water to adjust and then use .

[0079] Add appropriate amount of water to the dry mortar material prepared in the above examples to make the consistency of the mortar mixture reach 80 mm, and mold it into a sample according to the standard re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a method for preparing heat-preservation mortar utilizing solid castoffs, in which, the raw material is composed of two groups: group A includes the following components and weight percentage: slag powder 20-40%, powdered coal ash 20-30%, Portland cement 30-40%, Ca reinforcing agent 5-15%, abandon polystyrene foams 3-8%, PP fiber 0.05-0.15%, re-dispersible latex powder 1-3%, water preservation agent 0.2-0.6%, water reducer 0.1-0.5%, defoamer 0.05-0.10%, and quartz sand is the raw material of group B, and the weight ratio of group A and B is 1:1. Raw materials of group A are weighed and matched then to be put into a sterring mill and mixed uniformly and then quartz sand of equal volume is added in it to be mixed continuously to get the heat preservation mortar, which can be used by adding suitable volume of water.

Description

technical field [0001] The invention relates to a method for preparing thermal insulation mortar by utilizing solid waste, and belongs to the technical field of comprehensive utilization of chemical building materials and waste residues. Background technique [0002] The extensive use of thermal insulation materials with excellent performance and scientific thermal insulation technology in building materials will achieve good social and economic benefits. [0003] Insulation mortar is made of some materials with better thermal insulation properties as aggregate, together with cementitious materials, additives, and water, and is made into mortar for wall insulation in a certain proportion. The traditional thermal insulation mortar uses expanded perlite as the aggregate, but due to the high water absorption rate of expanded perlite, high brittleness, low bond strength, and poor crack resistance, it cannot meet the performance requirements of modern buildings for thermal insula...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B16/08C04B18/08C04B18/12C04B16/02C04B14/06C04B14/28C04B16/10C04B24/38C04B24/20C04B22/00C04B103/46C04B103/30C04B103/50
CPCC04B20/026C04B28/04C04B40/065C04B20/12C04B40/0039Y02W30/91C04B16/10C04B18/08C04B18/141C04B20/006C04B20/008C04B22/064C04B22/10C04B2103/0057C04B2103/302C04B2103/46C04B2103/50C04B16/0633C04B24/226C04B24/2676C04B24/383C04B14/06C04B20/0076C04B16/08C04B16/087C04B20/0012C04B20/1077C04B20/1088
Inventor 杨瑞海陆文雄李柯余淑华李小亮
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com