Flow liner crystallite glass composite plate preparation method

A technology of glass-ceramic and composite plate, which is applied in glass pressing, glass manufacturing equipment, glass forming and other directions, can solve the problems of difficult to flexibly adjust the color of products, difficult to generate texture on the surface of products, unable to prepare glass-ceramics, etc. Far-reaching resources and environmental protection significance, good overall sense of decoration, and the effect of realizing waste recycling

Inactive Publication Date: 2008-01-23
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the glass-ceramics prepared from solid waste has a darker color, and it is impossible to prepare light-colored glass-ceramics, and the color of the product is not easy to adjust flexibly; in addition, it is difficult to generate texture on the surface of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flow liner crystallite glass composite plate preparation method
  • Flow liner crystallite glass composite plate preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] As shown in Figure 1, the preparation method of flow pattern glass-ceramic composite plate comprises the following steps:

[0033](1) Preparation of the surface mother glass plate: Weigh the batches (A, B, C color glass batches) for preparing green, yellow and white glasses respectively, wherein the mass percentage of the main chemical components of the green glass batches is: 56.0 %SiO 2 , 9.0%Al 2 o 3 , 21.0% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.3%TFe 2 o 3 , 0.7%Cr 2 o 3 , 4.0% ZrO 2 , the mass percentage of the main chemical composition of the yellow glass batch is: 56.0% SiO 2 , 8.0%Al 2 o 3 , 21.0% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.8%TFe 2 o 3 , 4.0% ZrO 2 , 1.2% MnO 2 , the mass percentage of the main chemical components of the white glass batch is: 56.0% SiO 2 , 9.0% Al 2 o 3 , 21.7% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.3%TFe 2 o 3 , 4.0% ZrO 2 , and then put the thr...

Embodiment 2

[0038] As shown in Figure 1, the preparation method of flow pattern glass-ceramic composite plate comprises the following steps:

[0039] (1) Preparation of the surface mother glass plate: Weigh the batches (A, B, C color glass batches) for preparing red, green and yellow glasses respectively, wherein the mass percentage of the main chemical components of the red glass batches is: 55.0 %SiO 2 , 7.0% Al 2 o 3 , 21.0% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.4%TFe 2 o 3 , 4.0% ZrO 2 , 1.2% MnO 2 , 1.6% CdS, 0.8% Se, the mass percentage of the main chemical components of the green glass batch is: 56.0% SiO 2 , 9.0% Al 2 o 3 , 21.0% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.3%TFe 2 o 3 , 0.7%Cr 2 o 3 , 4.0% ZrO 2 , the mass percentage of the main chemical composition of the yellow glass batch is: 56.0% SiO 2 , 8.0%Al 2 o 3 , 21.0% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.8%TFe 2 o 3 , 4.0% ZrO 2 , 1.2...

Embodiment 3

[0044] As shown in Figure 1, the preparation method of flow pattern glass-ceramic composite plate comprises the following steps:

[0045] (1) Preparation of the surface mother glass plate: Weigh the batches (A, B colored glass batches) for preparing green and yellow glasses respectively, wherein the mass percentage of the main chemical components of the green glass batches is: 56.0% SiO 2 , 9.0%Al 2 o 3 , 21.0% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.3%TFe 2 o 3 , 0.7%Cr 2 o 3 , 4.0% ZrO 2 , the mass percentage of the main chemical composition of the yellow glass batch is: 56.0% SiO 2 , 8.0%Al 2 o 3 , 2 1.0% CaO, 2.0% MgO, 2.0% K 2 O, 4.5% Na 2 O, 0.5% Sb 2 o 3 , 0.8%TFe 2 o 3 , 4.0% ZrO 2 , 1.2% MnO 2. Then put the glass batch materials of two colors into two glass melting furnaces respectively, keep the temperature at 1500°C for 120 minutes, then lower the temperature to 1400°C and keep the temperature for 60 minutes, and melt into two ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method for the microcrystal rhyolitic glass composite plate. Wherein, first, fusing the glass liquid with two or more colors by common material; then, mixing to prepare the uneven glass mixed liquid, and forming the surface mother glass plate with rhyolitic pattern; finally, overlapping the mother plate on the substrate to put into kiln furnace for thermal treatment to realize their sintering and both coring and crystallizing of composite plate and convert into the objective product, which has well decorative effect, and brings great resource and environmental protection benefits.

Description

technical field [0001] The invention relates to a preparation method of a glass-ceramic composite board, in particular to a preparation method of a glass-ceramic composite board with flow pattern for architectural decoration. Background technique [0002] Glass-ceramics has excellent physical and chemical properties such as compact structure, high mechanical strength, wear resistance, corrosion resistance, and strong weathering resistance. [0003] The use of solid waste to prepare glass-ceramics for architectural decoration can not only eliminate the environmental pollution of solid waste, but also expand the range of raw materials for glass-ceramics, reduce production costs, and realize waste recycling. However, the glass-ceramic prepared from solid waste has a darker color, and it is impossible to prepare light-colored glass-ceramics, and the color of the product is not easy to be flexibly adjusted; in addition, it is difficult to generate texture on the surface of the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03B23/203C03C1/06C03B32/02C03B13/00C03B19/02C03B11/00C03C6/00
Inventor 周俊王焰新
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap