Alloy powder capable of producing compression stress in the fused-on layer
A technology of compressive stress and alloy powder, which is applied in the field of alloy powder, can solve problems such as large tensile stress on the surface of structures, failure of metal structures, fatigue crack stress, etc., so as to delay the generation of fatigue cracks and stress corrosion cracks, prolong service life, The effect of preventing stress corrosion cracking
Inactive Publication Date: 2008-06-25
TIANJIN UNIV
View PDF4 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, after actual manufacturing and processing, there will be high levels of tensile stress locally in the metal structure, or additional tensile stress caused by stress concentration. After superimposed working loads, cracks will appear in these parts, especially fatigue cracks and stress corrosion cracks. Causes premature failure of metal structures
It is possible to alleviate some stress concentration problems by using the above-mentioned process methods, but for failure problems mainly caused by fracture, these methods are helpless, but will cause greater tensile stress on the surface of the structure
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0050] In Example 1 and Example 2, F3 alloy powder is used. When the stress concentration is equivalent to that of Comparative Example 1 and 2, the cladding layer has compressive stress, so the fatigue strength of the welded joint is greatly improved. Therefore, the use of compressive stress alloy powder combined with spraying, spray welding, spray melting, remelting and other processes can effectively improve the fatigue performance of metal components.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Login to view more
Abstract
The alloy powder capable of producing compression stress in the fused-on layer consists of Cr 6.0-12.0 wt%, Ni 5.0-11.0 wt%, Mn 0.5-1.8 wt%, Mo 0.1-0.9 wt%, Nb 0.1- 0.9 wt%, Ti 0.1-0.9 wt%, Si 0.1-0.9 wt%, except Fe. It has grain size of 50-200 microns, solid phase change temperature after melting and solidifying of 100-300 deg.c, and structure comprising martensite in 50-90 % and austenite in 10-50 %. The present invention is used in raising the fatigue resistance, stress corrosion resistance, safety and service life of iron and steel material, mechanical structure and equipment. The method and material of the present invention may be used in producing composite material product with compression stress in the surface.
Description
technical field [0001] The invention relates to an alloy powder, in particular to an alloy powder suitable for processes such as spray coating, spray welding, spray melting and remelting. Background technique [0002] By the end of 2005, my country's steel output was close to 300 million tons, 80-90% of which was used to manufacture large metal structures and equipment, which played an important role in improving people's living standards and social progress. However, large-scale metal structures and equipment often have failure problems, causing huge economic losses and even personal casualties. Therefore, their reliability and safety have always been a concern of people. [0003] Fracture, corrosion, and wear are the three main forms of metal structure failure. In order to reduce the failure loss caused by this, many methods of surface modification of metal materials have been proposed, such as: spray coating, spray welding, spray melting and remelting, etc. There are sev...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00C22C1/05C22C38/00
Inventor 王文先霍立兴王东坡张中平张玉凤荆洪阳
Owner TIANJIN UNIV
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap